A water-based inkjet and ink technology, used in inks, household appliances, applications, etc., can solve the problems of ink layering and caking, easy to block inkjet ports, ink oxidation, etc., to achieve good durability, clear and good printing ink. The effect of adhesion

Active Publication Date: 2016-03-30
北海市天硌打印耗材有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] An object of the present invention is to solve at least the above problems, and provide a water-based inkjet ink, which solves the problem that the ink is easy to block the inkjet port during use, or the ink is not used for a long time, and the ink is layered and agglomerated. Solve the problem of oxidation and fading of ink after printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The following raw materials, in parts by weight:

[0028] 1) Add 30 parts of deionized water, 10 parts of ethylene glycol, and 2004 parts of polyethylene glycol into the reaction kettle, raise the temperature to 60°C, then add 1 part of ethylene glycol dimethacrylate, methacrylic acid 1 part of ethyl ester, 1 part of polyurethane acrylic resin, 1 part of neopentyl glycol diacrylate, disperse with emulsification disperser for 20 minutes, cool down to 40 ℃ and keep warm for 10 minutes, and the dispersion speed is 9000rpm; first use deionized water, ethylene glycol, Polyethylene glycol 200 is used as a water solvent to dissolve and disperse ethylene glycol dimethacrylate, ethyl methacrylate, polyurethane acrylic resin, and neopentyl glycol diacrylate under the action of a disperser, so that the resin can be completely dissolved in In a solvent, a homogeneous liquid is formed;

[0029] 2) Add 10 parts of dye to the reaction kettle described in step 1) at a temperature of 4...

Embodiment 2

[0035] The following raw materials, in parts by weight:

[0036] 1), first pulverize 4 parts of ethylene glycol dimethacrylate, 3 parts of ethyl methacrylate, 3 parts of polyurethane acrylic resin, and 1 part of neopentyl glycol diacrylate, and pass through a nano-sieve to obtain nano-powder ethyl Glycol dimethacrylate, ethyl methacrylate, polyurethane acrylic resin, neopentyl glycol diacrylate, then 40 parts of deionized water, 15 parts of ethylene glycol, and 2005 parts of polyethylene glycol were added to the reaction In the kettle, heat up to 60°C, then add nano-powdered ethylene glycol dimethacrylate, ethyl methacrylate, polyurethane acrylic resin, and neopentyl glycol diacrylate, disperse with an emulsifying disperser for 20 minutes, and cool down to 40 Keep warm at ℃ for 10 minutes, and the dispersion speed is 11000rpm; the resin is crushed and sieved first, in order to better dissolve in the solvent and exist as nanoparticles, the ink is more delicate and the adhesion ...

Embodiment 3

[0043] The following raw materials, in parts by weight:

[0044] 1), first 3 parts of ethylene glycol dimethacrylate, 2 parts of ethyl methacrylate, 2 parts of polyurethane acrylic resin, and 2 parts of neopentyl glycol diacrylate are pulverized, and passed through a nano-sieve to obtain nano-powder ethyl Glycol dimethacrylate, ethyl methacrylate, polyurethane acrylic resin, neopentyl glycol diacrylate, then 35 parts of deionized water, 12 parts of ethylene glycol, and 2004 parts of polyethylene glycol were added to the reaction In the kettle, heat up to 60°C, then add nano-powdered ethylene glycol dimethacrylate, ethyl methacrylate, polyurethane acrylic resin, and neopentyl glycol diacrylate, disperse with an emulsifying disperser for 20 minutes, and cool down to 40 Keep warm at ℃ for 10 minutes, and the dispersion speed is 10000rpm; the resin is crushed and sieved first, in order to better dissolve in the solvent and exist as nanoparticles, the ink is more delicate and the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses water-based inkjet ink and a preparation method thereof. The ink is prepared from, deionized water, polyethylene glycol 200, a pigment, ethylene glycol dimethacrylate, ethyl methacrylate, neopentyl glycol diacrylate, lauryl alcohol polyoxyethylene, triethanolamine, polyoxyethylene polyoxypropylene pentaerythritol ether, ethylene bis stearamide, 4-[(4,6-bis(octylthio)-1,3,5-triazine-2-yl) amino]-2,6-ditert-butyl phenol, octyl methoxycinnamate, titanium dioxide and the like. The water-based inkjet ink has the advantages that the water-based inkjet ink meets the requirements of environmental protection, printing pollution is greatly reduced, the octyl methoxycinnamate and the titanium dioxide are added into the ink and are combined to form a protective film for ultraviolet light blocking on the dye surface layer of the ink, so that the ink does not fade under the outdoor light exposure, is resistant to scratching and is not easily oxidized, and output performed by using the ink does not need printing materials with special coatings.

Description

technical field [0001] The invention relates to the field of printer consumables. More specifically, the present invention relates to a water-based inkjet ink and its preparation method. Background technique [0002] Inkjet printing is printing achieved without the printing device contacting the substrate on which the printed characters are deposited, by jetting a stream of ink droplets onto a surface and by controlling the direction of the stream so that the droplets A desired printed image is formed on the surface. Due to the particularity of the inkjet printing method, the inkjet ink has higher requirements, such as ink viscosity, resistivity, component compatibility, solubility, and wettability to the substrate. [0003] According to the nature of the ink, inkjet ink can be divided into three types: water-based inkjet ink, solvent-based inkjet ink, UV inkjet ink, solvent-based inkjet ink is not environmentally friendly and pollutes the environment, UV inkjet ink requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/38C09D11/328C09D11/30
CPCC09D11/30C09D11/328C09D11/38
Inventor 王和平
Owner 北海市天硌打印耗材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap