Antibacterial and moldproof polymer modified spray asphalt waterproof paint and application method thereof

A bituminous waterproof coating, antibacterial and anti-mildew technology, applied in asphalt coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of secondary pollution of water bodies, loss of waterproof effect, erosion of waterproof coatings, etc., and achieve high viscosity The effect of high bonding strength, reducing the possibility of secondary pollution, and high elongation

Active Publication Date: 2016-04-06
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, polymer-modified rubber asphalt waterproof coatings contain high molecular polymers. When they are immersed in eutrophic groundwater for a long time, bacteria and algae may attach to the waterproof layer, which will cause the waterproof coating to be eroded, and even occur. Biodegradation causes leakage and loses waterproof effect
For example, CN201210500017.4 discloses the special spraying quick-setting rubber waterproof coating for sewage treatment plants. The spraying quick-setting rubber waterproof coating has the effect of preventing microbial growth by adding an anti-fungal agent to the asphalt component, but this invention is to apply the anti-mildew If the antifungal agent is directly added to the anionic asphalt emulsion component, it will easily lead to the instability of the product, and the antifungal agent directly contacts the external water layer in the asphalt emulsion component, which may cause secondary pollution of the water body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1. Preparation of component A polymer modified asphalt emulsion

[0018] Add 30 parts of chloroprene emulsion and 20 parts of styrene-butadiene emulsion to 15 parts of filler, stir well, add 1 part of thickener, then add 90 parts of anionic emulsified bitumen purchased from Sinopec, and keep stirring until completely mixed That is, the A component of the product is obtained. The preparation method of the filler is as follows: Add 0.5 parts of stabilizer, 3 parts of dispersant, 4 parts of wetting agent, 1 part of defoamer, and 0.5 parts of pH regulator into 100 parts of water, and after the dispersion is uniform, add 230 parts of kaolin, and disperse at a high speed 30 minutes to get the filler used.

[0019] 2. Preparation of B component special curing agent

[0020] Dissolve 2 parts of polyaluminium chloride and 8 parts of ammonium chloride in 100 parts of water, and then add 4 parts of cetyltrimethylammonium chloride, and disperse evenly to obtain component B of the...

Embodiment 2

[0026] 1. Preparation of component A polymer modified asphalt emulsion

[0027] Add 20 parts of chloroprene emulsion and 20 parts of styrene-acrylic emulsion to 10 parts of filler, stir well, add 0.5 parts of thickener, then add 100 parts of self-made anionic emulsified asphalt, and keep stirring until it is completely mixed. A component of the product.

[0028] Wherein, the preparation method of the filler is as follows: add 0.8 parts of stabilizer, 4 parts of dispersant, 4 parts of wetting agent, 1 part of defoamer, and 1 part of pH regulator into 100 parts of water, and add 200 parts of talcum powder after uniform dispersion, Disperse at high speed for 30 minutes to obtain the filler used. The preparation method of anionic emulsified asphalt is as follows: Dissolve 2 parts of polyvinyl alcohol into 50 parts of water at 50°C, then add 1 part of sodium dodecylbenzenesulfonate and 1 part of alkylphenol polyoxyethylene ether, after fully dissolving , the soap liquid and 65 pa...

Embodiment 3

[0036] 1. Preparation of component A polymer modified asphalt emulsion

[0037] Add 20 parts of styrene-butadiene emulsion and 20 parts of acrylic emulsion to 10 parts of filler, stir evenly, add 0.5 parts of thickener, then add 90 parts of self-made anionic emulsified asphalt, and keep stirring until it is completely mixed to get the product The A component.

[0038] Among them, the preparation method of the filler is as follows: add 0.5 parts of stabilizer, 3 parts of dispersant, 4 parts of wetting agent, 0.5 parts of defoamer, and 1 part of pH regulator into 100 parts of water, and add 160 parts of heavy calcium carbonate after dispersing evenly , high-speed dispersion for 30 minutes to obtain the filler used. The preparation method of anionic emulsified asphalt is as follows: Dissolve 2 parts of polyvinyl alcohol into 50 parts of water at 50°C, then add 1 part of sodium dodecylbenzenesulfonate and 1 part of alkylphenol polyoxyethylene ether, after fully dissolving , the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides antibacterial and moldproof polymer modified spray asphalt waterproof paint and an application method thereof. The paint is composed of a component A and a component B. The component A is prepared from, by weight, 90-120 parts of anionic emulsified asphalt, 40-90 parts of polymer emulsion, 0.5-5 parts of a thickening agent and 10-60 parts of filler. The component B is prepared from, by weight, 100 parts of water, 5-15 parts of a curing agent and 0.5-5 parts of an antibacterial agent. The invention further provides the application method of the antibacterial and moldproof polymer modified spray asphalt waterproof paint. The antibacterial and moldproof polymer modified spray asphalt waterproof paint has high ductility, high resilience and high adhering strength, is antibacterial and moldproof, excellent in low-temperature performance and high in construction speed and can be closely connected with a basic layer, and influences of deformation of the basic layer on the waterproof performance of a material can be effectively resisted; meanwhile, the situation that bacteria are bred on the surface of a coating film, and the coating function of a waterproof layer is damaged can be effectively prevented, and the possibility that an antibacterial agent has secondary pollution on water is reduced.

Description

technical field [0001] The invention relates to a polymer modified spraying bitumen waterproof coating and a preparation method thereof, in particular to an antibacterial and antifungal polymer modified spraying bitumen waterproof coating and a preparation method thereof. Background technique [0002] With the rapid development of my country's economic construction, especially infrastructure, the demand for waterproof materials is increasing, and the scope of application is also expanding rapidly. Polymer modified asphalt has excellent waterproof performance, good elasticity, strong weather resistance, fatigue resistance, aging resistance, etc., and has the advantages of reliability and economy. It is widely used in basement floors, side walls, subways, tunnels, and roofs , landfill and other anti-seepage and waterproof projects. However, with the improvement of people's living standards and the vigorous development of industrial industries, the problem of eutrophication of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D5/14C09D7/12
CPCC08K2201/011C08L2205/03C08L2205/035C09D5/14C09D7/61C09D7/62C09D7/65C09D195/00C08L11/00C08L9/08C08K13/02C08K3/346C08K2003/164C08L25/14C08K3/34C08K2003/3081C08K2003/162C08L33/00C08K2003/265C08K2003/0806C08K13/06C08L31/04C08L29/04
Inventor 于猛李文志郭子斌段文锋韩忠强
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com