Impact resistant natural rubber material and preparation method thereof

A natural rubber, impact-resistant technology, applied in the field of rubber, can solve the problems of shortened reaction time, single preparation method, cumbersome process, etc., and achieve the effect of superior comprehensive performance, good UV resistance, and high surface hardness

Inactive Publication Date: 2016-05-04
HEFEI JIEMING NEW MATERIAL TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition, scholars have inserted ionic liquids into kaolinite layers to form nanostructures, which are widely used in electrode modification, catalysts, and detection of anions. Ionic liquid intercalated kaolinite has good thermal stability, electrical conductivity and optical properties. However, the preparation method of ionic liquid intercalated kaolinite abroad is single, and the cycle is long and the process is cumbersome. In the present invention, it is improved and simplified. The experimental process is simplified, the reaction time is shortened, and a better intercalation effect can be obtained at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A kind of impact-resistant natural rubber material, it is made up of the raw material of following weight part:

[0027] Natural rubber 100, kaolinite powder 20, dimethyl sulfoxide 400, methanol 900, N-methylimidazole 70, ethyl bromide 100, nano silicon oxide 4, sulfur 1, antioxidant DPPD 1, aluminum ammonium sulfate 1, triglycerides Alcohol diisocaprylate 4, p-toluenesulfonic acid 0.2, ethoxylated alkylphenol ammonium sulfate 0.7, calcium aluminate 2, polyisoprene 4.

[0028] A kind of preparation method of described impact-resistant natural rubber material, comprises the following steps:

[0029] (1) Add the above ammonium aluminum sulfate to 5 times of deionized water, and stir evenly;

[0030] (2) Add the above-mentioned polyisoprene to 10 times of absolute ethanol, add p-toluenesulfonic acid, raise the temperature to 70°C, add kaolinite powder, stir for 2 minutes by magnetic force, add the above-mentioned aluminum ammonium sulfate aqueous solution , stirred to no...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
compression setaaaaaaaaaa
Login to view more

Abstract

The present invention discloses an impact resistant natural rubber material, which is composed of the following raw materials by weight: 100-140 parts of natural rubber, 20-30 parts of kaolin powder, 400-500 parts of dimethylsulfoxide, 900-1000 parts of methanol, 70-80 parts of N-methylimidazole, 100-120 parts of bromoethane, 4-6 parts of nanometer silicon oxide, 1-1.6 parts of sulfur, 1-2 parts of an antioxidant DPPD, 1-3 parts of aluminum ammonium sulfate, 4-7 parts of triethylene glycol Di-2-ethylhexoate(triglycol dioctate), 0.2-0.3 part of p-toluenesulfonic acid, 0.7-1 part of ethoxylated alkylphenol ammonium sulfate, 2-4 parts of calcium aluminate and 4-6 parts of polyisoprene. The natural rubber material has good impact strength, high surface hardness, good weather resistance, and excellent overall performance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to an impact-resistant natural rubber material and a preparation method thereof. Background technique [0002] Kaolinite is one of the clay minerals of kaolin (kaolinite, dickite, nacre, halloysite, etc.) with l:l layered structure, composed of SiO4 tetrahedral layer and AlO2(OH)4 octahedral layer. 1:1 superimposed to form an asymmetric layered structure, thus establishing a large stack of dipoles, the interlayers are connected by (Al—O—H…O—Si) hydrogen bonds, and the interlayer distance is about 072nm. There is no isomorphic replacement in the crystal lattice, and the charge in the interlayer domain is basically balanced, so that cations cannot be adsorbed in its two-dimensional layer. In addition, due to the interaction of hydrogen bonding force and van der Waals force between layers, it has a considerable Cohesion, so the crystal layers are tightly connected and stable in perform...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L47/00C08K13/06C08K9/04C08K3/36C08K3/34C08K3/06
CPCC08L7/00C08K2201/011C08L2201/08C08L47/00C08K13/06C08K9/04C08K3/36C08K3/34C08K3/06
Inventor 高芳
Owner HEFEI JIEMING NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap