A kind of multifunctional biosorbent material and preparation method thereof

A biological adsorption, multi-functional technology, applied in chemical instruments and methods, adsorbed water/sewage treatment, water pollutants, etc., can solve the problems of slow separation rate, difficult recovery, low recycling rate, etc. The effect of improving adsorption capacity and high treatment efficiency

Active Publication Date: 2019-03-29
CENT SOUTH UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of biosorbent and similar heavy metal adsorption materials are mainly separated by sedimentation and separation after adsorbing heavy metal ions, which has the disadvantages of slow separation rate, poor separation effect, difficult recovery and low recycling rate.
Moreover, the growth and reproduction of the bacteria mentioned in the patent is greatly affected by the habitat environment, and cannot adapt to the complex pollution status of the external actual environment, resulting in a weak ability to remove heavy metals, so that the actual adsorption effect of the entire biosorbent is large. discount

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of multifunctional biosorbent material and preparation method thereof
  • A kind of multifunctional biosorbent material and preparation method thereof
  • A kind of multifunctional biosorbent material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of multifunctional biosorbent material of the present invention, its preparation method comprises the following steps (as figure 2 shown):

[0039] (1) Preparation of α-ketoglutarate chitosan (KCTS): Weigh 4.500g of chitosan dry sample, fully swell with 120mL distilled water for more than 24h, weigh m(α-ketoglutarate):m( Chitosan)=1.6:1.0 alpha-ketoglutaric acid 7.200g, join in the sufficient swelling system of chitosan at room temperature, stir 1h, promptly obtain slightly yellow transparent viscous solution; With 0.1mol / Slowly adjust the pH of the filtrate system to 4.5-5.5 (preferably 5.0) with 1 L of sodium hydroxide solution to obtain a milky white viscous solution, then transfer it to a 500mL three-necked flask and continue to stir evenly. Control the reaction time to 4h; according to the molar number of n(sodium borohydride):n(α-ketoglutaric acid)=1.8:1.0, accurately weigh 3.360g of sodium borohydride, and prepare it into 30mL of NaBH 4 Solution, slowl...

Embodiment 2

[0053] A kind of multifunctional biosorbent material of the present invention, its preparation method comprises the following steps:

[0054] (1) Preparation of α-ketoglutarate chitosan (KCTS): Weigh 4.500g of chitosan dry sample, fully swell with 120mL distilled water for more than 24h, weigh m(α-ketoglutarate):m( Chitosan)=1.6:1.0 alpha-ketoglutaric acid 7.200g, join in the sufficient swelling system of chitosan at room temperature, stir 1h, promptly obtain slightly yellow transparent viscous solution; With 0.1mol / Slowly adjust the pH of the filtrate system to 4.5-5.5 (preferably 5.0) with 1 L of sodium hydroxide solution to obtain a milky white viscous solution, then transfer it to a 500mL three-necked flask and continue to stir evenly. Control the reaction time to 4h; according to the molar number of n(sodium borohydride):n(α-ketoglutaric acid)=1.8:1.0, accurately weigh 3.360g of sodium borohydride, and prepare it into 30mL of NaBH 4 Solution, slowly add dropwise to the ...

Embodiment 3

[0064] A kind of multifunctional biosorbent material of the present invention, its preparation method comprises the following steps:

[0065] (1) Preparation of α-ketoglutarate chitosan (KCTS): Weigh 4.500g of chitosan dry sample, fully swell with 120mL distilled water for more than 24h, weigh m(α-ketoglutarate):m( Chitosan)=1.6:1.0 alpha-ketoglutaric acid 7.200g, join in the sufficient swelling system of chitosan at room temperature, stir 1h, promptly obtain slightly yellow transparent viscous solution; With 0.1mol / Slowly adjust the pH of the filtrate system to 4.5-5.5 (preferably 5.0) with 1 L of sodium hydroxide solution to obtain a milky white viscous solution, then transfer it to a 500mL three-necked flask and continue to stir evenly. Control the reaction time to 4h; according to the molar number of n(sodium borohydride):n(α-ketoglutaric acid)=1.8:1.0, accurately weigh 3.360g of sodium borohydride, and prepare it into 30mL of NaBH 4 Solution, slowly add dropwise to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention provides a multifunctional biological adsorbent, and a preparation method thereof comprises the following steps: chitosan alpha-ketoglutaric acid is taken as a carrier, a heavy metal ion is taken as an imprinted template, an ionic imprinting material is obtained through the ionic imprinting technique, then the ionic imprinting material and magnetic nano-Fe3O4 are subjected to cross-linking reaction, a magnetic ionic imprinting material is obtained, and finally the surface of a Serratia marcescens thallus is coated with the magnetic ionic imprinting material through curing reaction. The obtained biological adsorbent integrates advantages of high adsorption with low cost, high selectivity with low pollution, high separating efficiency with low loss, and the like, also has advantages of magnetic materials and biological adsorbents, and can realize various functions such as magnetic separation, selective recognition, circulative recovery and the like; moreover, the method is simple, the cost is low, and the biological adsorbent is green and environment-friendly, avoids secondary pollution, and can be widely used for treatment of various specific heavy metal industrial wastewater, therefore, a novel material is provided for treatment of industrial wastewater.

Description

technical field [0001] The invention belongs to the field of adsorption materials, in particular to a multifunctional biological adsorption material and a preparation method thereof. Background technique [0002] Heavy metal pollution is one of the three major water pollution methods in the world, mainly including lead, chromium, mercury, zinc, copper, nickel and other heavy metal pollution. When heavy metals enter the water environment, they cannot be degraded by organisms, but also accumulate in organisms and accumulate in the food chain. After entering the human body, they will damage the normal metabolic activities of the human body and cause harm to people's health. Traditional heavy metal wastewater treatment methods mainly include chemical, physical or physicochemical methods. However, the traditional chemical and physical chemical treatment methods have many disadvantages, such as: large investment, troublesome operation and management, high operating cost, and easy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/24B01J20/30B01J20/28C02F1/28C02F1/62
CPCB01J20/06B01J20/24B01J20/28009B01J2220/46B01J2220/4806B01J2220/4825B01J2220/4868C02F1/281C02F1/286C02F1/288C02F2101/20
Inventor 丁萍杨飞肖稳李晶黄瑞雪陈翠梅
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com