A kind of silicon oxide/carbon/metal element composite material, preparation method and application thereof

A composite material and graphitized carbon technology, applied in electrical components, electrochemical generators, battery electrodes, etc., can solve the problems of poor capacity development, low initial coulombic efficiency, poor conductivity, etc., and achieve low cost and high coulombic efficiency , The effect of simple preparation method

Active Publication Date: 2017-11-10
BEIJING IAMETAL NEW ENERGY TECH CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

overcame SiO x The electrical conductivity of the material is extremely poor, the capacity is poor and the first coulombic efficiency is low, and it provides a process route with cheap and easy-to-obtain raw materials, simple production process, and commercial large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of silicon oxide/carbon/metal element composite material, preparation method and application thereof
  • A kind of silicon oxide/carbon/metal element composite material, preparation method and application thereof
  • A kind of silicon oxide/carbon/metal element composite material, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 3 kg of SiO with an average particle size of 5 μm x , 500g sucrose, 500g polyvinylpyrrolidone, 50g aluminum powder and 40L water are added in the planetary ball mill, the ball mill speed is 600r / min, after grinding for 12 hours, filter and remove the particles with a particle size greater than 1 μm in the slurry, and then The slurry is added to the sand mill grinding tank, the sand mill speed is 1200r / min, after grinding for 12 hours, then 6kg of flake graphite, 300g graphene and 300g SuperP with an average particle diameter of 5 μm are added to the above slurry , and transfer the slurry to a ball mill for ball milling for 4 hours, the speed of the ball mill is 400r / min, after the obtained slurry is dried and shaped by a spray dryer, it is sintered in a nitrogen atmosphere in a rotary kiln at a sintering temperature of 700°C, and the temperature rises The rate is 5°C / min, sintering for 2h, the obtained SiO x / C / M composite materials are screened, demagnetized and baled...

Embodiment 2

[0033] 3 kg of SiO with an average particle size of 1 μm x , 500g of sodium alginate, 500g of polyacrylic acid, 50g of magnesium powder and 40L of water were added to a planetary ball mill. and 300g of Ketjen Black were added to the above slurry, and ball milling was continued for 8 hours in a ball mill with a rotation speed of 400r / min. After the obtained slurry was dried and shaped by a spray dryer, it was sintered in an argon atmosphere in a roller kiln. treatment, the sintering temperature is 800°C, the heating rate is 10°C / min, and the sintering is 3h, the obtained SiO x / C / M composite materials are screened, demagnetized and baled.

[0034] Scanning electron microscope (JEOL-6700F) test obtained SiO under the above conditions x / C / M composite morphology, its particle size distribution was tested with a laser particle size analyzer, and the test results are shown in Table 1; SiO x The value of x in the middle is 1, and the content is 30%. The carbon material exists in ...

Embodiment 3

[0037] 4 kg of SiO with an average particle size of 5 μm x , 500g of polyacrylic acid, 1000g of polyvinylpyrrolidone, 100g of zinc powder and 40L of water were added to a planetary ball mill, the speed of the ball mill was 600r / min, after grinding for 12 hours, the particles with a particle size greater than 1 μm in the slurry were removed by sieve filtration, Slurry is then joined in the sand mill grinding tank, and the sand mill speed is 1200r / min, after grinding for 12 hours, then 5kg average particle diameter is 7 μ m flake graphite, 300g graphene joins in the above-mentioned slurry, and Transfer the slurry to a ball mill and mill for 4 hours at a speed of 400r / min. After the resulting slurry is dried and shaped by a spray dryer, it is sintered in a nitrogen atmosphere in a pusher kiln. The sintering temperature is 600°C and the heating rate is 5 ℃ / min, sintering 2h, the obtained SiO x / C / M composite materials are screened, demagnetized and baled.

[0038] Scanning ele...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an SiOx / C / M composite material and a preparation method and an application thereof. The SiOx / C / M composite material is prepared from an SiOx material, a carbon material and an M component and is prepared through a simple, efficient, low-cost and pollution-free production technology on a large scale. The composite material is taken as a negative electrode material for a lithium-ion battery, so that the electrochemical properties of the SiOx negative electrode material are significantly improved; and the defects that the SiOx negative electrode material is extremely poor in conductivity, poor in capacity development and relatively low in initial coulomb efficiency are overcome.

Description

technical field [0001] The invention relates to a silicon oxide / carbon / metal element composite material, in particular to the large-scale preparation of the silicon oxide / carbon / metal element composite material and its application as a high energy density lithium ion battery negative electrode material. Background technique: [0002] With the massive consumption of non-renewable energy and the increasing environmental pollution, it is very important to vigorously develop renewable complex energy. Lithium-ion batteries have been widely used in portable batteries due to their outstanding advantages such as high specific energy, long service life, green and pollution-free. fields such as electronic equipment and electric vehicles. Graphite is currently the most widely used negative electrode material for commercial lithium-ion batteries, but the theoretical capacity of graphite materials is only 372mAh / g, and the current commercially used graphite negative electrode materials a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M10/0525
CPCH01M4/364H01M10/0525Y02E60/10
Inventor 郭玉国徐泉李金熠殷雅侠
Owner BEIJING IAMETAL NEW ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com