Method for producing environment-friendly efficient electrophoretic paint

A production method and electrophoretic paint technology, applied in the field of coatings, can solve problems such as the environmental protection performance of electrophoretic paint needs to be improved, and achieve the effect of accelerating oxidation

Inactive Publication Date: 2016-08-24
GUANGDE RUIBANG PAINT
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CN104497786A (2015-4-8) discloses an electrophoretic paint, but the environmental performance of the electrophoretic paint needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing environment-friendly efficient electrophoretic paint
  • Method for producing environment-friendly efficient electrophoretic paint
  • Method for producing environment-friendly efficient electrophoretic paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] An environmentally friendly and efficient electrophoretic paint, comprising, by mass parts, 1 part of color paste, 4 parts of emulsion and 5 parts of deionized water;

[0060] The color paste formula includes 20 parts of main resin, 5 parts of alcohol ether co-solvent, 3 parts of organic acid, 0.3 part of emulsifier, 1 part of composite drier, 30 parts of deionized water and 15 parts of filler;

[0061] The emulsion formula includes, 40 parts of modified epoxy resin A, 10 parts of modified epoxy resin B, 10 parts of 4-4-diphenylmethane diisocyanate, 9 parts of curing agent, 3 parts of diethylenetriamine Diketimine and 2 parts of N-methylethanolamine, 0.1 part of emulsifier, 0.1 part of acetic acid and 30 parts of deionized water; the modified epoxy resin A formula includes, 10 parts of bisphenol A, 40 parts of epoxy Resin, 8 parts of solvent, 4 parts of bisphenol A polyoxyethylene ether, 10 parts of polyether diol with a number average molecular weight of 400-1500; the ...

Embodiment 2

[0076] Environmentally friendly and efficient electrophoretic paint, including by mass parts, 2 parts of color paste, 6 parts of emulsion and 5 parts of deionized water;

[0077] The color paste formula includes 30 parts of main resin, 10 parts of alcohol ether co-solvent, 8 parts of organic acid, 0.7 part of emulsifier, 5 parts of composite drier, 40 parts of deionized water and 20 parts of filler;

[0078]The emulsion formula includes, 50 parts of modified epoxy resin A, 20 parts of modified epoxy resin B, 30 parts of 4-4-diphenylmethane diisocyanate, 5 parts of curing agent, 4 parts of ketone of aminoethylethanolamine imine and 3 parts of diethanolamine, 2 parts of emulsifier, 1 part of acetic acid and 50 parts of deionized water; the modified epoxy resin A formula includes 20 parts of bisphenol A, 60 parts of epoxy resin, 16 parts of solvent, 16 parts of bisphenol A polyoxypropylene ether, 35 parts of polyether diamine with a number average molecular weight of 400 to 1500;...

Embodiment 3

[0094] Environmentally friendly and efficient electrophoretic paint, including by mass parts, 1.2 parts of color paste, 5 parts of emulsion and 6 parts of deionized water;

[0095] The color paste formula includes 25 parts of main resin, 8 parts of alcohol ether co-solvent, 5 parts of organic acid, 0.5 part of emulsifier, 4 parts of composite drier, 35 parts of deionized water and 15-20 parts of filler;

[0096] The preparation method of composite drier is

[0097] (1). Mix vanadium pentoxide and isooctanoic acid at a molar mass ratio of vanadium ions and isooctanoate ions of 1:4.5 for reaction, the reaction temperature is 225°C, and the reaction time is 0.6 hours;

[0098] (2). Continue to add manganese carbonate, add lanthanum carbonate or cerium carbonate, and isooctanoic acid for compound reaction, where the molar mass ion ratio of manganese ion to isooctanoate is 1:2.5, and lanthanum ion or cerium ion to isooctanoate ion The molar mass ratio is 1:4.5, the reaction temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of coating, in particular to a method for producing environment-friendly efficient electrophoretic paint. The environment-friendly efficient electrophoretic paint comprises 1-2 parts of color paste, 4-6 parts of emulsion and 5-7 parts of deionized water. The color paste in a formula comprises 20-30 parts of matrix resin, 5-10 parts of alcohol ether complex solubilizers, 3-8 parts of organic acid, 0.3-0.7 part of emulsifiers, 1-5 parts of compound driers, 30-40 parts of deionized water and 15-20 parts of fillers. The method for producing the environment-friendly efficient electrophoretic paint includes steps of A, preparing the color paste; B, preparing the emulsion; C, preparing electrophoretic paint. The method has the advantages that the emulsion and the color paste are in different compound formulas when modified, and accordingly the environment-friendly efficient electrophoretic paint which is cathode electrophoretic paint is safe and is environmentally friendly.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an environmentally friendly and efficient production method of electrophoretic paint. Background technique [0002] Since the advent of cathodic electrophoretic paint, because the formed paint film has excellent corrosion resistance and mechanical properties, and is suitable for automatic coating, it has quickly become popular in the automotive industry. The baking temperature range of traditional cathodic electrophoretic paint is generally 170 ~180°C. At present, many industrial workpieces are made of rubber, plastic and other materials, which are required to be dried together with electrophoretic paint after processing, so as to reduce the operating intensity of workers and control costs. However, such materials are easily deformed or melted when baked under high temperature conditions. In order to meet the needs of this type of process, there are very few varieties of low-temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D175/08C09D5/44C09D7/12C09F9/00C09D17/00
CPCC09D163/00C08L2205/025C08L2205/035C09D5/4457C09D5/4473C09D17/001C09F9/00
Inventor 陈爱林
Owner GUANGDE RUIBANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap