High hardness and ultraviolet resistant modified unsaturated polyester resin fiber reinforced plastic grid

A polyester resin, UV-resistant technology, applied in the field of FRP grating, can solve the problems of insufficient hardness and UV resistance.

Inactive Publication Date: 2016-09-21
NINGGUO CITY OF CAPE COMPOSITE MATERIAL LIMITED
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in practical applications, the requirements for FRP gratings are slightly different according to different occasions. The hardness and UV resistance of FRP gratings in the prior art cannot meet the needs of actual use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The present invention proposes a modified unsaturated polyester resin FRP grating with high hardness and UV resistance, and its raw materials include: 100 parts of modified unsaturated polyester resin, 40 parts of diphenylmethane bismaleimide , 10 parts of hydroquinone-type liquid crystal bismaleimide, 3.5 parts of styrene, 2.5 parts of carbon nanotubes, 6 parts of nano-calcium carbonate, 4 parts of nano-alumina, 2.5 parts of organically modified montmorillonite, ceramic powder 3.5 parts, 4 parts of glass fiber, 2.5 parts of benzotriazole, 3.5 parts of BYK-W940 wetting and dispersing agent, 5 parts of methyl ethyl ketone peroxide, 2.5 parts of ammonium polyphosphate, 6 parts of cobalt naphthenate, 2.5 parts of BYK-S740 additive 3 parts, 3 parts of silane coupling agent KH-560, 3.5 parts of curing agent, 4.5 parts of accelerator.

[0018] The modified unsaturated polyester resin was prepared according to the following process: 6 parts by weight of maleic anhydride, 3 par...

Embodiment 2

[0020] The present invention proposes a modified unsaturated polyester resin fiberglass grating with high hardness and UV resistance, and its raw materials include: 50 parts of modified unsaturated polyester resin, 60 parts of diphenylmethane bismaleimide , 5 parts of hydroquinone-type liquid crystal bismaleimide, 5 parts of styrene, 1 part of carbon nanotube, 9 parts of nano-calcium carbonate, 2 parts of nano-alumina, 4 parts of organically modified montmorillonite, ceramic powder 2 parts, 5 parts of glass fiber, 1 part of benzotriazole, 6 parts of BYK-W940 wetting and dispersing agent, 2 parts of methyl ethyl ketone peroxide, 4 parts of ammonium polyphosphate, 3 parts of cobalt naphthenate, 4 parts of BYK-S740 additive 1 part, 1 part of silane coupling agent KH-560, 5 parts of curing agent, 3 parts of accelerator.

[0021]The modified unsaturated polyester resin is prepared according to the following process: 3 parts by weight of maleic anhydride, 5 parts of ethylene glycol,...

Embodiment 3

[0023] The present invention proposes a modified unsaturated polyester resin FRP grating with high hardness and UV resistance, and its raw materials include: 150 parts of modified unsaturated polyester resin, 20 parts of diphenylmethane bismaleimide , 15 parts of hydroquinone-type liquid crystal bismaleimide, 2 parts of styrene, 4 parts of carbon nanotubes, 3 parts of nano-calcium carbonate, 6 parts of nano-alumina, 1 part of organically modified montmorillonite, ceramic powder 5 parts, 3 parts of glass fiber, 4 parts of benzotriazole, 1 part of BYK-W940 wetting and dispersing agent, 8 parts of methyl ethyl ketone peroxide, 1 part of ammonium polyphosphate, 9 parts of cobalt naphthenate, 1 part of BYK-S740 additive 5 parts, 5 parts of silane coupling agent KH-560, 2 parts of curing agent, 6 parts of accelerator.

[0024] The modified unsaturated polyester resin is prepared according to the following process: 9 parts by weight of maleic anhydride, 1 part of ethylene glycol, 5 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high hardness and ultraviolet resistant modified unsaturated polyester resin fiber reinforced plastic grid. The raw materials include: modified unsaturated polyester resin, diphenylmethane bismaleimide, hydroquinone type liquid crystal bismaleimide, styrene, carbon nanotube, nano calcium carbonate, nano alumina, organic modified montmorillonite, ceramic powder, glass fiber, benzotriazole, a BYK-W940 wetting dispersant, methyl ethyl ketone peroxide, poly nano titanium dioxide ammonium, cobalt naphthenate, a BYK-S740 assistant, a silane coupling agent KH-560, a curing agent and an accelerator. The fiber reinforced plastic grid provided by the invention has high hardness and strong ultraviolet resistance.

Description

technical field [0001] The invention relates to the technical field of FRP gratings, in particular to a modified unsaturated polyester resin FRP grating with high hardness and UV resistance. Background technique [0002] FRP grating is composed of glass felt skeleton and resin coating wrapped outside the skeleton. Because FRP grating is corrosion-resistant and strong in pressure resistance, the application of FRP has developed very fast in recent years. However, in practical applications, the requirements for FRP gratings are slightly different according to different occasions. The hardness and UV resistance of FRP gratings in the prior art cannot meet the requirements of actual use. Contents of the invention [0003] In order to solve the technical problems in the background technology, the present invention proposes a modified unsaturated polyester resin FRP grating with high hardness and UV resistance, which has high hardness and strong UV resistance. [0004] A modifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/01C08G63/547C08K13/06C08K3/22C08K7/24C08K3/26C08K3/34C08K7/14C08K5/3475
CPCC08F283/01C08G63/547C08K3/22C08K3/26C08K3/346C08K5/3475C08K7/14C08K7/24C08K13/06C08K2003/2227C08K2003/2241C08K2003/265C08K2201/011C08K2201/014
Inventor 黎嗣忠
Owner NINGGUO CITY OF CAPE COMPOSITE MATERIAL LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap