Heat-resistant rubber cable sheath material
A technology of cable sheath material and heat-resistant rubber, which is applied in the direction of rubber insulators and organic insulators, which can solve the problems of wear-resistant collision, temperature resistance, medium resistance, aging resistance and flame retardant properties that cannot meet the requirements, and the outer sheath of the cable is easily damaged. Problems such as shattering and damage to the surface of cable rubber, to achieve the effects of improving chemical stability, improving processing plasticity, and improving reinforcement
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0013] A heat-resistant rubber cable sheath material, made of the following raw materials in parts by weight (kg): magnesium stearate 3, mica powder 12, aluminum nitride 8, nano-silver fiber 4, urea 5, neoprene 55, Liquid paraffin 2, isoprene rubber 10, butadiene rubber 46, natural rubber 55, hollow glass microspheres 30, antioxidant BHT0.3, sulfur 2, organic bentonite 2, silane coupling agent kh5501, epoxy resin E4412, divinyl Triamine 0.06, accelerator DA0.1, silane coupling agent kh5702.6, appropriate amount of distilled water.
[0014] The heat-resistant rubber cable sheathing material is prepared through the following specific steps:
[0015] (1) Dry the hollow glass microspheres at 120°C for 2 hours, make a solution with absolute ethanol and distilled water at a mass ratio of 9:1, then add silane coupling agent KH550 to dissolve to make a 3% solution, and then add glass Sonicate the microbeads at 60°C for 60min, dry at 120°C for 3h after the end, cool down and set aside...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com