Cold application water-blocking type optical power cable filling past and production method thereof
A technology for filling paste and optical cables, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of affecting the electrical conductivity of cables, stress concentration, loss of filling paste, etc., achieve good water blocking effect, good water absorption effect, and reduce production costs Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example one
[0024] Pour the base oil composed of 60g hydrogenated white oil and 10g lubricating oil into the kettle and heat it to 70℃, then add 0.6g phenol antioxidant and 4.5g alkylphenol polyoxyethylene ether emulsifier into it in sequence , And 7.8g water blocking agent, fully stir for 5 hours, after the entire liquid is completely emulsified, quickly cool it to room temperature through a cooling device, and then add 6g white carbon black and 2g diatomaceous earth to the cooled mixture. Thickener, and 0.6g fatty acid ester dispersant, stir uniformly for 0.5 hours, and finally add 8.5g of cross-linked sodium polyacrylate polymer water-absorbing resin to the uniformly stirred mixture. After uniformly stirring, the mixture is mixed with a vacuum pump The air bubbles are drawn out, and the mixture is poured out of the container after the air extraction is completed.
Example Embodiment
[0025] Example two
[0026] Pour 75g of synthetic olefin oil base oil into the kettle and heat it to a temperature of 80°C, then add 0.2g of phenolic antioxidants and 0.3g of aniline antioxidants to it, and 3.5g of benzene. Ethyl phenol polyoxyethylene ether emulsifier and 8g water blocking agent, fully stirred for 5.5 hours, after the entire liquid is completely emulsified, quickly cool it to room temperature through a cooling device, and then add 5g bentonite to the cooled mixture to thicken it And 0.5g of paraffin wax dispersant. Stir uniformly for 0.8 hours. Finally, add 7.5g of polyacrylonitrile-based polymer water-absorbing resin to the uniformly stirred mixture. After uniformly stirring, the bubbles in the mixture are removed by a vacuum pump. Take it out, and pour the mixed liquid out of the container after the gas is pumped.
Example Embodiment
[0027] Example three
[0028] Pour the base oil of 80g hydrogenated white oil into the kettle and heat it to a temperature of 90°C, then add 0.2g phosphite triester antioxidant, 2g fatty alcohol polyoxyethylene ether emulsifier, and 8.5g hinder Water agent, fully stir for 6 hours, after the entire liquid is completely emulsified, quickly cool it to room temperature with a cooling device, and then add 3g diatomite thickener and 0.3g paraffin dispersant to the cooled mixture for uniformity Stir for 1 hour, and finally add 6g of polymer water-absorbing resin synthesized by polyacrylonitrile resin to the evenly stirred mixture. After uniformly stirring, the bubbles in the mixture are extracted by a vacuum pump, and the mixture is poured after the exhaustion is completed. Out of the container.
[0029] The index parameters of the above embodiment are as follows:
[0030] Technical index standard Example one Example two Example three Dropping Point150℃ >200 >200 >200 Hydrogen evolu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap