Solar heat-absorbing paint

A technology of solar heat absorption and coating, which is applied in the field of solar energy utilization, can solve the problems of poor weather resistance and water resistance, and achieve the effects of strong water resistance, high feasibility, and good adhesion

Inactive Publication Date: 2016-10-12
NANNING KEYU ENERGY TECH CO LTD
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a solar heat-absorbing coating, which can solve the problem of poor weather resistance and water resistance of the heat-absorbing coating, and can ensure the heat-absorbing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Solar energy heat-absorbing paint, the mass parts of raw materials are:

[0028] Acrylate modified compound emulsion: 7kg acrylate emulsion, 6kg polyurethane modified acrylate emulsion, 6kg epoxy resin modified acrylate emulsion, 6kg silicone modified acrylate emulsion

[0029] Fluorocarbon surfactant 2kg

[0030] Absorbent: nano manganese dioxide 20kg, nano carbon powder 15kg

[0031] Hardener: dry oil alkyd resin 7kg

[0032] Absorption Enhancer 1kg

[0033] Solvent: ethanol 10kg

[0034] Thickener 0.5kg

[0035] Film-forming agent: modified silkworm protein-gelatin 35kg

[0036] Dispersant: sodium lauryl sulfate 2kg, polyethylene glycol or polyvinylpyrrolidone 3kg

[0037] The step of preparing modified acrylate emulsion according to above-mentioned raw material is as follows:

[0038] (1) The preparation method of polyurethane-modified acrylate emulsion is as follows: in a nitrogen atmosphere, heat 5kg of acrylate to 70°C, the stirring speed is 100r / min, and ...

Embodiment 2

[0044] A kind of solar heat absorbing paint, raw material mass fraction is:

[0045] Acrylate modified composite emulsion: 8kg acrylate emulsion, 8kg polyurethane modified acrylate emulsion, 10kg epoxy resin modified acrylate emulsion, 9kg silicone modified acrylate emulsion

[0046] Fluorocarbon surfactant 6kg

[0047] Absorbent: nano manganese dioxide 30kg, nano carbon powder 25kg

[0048] Curing agent 12kg

[0049] Absorbent: 30kg of nano-nickel powder, 25kg of carbon nanotubes

[0050] Absorption Enhancer 3kg

[0051] Solvent: Propylene Glycol 20kg

[0052] Film-forming agent: modified silkworm protein-gelatin 50kg

[0053] Dispersant: sodium lauryl sulfate 4kg, polyethylene glycol or polyvinylpyrrolidone 6kg

[0054] Thickener: 0.7kg

[0055] The step of preparing modified acrylate emulsion according to above-mentioned raw material is as follows:

[0056] (1) The preparation method of polyurethane-modified acrylate emulsion is as follows: in a nitrogen atmosphere,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses solar heat-absorbing paint which is prepared from the following components in parts by weight: 25-35 parts of an acrylate-modified composite emulsion, 2-6 parts of a fluorocarbon surfactant, 35-55 parts of a nano carbon powder and manganese dioxide mixture, 7-12 parts of a curing agent, 50-35 parts of a film forming agent, 1-3 parts of an absorption enhancer, 10-20 parts of a solvent, 5-10 parts of dispersants, and 0.5 to 0.7 part of a thickening agent, wherein the dispersants are sodium dodecyl sulfate and polyethylene glycol / polyvinyl pyrrolidone; the film forming agent is modified fibroin-gelatin; nano carbon powder is 10-20 nm in particle size, 150-180 m<2> / g in specific surface area and 90-95% in carbon content. The prepared solar heat-absorbing paint has excellent weather resistance and water resistance under the outdoor condition, the preparation process is simple and easy to understand, and the heat absorption efficiency of the heat-absorbing paint is further ensured.

Description

technical field [0001] The invention relates to the field of solar energy utilization, in particular to a solar heat absorbing paint. Background technique [0002] Solar thermal application is one of the simplest, most direct, and most effective ways for human beings to utilize solar energy. However, due to the small and discontinuous energy density of solar energy after reaching the earth, it has brought difficulties to large-scale development and utilization. For a long time, how to convert low-grade solar energy into high-grade thermal energy and enrich solar energy so as to maximize the use of solar energy has become a hot topic of research. Among the existing photothermal application technologies, selective absorption coating technology is recognized as the core technology, which plays a vital role in improving the efficiency of solar thermal conversion and promoting large-scale solar thermal applications. [0003] As we all know, solar energy absorbing coatings are ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D189/00C09D133/04C09D175/04C09D163/00C09D5/18C09D5/32C09D5/08C09D5/16C09D7/12
CPCC09D189/00C08K2201/011C08L2201/02C08L2201/08C08L2205/025C08L2205/035C09D5/08C09D5/1656C09D5/1687C09D5/18C09D5/32C08L89/00C08L33/04C08L67/08C08L75/04C08L63/00C08L43/04C08K2003/2262C08K3/04
Inventor 马昭键金建荣陈会杰梁文莫小青陆竣行蒙献芳
Owner NANNING KEYU ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com