Multicolor ageing-resistant spraying-free polydicyclopentadiene composite material, and preparation method and application thereof

A technology of polydicyclopentadiene and composite materials, which is applied in the direction of building insulation materials, building components, building structures, etc., and can solve the problems of polydicyclopentadiene materials not being widely used, increasing process costs, and being unfriendly to the environment , to achieve the effect of bright colors, simple preparation process and excellent corrosion resistance

Inactive Publication Date: 2016-12-21
SHANGHAI COACHCHEM TECH
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, specified colors and color effects are required in many exterior parts, while traditional polydicyclopentadiene materials are black or dark brown, and most of them require additional painting processes, which are not environmentally friendly and costly increase, which makes the polydicyclopentadiene material with excellent mechanical properties not widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multicolor ageing-resistant spraying-free polydicyclopentadiene composite material, and preparation method and application thereof
  • Multicolor ageing-resistant spraying-free polydicyclopentadiene composite material, and preparation method and application thereof
  • Multicolor ageing-resistant spraying-free polydicyclopentadiene composite material, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Embodiment one, composite material 1#

[0064] A. Manufactured from raw materials in the following weight percentages:

[0065]

[0066] B. Preparation method:

[0067] (1), red toner (>5000 mesh), dicyclopentadiene, styrene, silicon dioxide, triphenylphosphine, p-tert-butylphenol, 2,4,6-tri(2'-butoxy Base phenyl)-1,3,5-triazine and 1 / 2 weight of toluene are fully mixed to obtain a slurry;

[0068] (2), will Dissolved in the remaining toluene to obtain a transparent solution;

[0069] (3) After fully mixing the solutions of steps (1) and (2), keep them below 30°C and inject them into the mold through an injection molding machine;

[0070] (4) The mold is raised to 65 degrees and kept at 65 degrees for 30 seconds to cure.

[0071] (5), product demoulding.

[0072] C. Spray-free products such as image 3 shown.

[0073] D. The performance indicators are as follows:

[0074] Color difference value ΔE: 3.2 (310nm wavelength xenon headlights and 100 degrees high...

Embodiment 2

[0076] Embodiment two, composite material 2#

[0077] A. Manufactured from raw materials in the following weight percentages:

[0078]

[0079] B. Preparation method:

[0080] (1), dark blue ester-soluble color paste, dicyclopentadiene, butadiene, carbon fiber, diethylene glycol dibutyl ether, tert-butyl hydroquinone, 2-hydroxy-4-methoxydi Benzophenone and 2 / 3 weight of methylene chloride are fully mixed to obtain a slurry;

[0081] (2), will Dissolved in the remaining dichloromethane to obtain a clear solution;

[0082] (3) After fully mixing the solutions of steps (1) and (2), keep the temperature below 30°C and inject them into the mold through an injection molding machine.

[0083] (4) The mold is raised to 70°C and kept at 70°C for 45 seconds to cure.

[0084] (5), product demoulding.

[0085] C. Transparent spray-free products such as Figure 4 shown.

[0086] D. The performance indicators are as follows:

[0087] Color difference value ΔE: 2.8 (310nm wavele...

Embodiment 3

[0090] A. Manufactured from raw materials in the following weight percentages:

[0091]

[0092]

[0093] B. Preparation method:

[0094] (1), white ivory color paste, dicyclopentadiene, butyl methacrylate, glass fiber, 2,6-di-tert-butyl p-cresol, 2-(2'-hydroxy-3',5'- Di-tert-phenyl)-5-chlorinated benzotriazole, aniline and THF of 3 / 5 weight are fully mixed to obtain a slurry;

[0095] (2), will Dissolved in the remaining tetrahydrofuran to obtain a transparent solution;

[0096] (3) After fully mixing the solutions of steps (1) and (2), keep them below 30°C and inject them into the mold through an injection molding machine;

[0097] (4) The mold is raised to 60°C and kept at 60°C for 15 seconds to cure.

[0098] (5), product demoulding.

[0099] C. Highlight spray-free products such as Figure 5 shown.

[0100] D. The performance indicators are as follows:

[0101] Color difference value ΔE: 4.5 (310nm wavelength xenon headlights and 100 degrees high temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a multicolor ageing-resistant spraying-free polydicyclopentadiene composite material, and a preparation method and an application thereof. Raw materials for preparing the composite material comprise 35-65% of dicyclopentadiene, 1-15% of a copolymer, 10-35% of a functional filler, 0.05-5% of environmentally-friendly color paste or high-mesh toner, and 0.01-0.1% of a ruthenium carbene catalyst. The material is integrally formed after high-efficiency dissolution of the environmentally-friendly color paste or the high-mesh toner with dicyclopentadiene, full mixing of the obtained material with other ingredients, reaction of the obtained mixture with a curing agent, and injection molding polymerization. The spraying-free polydicyclopentadiene composite material has the advantages of brilliant color, ageing resistance, long life, superior mechanical performances, and simple repairing of minimal scratches, and the preparation method is simple.

Description

technical field [0001] The invention belongs to the technical field of new materials, and in particular relates to a multi-color, anti-aging spray-free polydicyclopentadiene composite material and its preparation method and application. Background technique [0002] As an engineering plastic, polydicyclopentadiene (abbreviated as PDCPD) is a new type of engineering material with good comprehensive mechanical and physical properties. It also has high impact strength, high flexural modulus (toughness index), high Hardness, high heat distortion temperature and good anti-aging performance, flexible and simple manufacturing process, especially suitable for making ultra-thin parts with high strength and large area. [0003] It has shown a very broad application prospect in the fields of automobile industry, construction machinery manufacturing, medical and sports equipment, petrochemical pipelines and civil facilities. Especially famous companies such as Caterpillar, Terex, Liebh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F232/08C08F212/08C08F220/18C08F212/12C08F2/44C08F2/38C08F4/80C08K13/02C08K13/04C08K7/06C08K7/14C08K3/36C08K5/13C08K5/3492C08K5/132C08K3/34C08L45/00C08L95/00C08L25/06
CPCC08F2/38C08F2/44C08F4/80C08F232/08C08K3/346C08K3/36C08K5/13C08K7/06C08K13/02C08K13/04C08L45/00C08L2201/08C08L95/00C08K5/132C08L25/06C08K7/14C08F220/1804
Inventor 吴江张伟
Owner SHANGHAI COACHCHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap