Hyperbranched polyether modified organosilicon defoaming agent with lasting foam inhibiting effect and preparation method thereof

A technology of organosilicon defoamer and hyperbranched polyether, which is applied in chemical instruments and methods, separation methods, foam dispersion/prevention, etc., can solve problems such as limited application and unsatisfactory shear resistance, and achieve improved Foam efficiency, excellent shear resistance, good chemical stability

Inactive Publication Date: 2017-01-11
合肥新万成环保科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polyether modified silicone oil defoamer currently studied is not ideal in terms of shear resistance, which limits its application in some fields such as coatings, petrochemicals, and papermaking.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A hyperbranched polyether modified silicone defoamer with long-lasting antifoaming effect, which is composed of the following raw materials in parts by weight (kg): polysiloxane 40, hyperbranched polyether 23, allyl glycidyl ether 26 , propylene oxide 58, double metal cyanide complex 0.5, isopropanol 67, chloroplatinic acid catalyst 0.5, ultrafine aluminum silicate 5, sorbitol 2, Tween 60 2, sodium carboxymethylcellulose 3 , appropriate amount of deionized water, white carbon black 7, methyltriethoxysilane 2, ammonium carbonate 1, potassium hydroxide 1.6.

[0025] Specific steps are as follows:

[0026] (1) Preparation of allyl-terminated hyperbranched polyether:

[0027] Add hyperbranched polyether and double metal cyanide complex into a high-pressure reactor, vacuumize and dehydrate, and replace with nitrogen for 3 times, after heating up to 120°C, feed 2 / 3 parts of propylene oxide to control the temperature of the reaction process At about 135°C, when the pressure ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Branching factoraaaaaaaaaa
Branching factoraaaaaaaaaa
Login to view more

Abstract

The invention discloses a hyperbranched polyether modified organosilicon defoaming agent with a lasting foam inhibiting effect, composed of the following raw materials in parts by weight: 28-45 partsof polysiloxane, 16-26partsof hyperbranched polyether, 20-28 partsof allyl glycidyl ether, 45-60 partsof epoxy propane, 0.3-0.7 partof bimetal cyanide complex, 50-70 partsof isopropanol, 0.3-0.7 partof chloro-platinic acid catalyst, 3-7 partsof superfine aluminum silicate, 1-2partsof sorbitol, 1-2 partsof tween 60, 2-4 partsof sodium cellulose glycolate, an appropriate amount of de-ionized water, 4-10 partsof white carbon black, 1-2 partsof methyl triethoxy silane, 0.5-1partof ammonium carbonate and 0.6-2 partsof potassium hydroxide. The hyperbranched polyether modified organosilicon defoaming agent takes the hyperbranched polyether containing a large quantity of hydroxyl groups at the terminals as a raw material to prepare allyl-terminated hyperbranched polyether, and a polyether terminal modified double bond structure is used to generate silicon hydrogen addition reaction with the polysiloxane to synthesize hyperbranched polyether modified polysiloxane, and the defoaming agent has excellent shear resistant performance.

Description

technical field [0001] The invention relates to the field of chemical products, in particular to a hyperbranched polyether modified organic silicon defoamer with a long-lasting antifoaming effect and a preparation method thereof. [0002] technical background [0003] Defoamers, also known as defoamers or defoamers, will produce many foams that affect production during industrial production, and defoamers need to be added. It is widely used to remove harmful foam produced in the production process of latex, textile sizing, food fermentation, biomedicine, paint, petrochemical, papermaking, industrial cleaning, sewage treatment and other industries. [0004] The current defoamers can be divided into two categories: silicone type and polyether type according to the composition. Due to the addition of emulsifiers and other additives, silicone defoamers are prone to defects such as demulsification and oil floating at higher temperatures; Polyether-type defoamers are mostly polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D19/04C08G81/00C08G65/28
CPCB01D19/0404B01D19/0409B01D19/0413B01D19/0427B01D19/0463B01D19/0468B01D19/0472C08G65/2609C08G81/00
Inventor 杨成勇杨云胡亚琼任意何庆海
Owner 合肥新万成环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap