High polymer material and metal composite material, and preparation process therefor

A technology of polymer materials and composite materials, which is applied in the field of composite materials, can solve problems such as misjudgment and key switch function failure, and achieve the effects of preventing impact, good electrical conductivity, and offsetting thermal expansion

Active Publication Date: 2017-02-01
NANTONG MEMTECH TECH
View PDF16 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the contact resistance is too large, it will cause the function of the key switch to fail and misjudgment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High polymer material and metal composite material, and preparation process therefor
  • High polymer material and metal composite material, and preparation process therefor
  • High polymer material and metal composite material, and preparation process therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Formula A: the mixing rubber (SE4705U of Dow Corning Company for selection) 100 (parts by weight, the same below) containing the methyl vinyl silicone rubber of fumed white carbon black, simethicone oil (XiameterPMX-200 for selection of Dow Corning Company, 1000cs ) 50, vinyl tri-tert-butylperoxysilane (VTPS) 1, dicumyl peroxide (DCP) 0.5.

[0030] Formulation B: SE 4705U 100, VTPS 1, DCP 0.5.

[0031] Lay the mixed films of formula A and formula B respectively with a nickel expanded mesh (the purity of nickel is not less than 99.5%) with a thickness of 0.25mm, a hole diameter of 0.5mm, and a hole spacing of 0.25mm, and put them on a Teflon-coated In the mold cavity of the layer, under the temperature condition of 175° C., press and vulcanize for 10 minutes to form a thin sheet with a thickness of 0.25 mm. This sheet was die cut into small discs with a diameter of 3.0 mm. Using ethanol as a solvent, the small discs prepared by formula A and formula B were extracted wi...

Embodiment 2

[0034] One side of the nickel expanded metal in Example 1 is pasted with a 0.025mm thick polyimide (PI) self-adhesive film, then compounded with the compounded glue of formula A and the nickel expanded metal to make a 0.8mm thick composite sheet material. The PI self-adhesive film was removed, and punched into small discs with a diameter of 2.0-5.0 mm. Soak in solvent gasoline to extract the silicone oil contained in the small disc silicone rubber, and the rubber in the holes of the nickel plate mesh shrinks ( image 3 ).

[0035] These small discs serve as electrical contacts and are also capable of conducting electricity well at elevated ambient temperatures. This is because when the temperature rises, such as from 25°C to 80°C, even if the rubber in the porous metal hole has a low expansion coefficient, it will not protrude from the surface of the porous metal (such as Figure 4 shown).

Embodiment 3

[0037] Formula C: PVC (P=500) 100, ethylene-vinyl acetate-carbon monoxide copolymer (select Elvaloy 741 of DuPont Company) 45, dioctyltin dilaurate 2, epoxy soybean oil 3.5, polyethylene wax 0.3, monostearin Glyceride 3, trioctyl trimellitate 65, polyvinyl butyral (molecular weight 20000) 5. The addition of polyvinyl butyral is to improve the adhesion of PVC to metal.

[0038] According to formula C, put all the materials into a high-speed mixer for mixing and stirring. The time is controlled at about 15 minutes, and the temperature is 110-120°C. Let the PVC powder absorb the plasticizer without stickiness. Put it into a low-speed cooling mixer while stirring. Cooling; when cooling to about 25°C, release the material. This material is applied to a multi-layer stainless steel sintered net made of 5 layers of 80-mesh AISI 304 stainless steel plain weave net through special lamination pressing and vacuum sintering processes, or it is plasticized at 160 °C by a double-roll mill. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high polymer material and a metal composite material, and a preparation process therefor. The high polymer material containing an extractable material and a porous metal are compounded and formed under a certain condition to prepare a sheet; and then the prepared sheet is subjected to solvent extraction to enable the extractable material therein to be extracted so as to obtain the composite material, wherein the high polymer material of the composite material is shrunk or collapsed. According to the composite material prepared by the preparation method, the porous metal protrudes out of the surface of the conductive composite material, so that the composite material is more suitable for being used as an electric contact material.

Description

technical field [0001] The invention relates to the field of composite materials, more specifically, the invention relates to a conductive material composited by polymer materials and metals, and the composite material can be used to make electrical contacts in conductive plates and keys. Background technique [0002] Various rubbers are inherently electrically insulating. So far, all conductive rubbers are not intrinsic. Although there are intrinsic types of conductive plastics, intrinsic conductive plastics have high production costs, difficult production processes, poorer conductivity and stability than metal conductors, and have not yet been mass-produced and applied. The currently widely used conductive polymer materials are generally composite polymer materials, which are composed of polymer materials (such as rubber and plastic) and conductive fillers. Adding conductive carbon black to the polymer substrate can prepare antistatic polymer materials and conductive pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01H1/04
CPCH01H1/04H01B1/22B29K2705/00
Inventor 韩辉升丁阳张红梅陆婷施捷孙强
Owner NANTONG MEMTECH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap