Method for preparing crosslinking waterborne acrylic emulsion

A technology of water-based acrylic acid and acrylate, applied in the field of preparation of cross-linked water-based acrylic emulsion, can solve problems such as limited application, and achieve the effect of solving yellowing and good wear resistance

Active Publication Date: 2017-02-22
厦门市禾合科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a contradiction between low-temperature film-forming and high hardness in water-based acrylic resin coatings, which limits its wide application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing crosslinking waterborne acrylic emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] First, mix 100 parts of glutaraldehyde aqueous solution and 70 parts of methanol, adjust the pH value to 1-2 with dilute hydrochloric acid, reflux at 60°C for 1 hour, cool to room temperature, add 70 parts of 30% formaldehyde aqueous solution and 1 part of Na 2 CO 3 , heated up again to 90° C. for reflux for 2 hours, cooled down and discharged. Unreacted methanol and formaldehyde were distilled off under reduced pressure, and water was added to obtain a modified glutaraldehyde crosslinking agent with a concentration of 20%.

[0024] Add 140 parts of water, 1 part of sodium dodecylbenzenesulfonate, and 2 parts of OP-10 emulsifier into the pre-emulsification tank, start stirring, raise the temperature to 40-50°C, and evenly add 9 / 10 of acrylate mono Liquid mixture (106 parts of butyl acrylate, 86 parts of methyl methacrylate, 8 parts of methacrylic acid and 3.55 parts of acrylamide), dripping in 0.5~1h. Add 80 parts of water, 0.5 parts of sodium dodecylbenzene sulfonate...

Embodiment 2

[0026] First, mix 100 parts of glyoxal aqueous solution and 70 parts of methanol, adjust the pH value to 1-2 with dilute hydrochloric acid, reflux at 60°C for 1 hour, cool down to room temperature, add 70 parts of 30% formaldehyde aqueous solution and 1 part of Na 2 CO 3 , heated up again to 90° C. for reflux for 2 hours, cooled down and discharged. Unreacted methanol and formaldehyde were distilled off under reduced pressure, and water was added to obtain a modified glyoxal crosslinking agent with a concentration of 20%.

[0027] Add 140 parts of water, 0.75 parts of sodium lauryl sulfate, and 0.75 parts of OP-10 emulsifier into the pre-emulsification tank, start stirring, raise the temperature to 40-50°C, and evenly add 9 / 10 acrylate monomer dropwise to mix Liquid (113 parts of butyl methacrylate, 10 parts of methyl methacrylate, 10 parts of diethylene glycol diacrylate, 40 parts of styrene, 20 parts of methacrylic acid, 7 parts of acrylamide), drop in 0.5-1h . Add 80 par...

Embodiment 3

[0029] First, mix 100 parts of succinic dialdehyde aqueous solution and 70 parts of methanol, adjust the pH value to 1-2 with dilute hydrochloric acid, reflux at 60°C for 1 hour, cool to room temperature, add 70 parts of 30% formaldehyde aqueous solution and 1 part of Na 2 CO 3 , heated up again to 90° C. for reflux for 2 hours, cooled down and discharged. Unreacted methanol and formaldehyde were distilled off under reduced pressure, and water was added to obtain a modified succinaldehyde crosslinking agent with a concentration of 20%.

[0030] Add 140 parts of water, 0.6 parts of dodecyl diphenyl ether sulfonic acid disodium salt, 2.4 parts of TX-100 emulsifier into the pre-emulsification tank, start stirring, raise the temperature to 40-50°C, and evenly add 9 / 10 Acrylic monomer mixture (95 parts of butyl acrylate, 10 parts of hydroxyethyl acrylate, 10 parts of isobornyl methacrylate, 40 parts of methyl methacrylate, 30 parts of α-methylstyrene, 10 parts of acrylic acid , m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing crosslinking waterborne acrylic emulsion. The method comprises the following steps that A, a modified dialdehyde crosslinking agent is prepared, wherein the general formula of the dialdehyde crosslinking agent is CHO-R-CHO, R is an alkyl group of a linear chain or branched chain or an aryl group of a linear brain or branched chain; B, acrylate copolymer emulsion containing amino functional groups is prepared; C, the modified dialdehyde crosslinking agent obtained in the step A is added into the acrylate copolymer emulsion obtained in the step B, the crosslinking waterborne acrylic emulsion is obtained, and the crosslinking reaction equation is 2P-NH2+CHO-R-CHO-P-N=H-R-CH=N-P+H2O. An obtained crosslinking film has good abrasion resistance, chemical resistance, water resistance and tensile strength, and the problem of yellowing is successfully solved.

Description

technical field [0001] The invention relates to a preparation method of cross-linked water-based acrylic emulsion. Background technique [0002] Due to its low VOC, water-based coatings are an important direction for the development of environmentally friendly coatings. Acrylic resin water-based coatings have attracted much attention due to their excellent weather resistance, acid and alkali resistance, and water resistance. However, there is a contradiction between low-temperature film-forming and high hardness in water-based acrylic resin coatings, which limits its wide application. In order to solve this problem, the most effective way is to introduce a cross-linking agent to make the molecules form a cross-linked structure. If the emulsion polymer film can form a cross-linked structure, it can not only improve the physical and chemical stability of the coating film, but also improve its tensile strength and wear resistance. Contents of the invention [0003] The obj...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J3/24C08K5/07C08L33/08C08L33/12C08L25/14C08F220/18C08F220/14C08F220/06C08F220/56C08F212/08C08F222/14C08F212/12C08F220/28C08F222/38
CPCC08F212/08C08F220/14C08F220/18C08J3/24C08K5/07C08J2333/08C08F220/1804C08L33/08C08L33/12C08L25/14C08F220/1812C08F220/06C08F222/385C08F220/56C08F222/102C08F220/281C08F220/58C08F220/1808C08F212/12
Inventor 高屹陈佳宁
Owner 厦门市禾合科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com