Anti-cracking exterior wall coating used for building

A technology for exterior wall coatings and construction, applied in the direction of polyester coatings, coatings, etc., can solve problems such as cracking, and achieve the effects of good water resistance, good cracking resistance, and not easy to fall off

Active Publication Date: 2017-04-26
湖南鹏志新材料有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the current exterior wall coatings have sufficient anti-aging properties after being exposed to wind and sun, they often crack within their theoretical lifespan.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-cracking exterior wall coating used for building

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] An anti-cracking architectural exterior wall coating, which is formulated according to the following proportions: styrene-acrylic emulsion 25kg, methyl acrylate 12kg, acrylic acid modified alkyd resin 10kg, dimethyldichlorosilane 5kg, unsaturated poly Ester resin 5kg, bisphenol A diglycidyl ether 9kg, heavy calcium powder 1kg, sodium bentonite 2kg, sepiolite fiber 0.5kg, zinc oxide 1.5kg, magnesium stearate 5kg, triglycidyl isocyanurate 0.5kg , water 5kg, diethylenetriamine 0.3kg, other additives 1kg, the acid value of the unsaturated polyester resin is 110, and the epoxy value of bisphenol A diglycidyl ether is 0.48-0.5mol / 100g.

Embodiment 2

[0026] An anti-cracking architectural exterior wall coating, which is formulated according to the following proportions: 34kg of styrene-acrylic emulsion, 15kg of methyl acrylate, 15kg of acrylic acid modified alkyd resin, 3kg of dimethyldichlorosilane, unsaturated poly 3kg of ester resin, 7kg of bisphenol A diglycidyl ether, 3kg of heavy calcium powder, 5kg of sodium bentonite, 1.5kg of sepiolite fiber, 1kg of zinc oxide, 3kg of magnesium stearate, 0.3kg of triglycidyl isocyanurate, 10kg of water, 0.5kg of diethylenetriamine, 3kg of other additives, the acid value of the unsaturated polyester resin is 80, and the epoxy value of bisphenol A diglycidyl ether is 0.48-0.5mol / 100g.

Embodiment 3

[0028] An anti-cracking architectural exterior wall coating, which is formulated according to the following proportions: styrene-acrylic emulsion 27kg, methyl acrylate 14kg, acrylic acid modified alkyd resin 12kg, dimethyldichlorosilane 3kg, unsaturated poly 5kg of ester resin, 8kg of bisphenol A diglycidyl ether, 1kg of heavy calcium powder, 5kg of sodium bentonite, 1.5kg of sepiolite fiber, 1kg of zinc oxide, 5kg of magnesium stearate, 0.5kg of triglycidyl isocyanurate, 5kg of water, 0.4kg of diethylenetriamine, and 3kg of other additives. The acid value of the unsaturated polyester resin is 80, and the epoxy value of bisphenol A diglycidyl ether is 0.48-0.5 mol / 100g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of building coating, and in particular relates to an anti-cracking exterior wall coating used for a building. The exterior wall coating comprises the following components in parts by weight: 25-34 parts of styrene-acrylic emulsion, 12-15 parts of methyl acrylate, 10-15 parts of acrylic modified alky resin, 3-5 parts of dimethyl dichlorosilane, 3-5 parts of unsaturated polyester resin, 7-9 parts of bisphenol A diglycidyl ether, 1-3 parts of ground calcium carbonate powder, 2-5 parts of sodium bentonite, 0.5-1.5 parts of sepiolite fiber, 1-1.5 parts of zinc oxide, 3-5 parts of magnesium stearate, 0.3-0.5 part of triglycidyl isocyanurate, 0.3-0.5 part of diethylenetriamine, 5-10 parts of water and 1-3 parts of other auxiliaries. The exterior wall coating provided by the invention has excellent ageing-resistant performance so as to have better anti-cracking performance, has better water resistance so as to be incapable of being damp easily, has stronger bonding power so as to be incapable of falling off easily and has better stability so as to be incapable of cracking easily.

Description

technical field [0001] The invention relates to the technical field of architectural coatings, in particular to an anti-cracking architectural exterior wall coating. Background technique [0002] Wall paint refers to the decoration and protection of the building wall, making the building wall beautiful and tidy, and at the same time protecting the building wall and prolonging its service life. According to the classification of building walls, wall coatings include two major parts: interior wall coatings and exterior wall coatings. Interior wall coatings focus on decoration and environmental protection; exterior wall coatings focus on protection and durability. In addition to its own decorative and protective functions, wall paint is also developing towards a colorful, fashionable, healthy and environmentally friendly trend. People hope that the decorative effect will be radiant and beautiful, noble, elegant, romantic, and warm; they also hope that the material itself is p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D167/08C09D167/06C09D7/12
CPCC08L2205/02C08L2205/03C09D7/61C09D7/63C09D7/70C09D125/14C08L67/08C08L67/06C08K13/04C08K7/10C08K2003/2296C08K2003/265C08K5/098C08K3/346
Inventor 谢咸颂王建才姚创张浩矗秦保刚孙杰
Owner 湖南鹏志新材料有限公司