An electrostatic spraying, LED lamp technology, applied in polyester coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of untimely cooling LED lamp life, affecting the luminous efficiency of lamps, and the heat dissipation effect needs to be improved. , to achieve the effect of excellent synergy, low curing temperature and high brittleness improvement

Inactive Publication Date: 2017-05-17
TIANCHANG JINLING ELECTRONICS
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to the characteristics of energy saving, good applicability, short response time, and environmental protection, LED lights have been used in mobile phones, table lamps, home appliances and other daily household appliances and machinery production, but their prices are relatively high. The rapid expansion and prolonging the service life have also become an urgent problem to be solved
[0003] LED lights still have a certain amount of heat during use, and failure to dissipate heat in time is an important reason for shortening the life of LED lights
In order to solve the problem that the luminous efficiency of the lamp is affected by the heat generated during the use of the lamp and the service life of the lamp is shortened, the current method used is to coat a layer of heat-dissipating paint on the lamp, but the heat dissipation effect of the existing heat-dissipating paint has yet to be solved. improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The present invention proposes a special heat-dissipating electrostatic spraying paint for LED lamps. Its raw materials include, by weight, 100 parts of epoxy resin, 25 parts of polyurethane, 35 parts of unsaturated polyester resin, 8 parts of maleic anhydride, methyl tetra 20 parts of hydrophthalic anhydride, 5 parts of isophthalic anhydride, 8 parts of 2,4,6-tris(dimethylaminomethyl)phenol, 2 parts of trimethylolpropane, 2-butyl-2-ethyl- 3.5 parts of 1,3-propanediol, 5 parts of magnesium nitride, 30 parts of modified carbon nanotubes, 2 parts of graphene, 10 parts of nano calcium carbonate, 2 parts of cerium oxide, 10 parts of silicon micropowder, hexamethyldisilazane 2 parts, 8 parts of phenyltrimethoxysilane, 1 part of phenylmethyldimethoxysilane, 1.5 parts of dibutyltin dilaurate, 0.1 part of leveling agent, 1 part of benzoin;

[0019] Wherein, the epoxy resin is a mixture of dicyclopentadiene dioxide epoxy resin and o-cresol novolak epoxy resin.

Embodiment 2

[0021] The present invention proposes a special heat-dissipating electrostatic spraying paint for LED lamps. Its raw materials include by weight: 100 parts of epoxy resin, 40 parts of polyurethane, 15 parts of unsaturated polyester resin, 18 parts of maleic anhydride, methyl tetra 8 parts of hydrophthalic anhydride, 12 parts of isophthalic anhydride, 2 parts of 2,4,6-tris(dimethylaminomethyl)phenol, 5 parts of trimethylolpropane, 2-butyl-2-ethyl- 1 part of 1,3-propanediol, 15 parts of magnesium nitride, 10 parts of modified carbon nanotubes, 10 parts of graphene, 2 parts of nano calcium carbonate, 5 parts of cerium oxide, 2 parts of silicon micropowder, hexamethyldisilazane 5 parts, 3 parts of phenyltrimethoxysilane, 5 parts of phenylmethyldimethoxysilane, 0.5 part of dibutyltin dilaurate, 1.2 parts of leveling agent, 0.1 part of benzoin;

[0022] Wherein, the epoxy resin is a mixture of dicyclopentadiene dioxide epoxy resin and o-cresol novolak epoxy resin.

Embodiment 3

[0024] The present invention proposes a heat-dissipating electrostatic spray coating for LED lamps, whose raw materials include, by weight, 100 parts of epoxy resin, 37 parts of polyurethane, 20 parts of unsaturated polyester resin, 16 parts of maleic anhydride, methyl tetra 12 parts of hydrophthalic anhydride, 10 parts of isophthalic anhydride, 3.8 parts of 2,4,6-tris(dimethylaminomethyl)phenol, 4 parts of trimethylolpropane, 2-butyl-2-ethyl- 1.6 parts of 1,3-propanediol, 13 parts of magnesium nitride, 18 parts of modified carbon nanotubes, 8.5 parts of graphene, 6 parts of nano calcium carbonate, 3.5 parts of cerium oxide, 5 parts of silicon micropowder, hexamethyldisilazane 4 parts, 5 parts of phenyltrimethoxysilane, 4 parts of phenylmethyldimethoxysilane, 0.8 part of dibutyltin dilaurate, 1 part of leveling agent, 0.5 part of benzoin;

[0025] Wherein, the epoxy resin is a mixture of dicyclopentadiene dioxide epoxy resin and o-cresol novolac epoxy resin in a weight ratio o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a special heat dissipation electrostatic spraying coating for an LED lamp. The heat dissipation electrostatic spraying coating is prepared from the following raw materials: epoxy resin, polyurethane, unsaturated polyester resin, maleic anhydride, methyl tetrahydrophthalic anhydride, m-phthalic anhydride, 2,4,6-tri(dimethylamine methyl) phenol, trimethylolpropane, 2-butyl-2-ethyl-1,3-propylene glycol, magnesium nitride, modified carbon nano tube, graphene, nano calcium carbonate, cerium oxide, silica powder, hexamethyl-disilazane, phenyltrimethoxysilane, phenyl methyl dimethoxysilane, dibutyltin dilaurate, a leveling agent and benzoin, wherein the epoxy resin is a mixture of biscyclopentadiene dioxide epoxy resin and o-cresol formaldehyde epoxy resin. The heat dissipation electrostatic spraying coating is high in heat dissipation property and high in high temperature resistance, and the service life of the LED lamp can be prolonged.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a special heat-dissipating electrostatic spray coating for LED lamps. Background technique [0002] Due to the characteristics of energy saving, good applicability, short response time, and environmental protection, LED lights have been used in mobile phones, table lamps, home appliances and other daily household appliances and machinery production, but their prices are relatively high. Rapid expansion and prolonging the service life have also become urgent problems to be solved. [0003] LED lights still have a certain amount of heat during use, and failure to dissipate heat in time is an important reason for shortening the life of LED lights. In order to solve the problem that the luminous efficiency of the lamp is affected by the heat generated during the use of the lamp and the service life of the lamp is shortened, the current method used is to coat a layer of heat-dissipa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D163/04C09D175/04C09D167/06C09D5/46C09D7/12C08G59/62
CPCC09D163/00C08G59/623C08K2201/011C08L2201/08C08L2205/035C08L2205/04C09D5/033C09D163/04C08L63/04C08L75/04C08L67/06C08L83/04C08K13/06C08K9/06C08K9/08C08K7/24C08K3/28C08K3/04C08K2003/265C08K2003/2213C08K3/36C08K5/3445C08K5/01C08L63/00
Inventor 茆文斌
Owner TIANCHANG JINLING ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap