Construction method for damp-proof wall

A construction method and wall technology, applied in coating, construction, filling slurry, etc., can solve the problems of long-term light fading, easy to be dirty, short service life, etc., to increase the overall strength and moisture-proof performance, good film formation The effect of improving the bonding stability and compressive shear bond strength

Active Publication Date: 2017-07-14
常州东华建筑安装工程有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the construction industry uses paint or paint coating on the interior walls of buildings as a decorative surface layer, which generally has defects such as cracking, falling off, easy corrosion by water, mildew, easy dirt after absorbing dust, easy fading under long-term light, and short service life; In wet weather, the wall surface will return to moisture and even condense water droplets. In addition, the existing plaster has poor thermal insulation performance, is easy to fall off, and has poor bonding force with the wall. The existing wall construction method has poor construction stability, safety and reliability. Poor performance, poor durability and other defects, can not meet the construction needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A moisture-proof wall construction method, comprising the following steps:

[0027] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide The molar ratio with polyvinyl alcohol is 1:2:0.5:2.5, the composite mother liquor and microsilica powder, silane-terminated polyether, alkylsulfonic acid phenyl ester, phenylmaleimide-based silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30min and cool naturally to obtain a wall surface interface agent; The mass ratio of imine-based silicone resin is 35:10:6:2:1, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reach...

Embodiment 2

[0033] A moisture-proof wall construction method, comprising the following steps:

[0034] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide The molar ratio with polyvinyl alcohol is 1:3:0.9:2, the composite mother liquor and microsilica powder, silane-terminated polyether, alkyl sulfonic acid phenyl ester, phenylmaleimide-based silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30min and cool naturally to obtain a wall surface interface agent; The mass ratio of imine-based silicone resin is 36:15:5:2:2, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reache...

Embodiment 3

[0040] A moisture-proof wall construction method, comprising the following steps:

[0041] Add ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide, and polyvinyl alcohol into the chemical kettle, stir evenly, and pressurize to 0.2-0.3MPa, hold the pressure for 1.5-2 hours to obtain a composite mother liquor; in which ethylene glycol diacrylate, hydroxyethyl methacrylate, 2,4,6-trimethylbenzoyl-diphenylphosphine oxide And polyvinyl alcohol molar ratio is 1:1.5:0.5:3, described composite mother liquor and microsilica fume, silane-terminated polyether, alkylsulfonic acid phenyl ester, phenylmaleimide base silicone resin are put into Stir in an internal mixer at 50-60°C for 20-30 minutes and cool naturally to obtain a wall interface agent; The mass ratio of imine-based silicone resin is 40:10:9:3:1.5, and the interface agent is evenly coated on the wall base to form an interface layer. The thickness of the interface layer reaches ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a construction method for a damp-proof wall. The construction method comprises the following steps that ethylene glycol diacrylate, hydroxyethyl methylacrylate, 2, 4, 6-trimethylbenzoyl-diphenyl phosphine oxide and polyvinyl alcohol are added into a chemical industry kettle to be stirred evenly, the pressure is increased to 0.2-0.3 MPa and kept for 1.5-2 h, and a compound mother solution is obtained. According to an interface agent provided by the invention, the bonding strength of the interface agent and the wall is improved by adding silica fume, silane end-capping polyether, alkyl sulfonic acid phenyl ester and phenyl maleimide group silicone resin. The interface agent bears the load acted on the wall, meanwhile the interface agent has good anti-permeability and has good bonding effect with plastering mortar, the overall strength and moisture-proof performance of the wall are improved, and the interface agent has good fluidity and is convenient for construction.

Description

technical field [0001] The invention relates to a moisture-proof wall construction method, which belongs to the field of wall construction. Background technique [0002] At present, the construction industry uses paint or paint coating on the interior walls of buildings as a decorative surface layer, which generally has defects such as cracking, falling off, easy corrosion by water, mildew, easy dirt after absorbing dust, easy fading under long-term light, and short service life; In wet weather, the wall surface will return to moisture and even condense water droplets. In addition, the existing plaster has poor thermal insulation performance, is easy to fall off, and has poor bonding force with the wall. The existing wall construction method has poor construction stability, safety and reliability. Poor performance, poor durability and other defects cannot meet the construction requirements. Therefore, a new technical solution should be provided to solve the above problems. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/02C09D183/08C09D7/12C09D5/34
CPCC08L2205/02C08L2205/03C09D1/00C09D4/06C09D5/34C09D183/08C09D7/61C09D7/63C09D7/65E04B1/644E04F13/02C08L83/04C08K3/36C08K5/42
Inventor 凃义亮
Owner 常州东华建筑安装工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com