Preparation method of electrothermal film

A technology of electrothermal film and preparation steps, which is applied in the direction of electric heating devices, ohmic resistance heating, electrical components, etc., can solve the problems of electrothermal film shedding, insufficient stability of electrothermal film, poor adhesion, etc., and achieve increased stability and increased stability And adhesion, enhance the effect of high temperature resistance

Active Publication Date: 2017-08-15
唐山烯彤科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention: Aiming at the problem that the traditional electric heating film has insufficient stability and poor adhesion, the electric heating film is easy to fall off from the substrate, and a preparation method of the electric heating film is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022] First weigh 40g of tin tetrachloride, 10g of antimony trichloride, 12g of ferric chloride, 20g of titanium tetrachloride, 5g of chromium chloride, 8g of calcium chloride and 10g of antimony trichloride, and add them to a container with a mass fraction of 200mL. 25% ethanol solution in a beaker, move the beaker into a magnetic stirrer with constant temperature and digital display speed measurement, stir and mix for 30min at a temperature of 70°C and a speed of 400r / min to obtain a mixed solution; then weigh 4g of dopamine and add it to the container In a beaker with 300mL of water, place the beaker in a water bath, control the temperature of the water bath to 60°C, stir and dissolve for 15 minutes to obtain a dopamine solution, take 30mL of dopamine solution, 100mL of mixed solution, 60mL of 35% ammonia solution by mass fraction and 60mL of pH Add the tromethamine-hydrochloric acid buffer solution of 8.3 into the beaker, stir and mix for 5 minutes to obtain the electrothe...

example 2

[0024]First weigh 30g of tin tetrachloride, 5g of antimony trichloride, 8g of ferric chloride, 15g of titanium tetrachloride, 3g of chromium chloride and 6g of calcium chloride into a beaker containing 100mL of 25% ethanol solution , move the beaker into a magnetic stirrer with a constant temperature digital display and speed measurement, stir and mix for 25 minutes at a temperature of 60°C and a speed of 300r / min to obtain a mixed solution; then weigh 3g of dopamine and add it to a beaker filled with 200mL of water, Place the beaker in a water bath, control the temperature of the water bath to 50°C, stir and dissolve for 10 minutes to obtain a dopamine solution, take 20mL dopamine solution, 80mL mixed solution, 50mL ammonia solution with a mass fraction of 35% and 50mL tromethamine with a pH of 8.3- Add the hydrochloric acid buffer solution into the beaker, stir and mix for 3 minutes to obtain the electrothermal film mixed solution, weigh 30g of graphene, 40g of gum arabic, 5g...

example 3

[0026] First weigh 35g of tin tetrachloride, 7g of antimony trichloride, 10g of ferric chloride, 17g of titanium tetrachloride, 4g of chromium chloride and 7g of calcium chloride into a beaker containing 150mL of 25% ethanol solution , move the beaker into a magnetic stirrer with constant temperature and digital display speed measurement, stir and mix for 27 minutes at a temperature of 65°C and a speed of 350r / min to obtain a mixed solution; then weigh 3g of dopamine and add it to a beaker filled with 250mL of water, Place the beaker in a water bath, control the temperature of the water bath to 55°C, stir and dissolve for 12 minutes to obtain a dopamine solution, take 25mL dopamine solution, 90mL mixed solution, 55mL ammonia solution with a mass fraction of 35% and 55mL tromethamine with a pH of 8.4- Add the hydrochloric acid buffer solution into the beaker, stir and mix for 4 minutes to obtain the electrothermal film mixed solution, weigh 35g graphene, 45g guar gum, 7g ferrous...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an electrothermal film, and belongs to the technical field of electrothermal materials. A metal chloride is prepared into a solution, dopamine is used to modify the metal chloride solution to obtain a mixed solution of the electrothermal film, graphene, gum and sulfate reducing bacteria are mixed for fermentation, under the effect of microbes, the graphene is combined with the gum, a binding force with resin is improved, nitrogen and sulfur elements are introduced into graphene molecules to enhance the stability of the graphene film, the mixed solution of the electrothermal film is injected on the basal body and serves as a bottom film, and one graphene layer is combined to obtain the electrothermal film. The prepared electrothermal film is high in stability and adhesive force, tends not to fall off the basal body, and has wide application prospects.

Description

technical field [0001] The invention relates to a method for preparing an electrothermal film, which belongs to the technical field of heating materials. Background technique [0002] Electric heating film is divided into high temperature and low temperature electric heating film. High temperature electric heating film is generally used in electronic appliances, military and so on. Low-temperature electric heating film is a translucent polyester film that can generate heat after being energized. It is made of conductive special ink and metal current-carrying strips, which are processed and hot-pressed between insulating polyester films. When working, the electric heating film is used as the heating body, and the heat is sent into the space in the form of radiation, so that the human body and objects are warmed first, and its comprehensive effect is better than the traditional convection heating method. The low-temperature radiation heating film system consists of a power s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H05B3/14
CPCH05B3/145
Inventor 邱洪荣薛洋王维
Owner 唐山烯彤科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products