A system and method for co-producing sulfur by using desulfurized gypsum and aluminum ash to produce sulphoaluminate cement

A technology of sulphoaluminate cement and desulfurized gypsum, which is applied in chemical instruments and methods, preparation/purification of sulfur, sulfur compounds, etc., can solve problems such as insufficient gypsum carbon, difficulty in controlling the atmosphere in the kiln, and rising sulfur prices

Active Publication Date: 2020-01-24
中芈(山东)环保科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's application of gypsum decomposition and co-production of cement and sulfuric acid technology started relatively late. At present, the mature technology is to combine the dried powdery materials with other raw materials and grind them into the hollow rotary kiln for decomposition and calcination. The atmosphere in the kiln is difficult to control. , prone to problems such as high oxygen content in the kiln, which will cause the carbon added in the raw material to partially react with oxygen, resulting in insufficient carbon required for the decomposition reaction of gypsum, and lower decomposition rate and desulfurization rate.
[0007] At the same time, my country is short of sulfur resources. Natural gypsum ore is generally used to produce sulfur, but the cost of producing sulfur from natural gypsum ore is relatively high. Chemical production mainly relies on imported sulfur, which leads to rising sulfur prices and increases the cost of chemical production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A system and method for co-producing sulfur by using desulfurized gypsum and aluminum ash to produce sulphoaluminate cement
  • A system and method for co-producing sulfur by using desulfurized gypsum and aluminum ash to produce sulphoaluminate cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Such as figure 1 As shown, the aluminum ash and desulfurized gypsum are sent into the dryer respectively. In terms of solid matter after drying, desulfurized gypsum: 61%, aluminum ash: 38%, and activated carbon account for 1%. It is directly transported into the hollow rotary kiln for calcination, the calcination temperature is 1280°C, and the calcination time is 60 minutes. The high-temperature kiln gas produced passes through the waste heat recovery equipment, and the by-product high-temperature steam and hot water are used for indirect drying of the original aluminum ash and desulfurized gypsum. The kiln gas exiting the waste heat recovery equipment, the gas temperature is reduced to 860°C, and after dust removal, dehumidification purification, supplementary air to adjust the oxygen-sulfur ratio and drying, it enters the fixed bed of activated carbon with a particle size of 10 mesh, and generates elemental sulfur through catalytic reduction. The prepared sulfur The ...

Embodiment 2

[0070] Send the aluminum ash and desulfurized gypsum into the dryer respectively. In terms of dried solid matter, desulfurized gypsum: 66%, aluminum ash: 33%, and activated carbon 1%. It is directly transported into the hollow rotary kiln for calcination, the calcination temperature is 1250°C, and the calcination time is 50 minutes. The high-temperature kiln gas produced passes through the waste heat recovery equipment, and the by-product high-temperature steam and hot water are used for indirect drying of the original aluminum ash and desulfurized gypsum. The kiln gas exiting the waste heat recovery equipment, the gas temperature is reduced to 855°C, after dust removal, dehumidification purification, supplementary air to adjust the oxygen-sulfur ratio and drying, it enters the fixed bed of activated carbon with a particle size of 10 mesh, and generates elemental sulfur through catalytic reduction. The prepared sulfur The purity reaches 99%. Microwave heating is used to evapor...

Embodiment 3

[0073] Such as figure 2 As shown, the aluminum ash and desulfurized gypsum are sent into the dryer respectively. In terms of solid matter after drying, desulfurized gypsum: 65%, aluminum ash: 34%, and activated carbon account for 1%. It is directly conveyed into the hollow rotary kiln, and gas is passed into the rotary kiln for calcination. The calcination temperature is 1300°C and the calcination time is 30 minutes. The high-temperature kiln gas produced passes through the waste heat recovery equipment, and the by-product high-temperature steam and hot water are used for indirect drying of the original aluminum ash and desulfurized gypsum. The kiln gas exiting the waste heat recovery equipment, the gas temperature is reduced to 860°C, and after dust removal, dehumidification purification, supplementary air to adjust the oxygen-sulfur ratio and drying, it enters the two-stage reactor, and each reactor is filled with Cu / Al 2 o 3 Catalyst, and gas is fed into the two-stage re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

A method for co-producing sulphoaluminate cement and sulfur by using desulfurized gypsum and aluminum ash, comprising: (1) drying aluminum ash, and heating desulfurized gypsum for dehydration to obtain semi-hydrated gypsum; (2) mixing the aluminum ash with the semi-hydrated gypsum according to a preset ratio, pulverizing, and homogenizing; (3) calcining the pulverized and homogenized mixture of the aluminum ash and the semi-hydrated gypsum while adding coal dust to the mixture, and performing oxygen-enriched combustion to obtain a sulphoaluminate cement clinker and sulfur dioxide-containing flue gas; (4) mixing the sulphoaluminate cement clinker and the desulfurized gypsum according to a ratio, and pulverizing to obtain sulphoaluminate cement; and (5) dedusting the sulfur dioxide-containing flue gas, and performing catalytic reduction to obtain a sulfur product, wherein the mass ratio of the aluminum ash to the desulfurized gypsum to carbon powder is (33-39):(61-66):1.

Description

technical field [0001] The patent of the invention relates to the fields of chemical industry, building material technology, comprehensive utilization of desulfurized gypsum and aluminum ash resources, and environmental protection and management, and specifically relates to a system and method for producing sulphoaluminate cement and co-producing sulfur by using desulfurized gypsum and aluminum ash. Background technique [0002] In today's society where land resources are increasingly tight and environmental protection is becoming more and more important, the Ministry of Industry and Information Technology of China has included tailings, coal gangue, fly ash and smelting slag from five major industries in the "Twelfth Five-Year Plan" Special Plan for Comprehensive Utilization of Bulk Industrial Solid Waste , by-product gypsum and red mud are listed as bulk industrial solid waste, and they are the main objects of treatment. Among them, red mud, aluminum ash, and desulfurized ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/32C01B32/40C01B17/04
CPCC01B17/04C01B17/0473C01B17/0482C01P2006/80C04B7/323
Inventor 任常在吴长亮刘晓斌刘全勋王勇付华辉
Owner 中芈(山东)环保科技有限公司