Preparation method and application of biomass porous carbon sheet based on kapok fiber
A kapok fiber and porous carbon technology is applied in the field of preparation of biomass porous carbon sheets, which can solve the problems of unfavorable electrolyte ion diffusion and movement, poor high current charging and discharging capability of electrode materials, etc. The effect of specific surface area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0028] (3) Precursor preparation: take pre-carbonized kapok fiber and place it in a beaker, add activator and deionized water, stir evenly, ultrasonically disperse for 0.5-1 h, and then put it in a drying oven at 60 °C for 12-24 h , obtain carbonized precursor mixture after grinding; Wherein, the weight ratio of activator and pre-carbonized kapok fiber is 1:1-10:1, is preferably 4:1-6:1, and the consumption of deionized water is expressed as per gram Use 5-50 mL of pre-carbonized kapok fiber; the activator used includes any one of potassium hydroxide, sodium hydroxide, sodium carbonate, sodium bicarbonate, potassium carbonate, phosphoric acid, sulfuric acid, potassium thiocyanate, and zinc chloride;
[0029] (4) Preparation of porous carbon sheets: Take the obtained carbonized precursor mixture and place it in a 20 mL graphite crucible, then fill it with carbon powder in a 40 mL porcelain crucible, put it into a box-type resistance furnace, and heat it up to 400 -1100°C, prefe...
Embodiment 1
[0034] (1) Put the kapok fiber in a beaker, add 5% sodium hydroxide aqueous solution, stir evenly, put it on the heater and boil for 0.5 h, then cool to room temperature, use a vacuum filter pump, use deionized water Repeated suction filtration and washing until the filtrate is neutral; then put the washed kapok fibers into a beaker, add an appropriate amount of ethanol solution for cleaning, and finally put them in a drying oven and dry them at 60 °C for 24 hours to obtain pretreated kapok fibers ;
[0035] (2) Take an appropriate amount of pretreated kapok fiber and put it in a 20 mL porcelain crucible, cover the lid, fix it with iron wire, then fill it with carbon powder in a 40 mL porcelain crucible, put it into a box-type resistance furnace, Raise the temperature to 500 °C, keep it warm for 2 hours, take it out after cooling to room temperature, and obtain pre-carbonized kapok fibers;
[0036](3) Take 1 g of the obtained pre-carbonized kapok fiber and put it in a 100 mL ...
Embodiment 2
[0042] (1) The pretreatment step of kapok fiber is the same as embodiment 1 step (1);
[0043] (2) Take an appropriate amount of pretreated kapok fiber and put it in a 20 mL porcelain crucible, cover the lid, fix it with iron wire, then fill it with carbon powder in a 40 mL porcelain crucible, put it into a box-type resistance furnace, Raise the temperature to 500 °C, keep it warm for 2 hours, take it out after cooling to room temperature, and obtain pre-carbonized kapok fibers;
[0044] (3) Take 1 g of the obtained pre-carbonized kapok fiber and put it in a 100 mL beaker, add 5 g of potassium hydroxide solid and 20 mL of deionized water, stir evenly and ultrasonically disperse for 0.5 h, then put the beaker in a drying oven for 60 After drying at ℃ for 24 h, the carbonized precursor mixture was obtained after grinding;
[0045] (4) Put the obtained carbonized precursor mixture into a 20 mL graphite crucible, screw on the lid, and then fill it with carbon powder in a 40 mL po...
PUM
Property | Measurement | Unit |
---|---|---|
specific surface area | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com