A kind of pouring dry abrasive material

A sheet material, dry grinding technology, used in abrasives, grinding devices, grinding/polishing equipment, etc., can solve the problems of diamond subsidence, uncontrollable large pores, and low abrasive holding strength

Active Publication Date: 2019-06-28
QUANZHOU ZHONGZHI NEW MATERIAL TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are cast-type diamond dry grinding discs for stone grinding, but they have the following problems: 1. The abrasive grains have low holding strength, and the abrasive grains fall off without being fully utilized; 2. The wear resistance of the abrasive discs The abrasiveness is poor, which leads to the low strength of the carcass in the dry grinding process of the grinding disc, and the diamond sinks, which does not give full play to its grinding use; 4. There are large pores on the surface of the dry grinding disc, and the large pores are uncontrollable. The method of vacuuming and defoaming is high in manufacturing cost and it is not easy to realize the temperature control of the mould.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pouring dry abrasive material
  • A kind of pouring dry abrasive material
  • A kind of pouring dry abrasive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) According to mass percentage, 15% of diamond crushed material with a particle size of 50 mesh, 10% of silicon carbide powder with a particle size of 80 mesh, 8% of white corundum with a particle size of 200 mesh, 13% of aluminum oxide, 10% of zinc oxide, ice crystal Stone 6%, after mechanical stirring, add epoxy resin (E44) 10%, liquid phenolic resin 20%, liquid nitrile rubber 5%, coupling agent (KH550) 2%, defoamer (BYK-A555) 1 %, stir into a uniform slurry with suitable viscosity.

[0040] (2) Fix the prepared lower base cloth on the flat workbench, then place the mold on the base cloth and fix it with a clamp, pour the slurry prepared in step (1) into the mold by pouring, and pour the slurry into the mold. After the material is scraped off, it is demoulded to obtain a semi-finished product. Put the semi-finished product in an oven at 160°C to cure for 2 hours, and then apply AB glue on the base cloth to adhere a layer of nylon buckle rough surface to obtain the ...

Embodiment 2

[0042] (1) According to the mass percentage, the particle size number is 200 mesh diamond broken material 13%, the particle size number is 200 mesh silicon carbide powder 10%, the particle size number is 400 mesh white corundum 8%, aluminum oxide 11%, zinc oxide 12%, ice crystal Stone 6%, after mechanical stirring, add epoxy resin (E44) 11%, liquid phenolic resin 21%, liquid nitrile rubber 5%, coupling agent (KH550) 2%, defoamer (BYK-A555) 1 %, stir into a uniform slurry with suitable viscosity.

[0043] (2) Fix the prepared lower base cloth on the flat workbench, then place the mold on the base cloth and fix it with a clamp, pour the slurry prepared in step (1) into the mold by pouring, and pour the slurry into the mold. After the material is scraped off, it is demoulded to obtain a semi-finished product. Put the semi-finished product in an oven at 160°C to cure for 2 hours, and then apply AB glue on the base cloth to adhere a layer of nylon buckle rough surface to obtain th...

Embodiment 3

[0045] (1) According to the mass percentage, the particle size number is 1000 mesh diamond crushing material 12%, the particle size number is 2000 mesh silicon carbide powder 10%, the particle size number is 2000 mesh white corundum 8%, aluminum oxide 10%, zinc oxide 12%, ice crystal Stone 6%, after mechanical stirring, add epoxy resin (E44) 12%, liquid phenolic resin 22%, liquid nitrile rubber 5%, coupling agent (KH550) 2%, defoamer (BYK-A555) 1 %, stir into a uniform slurry with suitable viscosity.

[0046](2) Fix the prepared lower base cloth on the flat workbench, then place the mold on the base cloth and fix it with a clamp, pour the slurry prepared in step (1) into the mold by pouring, and pour the slurry into the mold. After the material is scraped off, the semi-finished product is produced. Put the semi-finished product in an oven at 170°C to cure for 1 hour, and then apply AB glue on the base cloth to adhere a layer of nylon buckle rough surface to obtain the cast dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pouring dry grinding piece material. The pouring dry grinding piece material comprises the following components, by mass, of 30%-40% of bonding agents, 10%-15% of diamond grinding materials, 5%-10% of silicon carbide, 5%-10% of white corundum, 20%-30% of fillers, 1%-5% of toughening agents, 0.5%-2% of coupling agents and 0.3%-1% of defoaming agents. The pouring dry grinding piece material has the advantages of high in grinding particle holding strength and good in heat resistance and abrasion resistance and is capable of improving the processing effect and reducing the processing cost.

Description

technical field [0001] The invention relates to the technical field of stone grinding and polishing, in particular to a diamond dry grinding disc with high abrasive holding strength, good wear resistance and good heat resistance. Background technique [0002] Casting dry grinding discs are mainly used for grinding and cutting stone cutting surfaces. The previous process is metal saw blades. After sawing, dry grinding discs can be directly used to polish and polish, so that the sawing surface and the surface have the same gloss. Dry grinding discs Grinding and polishing are no longer required after grinding. [0003] At present, there are cast-type diamond dry grinding discs for stone grinding, but they have the following problems: 1. The abrasive grains have low holding strength, and the abrasive grains fall off without being fully utilized; 2. The wear resistance of the abrasive discs The abrasiveness is poor, which leads to the low strength of the carcass in the dry grind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/28B24D3/34B24D18/00B24D7/00
CPCB24D3/28B24D3/34B24D7/00B24D18/0009B24D18/0072
Inventor 钟剑明林江程赵扬陈敏
Owner QUANZHOU ZHONGZHI NEW MATERIAL TECH