Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Toilet brush hair brush head processing material, and preparation method thereof

A technology for processing materials and toilet brushes, which is applied in the field of toilet brush head processing materials and its preparation, which can solve the problems that plastic brush heads are easy to adhere to dirt, shorten the service life of toilet brushes, and clean dirt, etc., and achieve simple and easy processing steps line, avoid falling off and breaking, strong corrosion resistance

Inactive Publication Date: 2017-09-22
ANHUI XUEYU SANITARYWARE
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of using the toilet brush, people often find that the plastic brush head is easy to adhere to dirt. Even when cleaning the toilet, it is difficult to remove the dirt on the brush head. Mosquitoes and flies, thus directly shortening the service life of the toilet brush

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) Warm up 20g of ethylene-vinyl acetate copolymer to a molten state and mix for 10 minutes, then add 0.5g of hexamethylolmelamine hexamethyl ether and 0.5g of diacetone acrylamide, keep it in a molten state for 30 minutes, and wait for natural cooling After reaching room temperature, put it into the environment of -15°C and freeze it for 5 hours, and then grind it into particles with a particle size of 0.5-1mm to obtain the modified ethylene-vinyl acetate copolymer;

[0019] (2) Add 0.5g nano-titanium dioxide and 0.5g polytetrafluoroethylene superfine powder to 5g hydrogenated rosin pentaerythritol ester, heat up to a molten state and mix for 30min, and cool to room temperature naturally to obtain modified hydrogenated rosin pentaerythritol ester;

[0020] (3) Add 1g of chlorinated polyethylene rubber and 1g of polyvinyl butyral to 10g of aromatic modified terpene resin, heat up to a molten state and mix for 10min, then add 0.3g of zirconia and 0.01g of ferrocene, cont...

Embodiment 2

[0024] (1) Heat 25g of ethylene-vinyl acetate copolymer to a molten state and mix for 15 minutes, then add 1g of hexamethylolmelamine hexamethyl ether and 0.5g of diacetone acrylamide, continue to maintain the molten state for 1 hour, and wait for natural cooling to After room temperature, put it into -15°C environment, seal and freeze for 5 hours, and then grind it into particles with a particle size of 0.5-1mm to obtain the modified ethylene-vinyl acetate copolymer;

[0025] (2) Add 0.5g nano-titanium dioxide and 0.5g polytetrafluoroethylene superfine powder to 5g hydrogenated rosin pentaerythritol ester, heat up to a molten state and mix for 30min, and cool to room temperature naturally to obtain modified hydrogenated rosin pentaerythritol ester;

[0026] (3) Add 1g of chlorinated polyethylene rubber and 1g of polyvinyl butyral to 5g of aromatic modified terpene resin, heat up to a molten state and mix for 15min, then add 0.5g of zirconia and 0.02g of ferrocene, continue Ke...

Embodiment 3

[0051] The brush heads made in Example 1, Example 2, Comparative Example 1, Comparative Example 2, Comparative Example 3, and Comparative Example 4 were tested for use performance, and the test results are shown in Table 1.

[0052] The performance of the brush head made by the embodiment of the present invention in table 1

[0053] group

[0054] Since it is difficult to accurately measure the dirt cleaning performance, dirt adhesion and service life of the brush head, the number of * is used to characterize the usage observed in the test. The more the number * in the column of dirt cleaning ability, the stronger the dirt cleaning ability of the brush; the more the number * in the column of dirt adhesion, it means that the brush is more likely to adhere to dirt; the column of service life * The more the number, the longer the service life of the brush.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a toilet brush hair brush head processing material, and a preparation method thereof, and belongs to the technical field of sanitary equipment part processing. The toilet brush hair brush head processing material is prepared from, by weight, 15 to 25 parts of ethylene-vinyl acetate copolymer, 5 to 10 parts of an aromatic hydrocarbon modified terpene resin, 3 to 5 parts of methoxypolyethylene glycols / polyglutamic acid, 3 to 5 parts of pentaerythritol ester of hydrogenated rosin, 1 to 3 parts of chlorinated polyethylene rubber, 1 to 3 parts of polyvinyl butyral, 0.5 to 1 part of nanometer titanium dioxide, 0.5 to 1 part of polytetrafluoroethylene micropowder, 0.5 to 1 part of hexakis(methoxymethyl)melamine, 0.5 to 1 part of diacetone-acryloamide, 0.1 to 0.5 part of zirconium oxide, and 0.01 to 0.1 part of ferrocene. Brush hair prepared from the toilet brush hair brush head processing material is excellent in flexiblility and wear resistance, and can be used for removing stain on the internal parts of toilets; and the removed dirt enters into washing water immediately, and adhesion on the brush hair is avoided.

Description

Technical field: [0001] The invention relates to the technical field of processing sanitary ware accessories, in particular to a processing material for a toilet brush bristle and a brush head and a preparation method thereof. Background technique: [0002] The toilet is an essential appliance in every family, and cleaning the toilet has become a must in daily life. If the cleaning method is not appropriate or the cleaning tools used are not appropriate, it may be time-consuming and laborious, and ultimately a good cleaning effect cannot be achieved. The toilet brush is a cleaning accessory for the toilet, and is generally given to consumers as a gift when the toilet is sold. [0003] A toilet brush consists of a brush handle and a brush head. The brush head directly determines the cleaning effect. At present, there are many patents for improving the structure of the brush head, but the cleaning effect depends not only on the structure of the brush head but also on the mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L45/00C08L71/02C08L77/04C08L93/04C08L23/28C08L27/18C08K13/02C08K3/22C08K5/3492C08K5/20C08K5/56A46D1/00A46D1/04
CPCC08L23/0853A46D1/0207A46D1/04C08K2003/2241C08K2003/2244C08K2201/011C08L2205/035C08L45/00C08L71/02C08L77/04C08L93/04C08L23/286C08L27/18C08K13/02C08K3/22C08K5/34922C08K5/20C08K5/56
Inventor 马士永郎泽恩赵刚项卫军
Owner ANHUI XUEYU SANITARYWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com