Nano inorganic powder modified organic silicon waterproof paint

A nano-inorganic and powder modification technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of poor weather resistance and short service life of waterproof membranes, and achieve the effects of promoting bonding, increasing service life and avoiding aging

Active Publication Date: 2017-10-20
宁夏双玉防水防腐材料集团有限公司
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: during the use of traditional waterproof coatings, the waterproof film formed by curing is easy to close the capillary pores of the base material, resulting in the moisture in the base unable to escape from the inside of the wall, and the weather resistance of the waterproof film is not good. , the problem of short service life, a nano-inorganic powder modified silicone waterproof coating is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0027] In parts by weight, add 60 parts of nano-silica, 20 parts of nano-alumina, 8 parts of nano-zirconia, and 10 parts of nano-hydroxyapatite into the mixer, and stir and mix for 2 hours to obtain a nano-inorganic powder; Then in parts by weight, successively take 100 parts of hydroxyl-terminated polydimethylsiloxane, 100 parts of carboxy-terminated polydimethylsiloxane, 10 parts of sodium stearate, 20 parts of dodecylbenzenesulfonate Na2SO4, 4 parts of triethanolamine, 180 parts of deionized water, 3 parts of sodium carboxymethyl cellulose, 100 parts of nano-inorganic powder, first deionized water, sodium stearate, sodium dodecylbenzenesulfonate, Add triethanolamine, sodium carboxymethylcellulose and nano-inorganic powder into the reaction kettle according to the formula, stir and mix at a constant temperature for 45 minutes at a temperature of 60°C and a speed of 600r / min, and then add hydroxyl-terminated polydimethylsiloxane Alkanes, carboxyl-terminated polydimethylsiloxa...

example 2

[0029]In parts by weight, 70 parts of tetraethyl orthosilicate, 130 parts of absolute ethanol, 25 parts of citric acid solution with a concentration of 0.1mol / L, and 15 parts of silane coupling agent KH-560 are taken successively. First, dehydrated alcohol, Pour the citric acid solution and the silane coupling agent KH-560 into the reaction kettle, stir at a constant temperature for 45min at a temperature of 63°C and a rotation speed of 400r / min, then add ethyl orthosilicate dropwise into the reaction kettle, and wait for the dropwise addition After completion, continue to stir and hydrolyze for 4 hours at a constant temperature to obtain a hydrolyzate, then pour the obtained hydrolyzate into an evaporating dish, heat and evaporate to obtain a mixed gel, and wash the obtained mixed gel with deionized water until the washing liquid is neutral. The washed mixed gel was transferred to an oven, and dried to a constant weight at a temperature of 108°C to obtain a dried gel, and then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses nano inorganic powder modified organic silicon waterproof paint and belongs to the technical field of building waterproofing. The nano inorganic powder modified organic silicon waterproof paint disclosed by the invention is prepared from the following raw materials in parts by weight: 200 to 300 parts of an oligomer siloxane base material, 10 to 30 parts of an emulsifier, 20 to 60 parts of a stabilizer, 4 to 6 parts of a curing agent, 180 to 200 parts of a diluting agent, 3 to 6 parts of a thickener and 100 to 150 parts of nano inorganic powder; the nano inorganic powder is prepared from the following raw materials in parts by weight through mixing: 60 to 80 parts of nano silicon dioxide, 20 to 30 parts of nano aluminum oxide, 8 to 10 parts of nano zirconium oxide and 10 to 15 parts of nano hydroxyapatite. The nano inorganic powder modified organic silicon waterproof paint disclosed by the invention has the beneficial effects that the nano inorganic powder modified organic silicon waterproof paint has a relatively excellent weather-resisting performance and a long service life; a hydrophobic bionic structure formed by added inorganic nanoparticles does not hinder the permeation of water vapor in a substrate.

Description

technical field [0001] The invention relates to a nano inorganic powder modified organic silicon waterproof coating, which belongs to the technical field of building waterproofing. Background technique [0002] Building waterproof coating has the characteristics of simple construction and strong adaptability to complex structures, and is widely used in building construction. Waterproof coatings are mainly used for waterproofing, moisture-proofing and anti-seepage of some structural parts of buildings that may be eroded by water. Therefore, there are certain requirements for high-temperature resistance and anti-corrosion performance of waterproof coatings. Existing architectural waterproof coatings mainly include polyurethane waterproof coatings, polymer cement waterproof coatings, and silicone waterproof coatings, among which silicone waterproof coatings are widely used. [0003] Silicone waterproof coatings are divided into water-based environmentally friendly waterproof c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/08C09D7/12
CPCC08K2201/011C08L2201/08C09D5/08C09D183/04C08L1/286C08K5/098C08K5/02C08K9/06C08K3/36C08L1/284
Inventor 袁玲燕方晓俊许蘅
Owner 宁夏双玉防水防腐材料集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap