Environment-friendly coating and making method thereof

An environmentally friendly paint and production method technology, applied in asphalt paint, antifouling/underwater paint, coating and other directions, can solve the problems of cumbersome paint production process, short paint service life, paint can not be sterilized, etc., to improve the sterilization effect, The effect of improving environmental performance and reducing damage

Inactive Publication Date: 2017-12-01
WUHU SANSHAN LONGCHENG NEW MATERIALS
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the problems of poor environmental protection performance, inability to sterilize the paint, short service life of the paint, small scope of application, and cumbersome paint production process in the existing environmental protection paint, and provide a low-cost and easy-to-make paint. Grasp the environmentally friendly coating with wide application range, good coating quality and performance, and high environmental protection performance and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of environmental protection coating, described environmental protection coating is made up of the raw material of following parts by weight, 20 parts of organosilicon resin, 15 parts of polydimethylsiloxane, 14 parts of distilled water, 10 parts of asphalt, 8 parts of magnesium stearate, 7 parts of diethylene glycol butyl ether, 7 parts of tributyl citrate, 5 parts of fragrance, 3 parts of calcium carbonate, 3 parts of talc powder, 2 parts of rare earth ion powder, 2 parts of dispersant, 2 parts of oleic acid, film-forming aid 1 part of antioxidant, 1 part of antioxidant.

[0021] The dispersant is polyacrylate.

[0022] The film-forming aid is polyacrylamide.

[0023] Described antioxidant is dibutyl hydroxytoluene.

[0024] The manufacturing method includes the following steps:.

[0025] A. Liquid material production: Add silicone resin, polydimethylsiloxane, distilled water, asphalt, diethylene glycol butyl ether, tributyl citrate, dispersant, oleic acid, f...

Embodiment 2

[0034] A kind of environmental protection coating, described environmental protection coating is made up of the raw material of following parts by weight, silicone resin 12 parts, polydimethylsiloxane 12 parts, distilled water 11 parts, polyester acrylate 10 parts, asphalt 9 parts, 8 parts of magnesium stearate, 7 parts of polyvinyl alcohol, 6 parts of diethylene glycol butyl ether, 4 parts of tributyl citrate, 4 parts of fragrance, 3 parts of vinyl acetate emulsion, 3 parts of calcium carbonate, 2 parts of talcum powder , 2 parts of rare earth ion powder, 2 parts of dispersant, 2 parts of oleic acid, 1 part of film-forming aid, 1 part of reactive diluent, and 1 part of antioxidant.

[0035] The dispersant is a mixture of polyacrylate, acrylic acid and polyphosphate in a weight ratio of 1:2:2.

[0036] The film-forming aid is a mixture of polyvinyl alcohol, polyvinylpyrrolidone, propylene glycol phenyl ether, and dialkylene glycol phenyl ether in a weight ratio of 2:1:3:2.

...

Embodiment 3

[0044] A kind of environmental protection coating, described environmental protection coating is made up of the raw material of following parts by weight, silicone resin 10 parts, polydimethylsiloxane 10 parts, distilled water 10 parts, water-based acrylic emulsion 9 parts, asphalt 9 parts, hard 8 parts of magnesium fatty acid, 7 parts of simethicone oil, 6 parts of diethylene glycol butyl ether, 5 parts of tributyl citrate, 4 parts of flavoring material, 3 parts of activated carbon powder, 3 parts of calcium carbonate, 3 parts of cosolvent, 2 parts of talc powder, 2 parts of rare earth ion powder, 2 parts of dispersant, 2 parts of glass micropowder, 2 parts of oleic acid, 1 part of film-forming aid, 1 part of diatomaceous earth powder, and 1 part of antioxidant.

[0045] The dispersant is a mixture of polycarboxylate, polyphosphate and ethyl acetate in a weight ratio of 2:1:2.

[0046] The film-forming aid is a mixture of polyacrylamide, propylene glycol phenyl ether, dipropyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an environment-friendly coating which is composed of, by weight, 15-20 parts of organic silicon resin, 10-15 parts of polydimethylsiloxane, 10-15 parts of distilled water, 6-10 parts of asphalt, 8-10 parts of magnesium stearate, 5-7 parts of diethylene glycol butyl ether, 4-6 parts of tributyl citrate, 4-6 parts of fragrant material, 2-3 parts of calcium carbonate, 2-3 parts of talcum powder, 1-2 parts of rare earth ions, 1-2 parts of dispersant, 1-2 parts of oleic acid, 1-2 parts of film forming aid and 1-2 parts of antioxidant. The fragrant material and the rare earth ions are added into raw materials of the environment-friendly coating, the coating coated on a building is enabled to emit fragrance through the fragrant material to play a role in insect expelling, and the coating is enabled to have sterilizing effect through the rare earth ions, so that the sterilizing effect of the coating is improved, damage to performance of the coating caused by bacteria is lowered, service life of the coating is prolonged, and environment friendliness is improved; the coating does not contain formaldehyde and formaldehyde-releasing substances, so that environment-friendly performance is improved, and application range of the coating can be expanded.

Description

technical field [0001] The invention relates to the technical field of paint processing, in particular to an environmentally friendly paint and a manufacturing method thereof. Background technique [0002] With the improvement of people's living standards and environmental protection awareness, the environmental protection requirements for home decoration materials are getting higher and higher. Although the volatility index of existing coatings has been reduced to meet the standards, there are still chemical volatiles. The patent No. 201610484168.3 discloses an environmentally friendly waterproof coating, which solves the problem of insufficient adaptability of existing coatings and cannot meet the needs of use well, but it has poor environmental protection performance of coatings, coatings that cannot be sterilized, and coatings that cannot be sterilized. Short service life, small scope of application, and cumbersome paint production process. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D195/00C09D5/14C09D7/12
CPCC09D183/04C08L2205/025C08L2205/035C09D5/14
Inventor 杨荣军杨荣兵赵传东
Owner WUHU SANSHAN LONGCHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap