Degradable plastic

A plastic and degradation agent technology, applied in the field of degradable plastics, can solve the problems of strong water absorption, fast decomposition rate, oxidation resistance, weak impact resistance, etc., and achieve low water absorption, slow decomposition speed, and good impact resistance Effect

Inactive Publication Date: 2018-03-06
GUANGXI NANNING ZHICUI SCI TECH CONSULTATION CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a degradable plastic to solve the problems of fast decomposition rate, weak oxidation resistance, impact resistance, strong water absorption, etc. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of the degradable plastic comprises the following steps:

[0031] S1: Polylactic acid resin, modified poly-β-hydroxybutyrate PHB, diisononyl phthalate DINP, unsaturated polyester resin, linear low-density polyethylene grafted with maleic anhydride, and γ-glycidyl ether Oxypropyltrimethoxysilane was mixed and stirred at a temperature of 105-120°C and a rotation speed of 200-400r / min for 10-15min to obtain mixture I;

[0032] S2: Under nitrogen protection, add alkaline clay, calcium carbonate, ramie fiber, methyl methacrylate-butadiene-styrene copolymer, aluminum potassium sulfate, citric acid ester, Ethylene-vinyl acetate copolymer, ethylene bisoleic acid amide, diphenylmethane diisocyanate, degradation agent, stirring at ultrasonic power of 120-180W, temperature of 90-96°C, rotation speed of 200-300r / min for 2- 2.5h, the mixture II was obtained;

[0033] S3: Add soybean protein powder, oxidized mung bean starch, anti-mold and antibacterial agent...

Embodiment 1

[0037] A degradable plastic, in parts by weight, including the following raw materials: 120 parts of polylactic acid resin, 80 parts of modified poly-β-hydroxybutyric acid PHB, 8 parts of diisononyl phthalate DINP, unsaturated poly 20 parts of ester resin, 13 parts of soybean protein powder, 10 parts of oxidized mung bean starch, 6 parts of alkaline clay, 5 parts of calcium carbonate, 12 parts of ramie fiber, 1.5 parts of linear low density polyethylene grafted maleic anhydride, γ-glycidol 1.5 parts of etheroxypropyltrimethoxysilane, 2.5 parts of methyl methacrylate-butadiene-styrene copolymer, 1.5 parts of potassium aluminum sulfate, 3.5 parts of citrate, 2.5 parts of ethylene-vinyl acetate copolymer, 2 parts of dioleic acid amide, 1.5 parts of diphenylmethane diisocyanate, 2.1 parts of antifungal and antibacterial agent, 1.5 parts of degradation agent, 0.9 part of antioxidant, 0.8 part of stabilizer;

[0038] The alkaline clay is nanoscale alkaline clay;

[0039] Described ...

Embodiment 2

[0050] A degradable plastic, in parts by weight, including the following raw materials: 102 parts of polylactic acid resin, 76 parts of modified poly-β-hydroxybutyrate PHB, 6 parts of diisononyl phthalate DINP, unsaturated poly 15 parts of ester resin, 10 parts of soybean protein powder, 7 parts of oxidized mung bean starch, 3 parts of alkaline clay, 3 parts of calcium carbonate, 8 parts of ramie fiber, 1 part of linear low density polyethylene grafted maleic anhydride, γ-glycidol 1 part of etheroxypropyltrimethoxysilane, 2 parts of methyl methacrylate-butadiene-styrene copolymer, 1 part of potassium aluminum sulfate, 3 parts of citrate, 2 parts of ethylene-vinyl acetate copolymer, 1 part of bisoleic acid amide, 1 part of diphenylmethane diisocyanate, 0.8 part of antifungal and antibacterial agent, 1 part of degradation agent, 0.6 part of antioxidant, 0.5 part of stabilizer;

[0051] The alkaline clay is nanoscale alkaline clay;

[0052] Described calcium carbonate is the cal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a degradable plastic. The degradable plastic comprising the following raw materials: polylactic acid resin, modified poly-beta-hydroxybutyric acid (PHB), diisodecyl phthalate (DINP), unsaturated polyester resin, soybean protein powder, oxidized mung bean starch, alkaline white clay, calcium carbonate, ramie fiber, linear low density polyethylene grafted maleic anhydride, gamma-glycidyloxypropyltrimethoxysilane, a methyl methacrylate-butadiene-styrene copolymer, potassium aluminum sulfate, citrate, an ethylene-vinyl acetate copolymer, ethylene bis(oleamide), diphenylmethane diisocyanate, a mildew-proof antibacterial agent, a degradation agent, an antioxidant and a stabilizer. The degradable plastic of the invention has good tensile strength, good elongation at break,good impact resistance, low water absorption and good light transmission performance, can be completely degraded into carbon dioxide and water in 133 to 136 days, and has no environmental hazards.

Description

【Technical field】 [0001] The invention belongs to the fields of plastic preparation technology and environmental protection, and in particular relates to a degradable plastic. 【Background technique】 [0002] Plastics are widely used, such as plastic toys, plastic bottles, plastic packaging, plastic bags, etc. We cannot live without plastics. Studies have found that plastic products produced from polylactic acid resin can be completely degraded into carbon dioxide and water in a composting environment. Moreover, polylactic acid resin has good compatibility, transparency, solvent resistance and biaxial stretching properties, etc., and can be processed in a variety of ways. At present, the more common plastic products at home and abroad are disposable cups, knives and forks, plates, Plastic bags, non-woven fabrics, etc., theoretically as long as they are plastic products, can be made of this bioplastic material. [0003] However, as we all know, ordinary PP / PE plastics are di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/04C08L67/06C08L89/00C08L3/10C08L1/02C08L51/06C08K13/02C08K3/34C08K3/26C08K3/22C08K5/19C08K3/32C08K5/17
CPCC08K2201/011C08L67/04C08L2201/06C08L2201/08C08L2205/025C08L2205/035C08L2205/16C08L67/06C08L89/00C08L3/10C08L1/02C08L51/06C08K13/02C08K3/346C08K2003/265C08K2003/2241C08K5/19C08K2003/322C08K5/175
Inventor 朱俊宇
Owner GUANGXI NANNING ZHICUI SCI TECH CONSULTATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com