Glass fiber reinforced plastic for fishing rod and preparation method thereof

A glass fiber and reinforced plastic technology, applied in the field of glass fiber reinforced plastic for fishing rods and its preparation, can solve the problems of limited use range, affecting the service life of glass fiber reinforced plastic, hard and fragile glass fiber reinforced plastic, etc., and achieves improved mechanical properties and thermal conductivity. performance, good oxidative synergy, and the effect of inhibiting degradation

Inactive Publication Date: 2018-03-20
班戈设备系统(苏州)有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

FRP is hard and fragile, which limits the scope of use and greatly affects the service life of FRP

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A glass fiber reinforced plastic for fishing rods, made of the following raw materials in parts by weight:

[0024] 8 parts of glass fiber, 5 parts of nano kaolin, 7 parts of white carbon black, 3 parts of carbon black, 10 parts of γ-glycidyl etheroxypropyl trimethoxysilane, 15 parts of polyimide resin, 3 parts of dopamine, nano nitrogen 5 parts of boron, 6 parts of polylactic acid, 14 parts of polycarbonate, 1 part of polyaluminum siloxane, 1 part of nickel aluminide, 3 parts of chromium carbide, 15 parts of ABS resin, 6 parts of sulfur, 1 part of nano-titanium dioxide, poly 6 parts of ethylene wax, 5 parts of zinc stearate, 10 parts of solubilizer, and 2 parts of initiator.

[0025] Among them, the initiator is formed by mixing tert-butyl benzoate and tert-butyl peroxy 2-ethylhexanoate in a mass ratio of 3:1; the solubilizer is ethylene-methyl acrylate-glycidyl methacrylate and ethylene - Butyl acrylate is mixed at a mass ratio of 4:2; the mass fraction of γ-glycidyl...

Embodiment 2

[0027] A glass fiber reinforced plastic for fishing rods, made of the following raw materials in parts by weight:

[0028] 10 parts of glass fiber, 3 parts of nano kaolin, 5 parts of white carbon black, 6 parts of carbon black, 5 parts of γ-glycidyl etheroxypropyl trimethoxysilane, 10 parts of polyimide resin, 5 parts of dopamine, nano nitrogen 7 parts of boron, 9 parts of polylactic acid, 21 parts of polycarbonate, 1.5 parts of polyaluminum siloxane, 2 parts of nickel aluminide, 1 part of chromium carbide, 17 parts of ABS resin, 4 parts of sulfur, 3 parts of nano titanium dioxide, poly 4 parts of ethylene wax, 7 parts of zinc stearate, 8 parts of solubilizer, and 3 parts of initiator.

[0029] Among them, the initiator is formed by mixing tert-butyl benzoate and tert-butyl peroxy 2-ethylhexanoate in a mass ratio of 3:1; the solubilizer is ethylene-methyl acrylate-glycidyl methacrylate and ethylene - Butyl acrylate is mixed at a mass ratio of 4:2; the mass fraction of γ-glyci...

Embodiment 3

[0031] A glass fiber reinforced plastic for fishing rods, made of the following raw materials in parts by weight:

[0032] 9 parts of glass fiber, 4 parts of nano kaolin, 6 parts of white carbon black, 5 parts of carbon black, 7 parts of γ-glycidyl etheroxypropyl trimethoxysilane, 12 parts of polyimide resin, 4 parts of dopamine, nano nitrogen 6 parts of boron, 7 parts of polylactic acid, 16 parts of polycarbonate, 1.2 parts of polyaluminum siloxane, 1.5 parts of nickel aluminide, 2 parts of chromium carbide, 16 parts of ABS resin, 5 parts of sulfur, 2 parts of nano titanium dioxide, poly 5 parts of ethylene wax, 6 parts of zinc stearate, 9 parts of solubilizer, and 2.5 parts of initiator.

[0033] Among them, the initiator is formed by mixing tert-butyl benzoate and tert-butyl peroxy 2-ethylhexanoate in a mass ratio of 3:1; the solubilizer is ethylene-methyl acrylate-glycidyl methacrylate and ethylene - Butyl acrylate is mixed at a mass ratio of 4:2; the mass fraction of γ-g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides glass fiber reinforced plastic for a fishing rod and a preparation method thereof, and relates to the technical field of glass reinforced products, and the glass fiber reinforced plastic is prepared from the following raw materials in parts by weight: 8 to 10 parts of glass fiber, 3 to 5 parts of nano-kaolin, 5 to 7 parts of white carbon black, 3 to 6 parts of carbon black,5 to 10 parts of gamma-glycidoxypropyltrimethoxysilane, 10 to 15 parts of polyimide resin, 3 to 5 parts of dopamine, 5 to 7 parts of nano-boron nitride, 6 to 9 parts of polylactic acid, 14 to 21 partsof polycarbonate, 1 to 1.5 parts of polyaluminosiloxane, 1 to 2 parts of nickel aluminide, 1 to 3 parts of chromium carbide, 15 to 17 parts of ABS resin, 4 to 6 parts of sulfur, 1 to 3 parts of nanotitanium dioxide, 4 to 6 parts of polyethylene wax, 5 to 7 parts of zinc stearate, 8 to 10 parts of a solubilizing agent and 2 to 3 parts of an initiator. The preparation method of the glass fiber reinforced plastic includes three steps. The glass fiber reinforced plastic for the fishing rod has the advantages of corrosion resistance, weather resistance, toughness, scratch resistance and flame retardancy. The glass fiber reinforced plastic has higher rigidity and bending strength, is not easy to break during use, and has long service life.

Description

technical field [0001] The invention relates to the technical field of glass reinforced products, in particular to a glass fiber reinforced plastic for fishing rods and a preparation method thereof. Background technique [0002] Glass fiber reinforced plastics, commonly known as glass fiber reinforced plastics, are made by adding fibrous reinforcement materials to thermosetting resin substrates, and are usually manufactured by compression molding. Compression molding includes methods such as lamination molding, compression molding, and hand lay-up molding. [0003] In reinforced plastics, unsaturated resins and m-phenylene resins are the most commonly used resin substrates, in which glass fibers, inorganic fillers, and metal oxides such as magnesium oxide are added as reinforcing materials. According to the different characteristics of the product, the amount of glass fiber added usually fluctuates between 20-35% by mass. [0004] Fishing rod is a kind of fishing tool and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L79/08C08L67/04C08L69/00C08L55/02C08L23/06C08L83/04C08K13/06C08K3/34C08K3/04C08K3/36C08K9/04C08K9/02C08K7/14C08K3/14C08K5/5435C08K3/16
CPCC08L79/08C08K2201/011C08L55/02C08L69/00C08L2201/02C08L2201/08C08L2205/035C08L67/04C08L23/06C08L83/04C08K13/06C08K3/346C08K3/04C08K3/36C08K9/04C08K9/02C08K7/14C08K3/14C08K5/5435C08K3/16
Inventor 钱理
Owner 班戈设备系统(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com