ABS composite material for automobile air intake pipe and preparation method of ABS composite material

A composite material and air intake pipe technology, applied in the field of composite materials, can solve problems such as insufficient power output, and achieve the effects of improving power output, simple process and alleviating exhaust emissions.

Inactive Publication Date: 2018-03-23
深圳市宏士通科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the insufficient power output of existing small-displacement cars and second-hand cars after the air conditioner is turned on in summer, the exhaust emission data is much higher than that of other vehicles, and the existing composite materials used for car intake pipes cannot improve the problem that the gas in the internal combustion engine cannot be fully burned. The invention provides an ABS composite material for automobile air intake pipe and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS composite material for automobile air intake pipe and preparation method of ABS composite material
  • ABS composite material for automobile air intake pipe and preparation method of ABS composite material
  • ABS composite material for automobile air intake pipe and preparation method of ABS composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] In one embodiment, the preparation method includes the following steps:

[0038] (1) Take each raw material component according to the raw material ratio;

[0039] (2) placing the raw material components in a high-temperature reaction kettle, and performing mixing treatment at 200-230° C. to obtain a high-temperature mixed liquid;

[0040] (3) The high-temperature mixed solution is subjected to injection molding treatment to obtain an ABS composite material for an automobile intake pipe.

[0041] The above-mentioned preparation method is further explained below:

[0042] Preferably, the mixing treatment time is 1-2 hours, so that the raw materials are mixed evenly.

[0043] Preferably, the injection molding process is realized by an injection molding machine to obtain an ABS composite material for an automobile air intake pipe.

[0044] The method has the advantages of simple preparation process, convenient operation, environmental protection, safety and reliability....

Embodiment 1

[0047] The ABS composite material used for automobile intake pipes, based on the mass of ABS composite materials used for automobile air intake pipes as 100%, includes the following raw material components in mass percentages:

[0048]

[0049] The ABS composite material that is used for automobile intake pipe, the preparation method comprises the following steps:

[0050] (1) Take each raw material component according to the raw material ratio;

[0051] (2) placing the raw material components in a high-temperature reaction kettle, and performing a mixing treatment at 200° C. for 2 hours to obtain a high-temperature mixed liquid;

[0052] (3) The high-temperature mixed solution is introduced into an injection molding machine, and subjected to injection molding treatment to obtain an ABS composite material for an automobile intake pipe.

Embodiment 2

[0054] The ABS composite material used for automobile intake pipes, based on the mass of ABS composite materials used for automobile air intake pipes as 100%, includes the following raw material components in mass percentages:

[0055]

[0056] The ABS composite material that is used for automobile intake pipe, the preparation method comprises the following steps:

[0057] (1) Take each raw material component according to the raw material ratio;

[0058] (2) Put the raw material components in a high-temperature reaction kettle, and perform a mixing treatment at 210°C for 1.5 hours to obtain a high-temperature mixed liquid;

[0059] (3) The high-temperature mixed solution is introduced into an injection molding machine, and subjected to injection molding treatment to obtain an ABS composite material for an automobile intake pipe.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of composite materials, and specifically discloses an ABS composite material for an automobile air intake pipe and a preparation method of the ABS composite material. The ABS composite material for the automobile air intake pipe, based on 100% of mass of the ABS composite material for the automotive air intake pipe, is prepared from the raw material components in percentage by mass: 40 to 60% of ABS; 20 to 30% of lanthanum-nickel alloy; 3 to 5% of dysprosium oxide; 7 to 9% of samarium oxide; 0.1 to 0.3% of niobium oxide; 2 to 10% of cerium; and 3 to6% of barium. The ABS composite material for the automobile intake pipe provided by the invention has good properties such as impact resistance, heat resistance, low temperature resistance, chemicalresistance and the like; gas entering an internal combustion engine has an effect of supporting combustion to promote full combustion of the internal combustion engine, improve power output of a car,and at the same time, alleviate a problem of tail gas emissions.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to an ABS composite material used for an automobile intake pipe and a preparation method thereof. Background technique [0002] The country's policy of first development and then governance has brought serious side effects of environmental and air pollution. From the beginning of the high incidence of smog in the Beijing-Tianjin region, it has extended to most of North China, East China, Northeast China, parts of South China, and some resource-rich provinces and regions in the west. A city dominated by heavy industry. Among them, vehicle exhaust emissions account for a large proportion. Because the number of cars in China has grown explosively in the past ten years, the equivalent of exhaust emissions has also risen sharply. Great damage to people's health. [0003] Small-displacement cars and second-hand cars account for a large proportion of China's car ownership. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08K13/02C08K3/22C08K3/08
CPCC08K13/02C08K3/08C08K3/22C08K2003/0862C08K2003/221C08K2201/003C08K2201/014C08L2201/08C08L2203/18C08L55/02
Inventor 于梅轩曲振江王铁生
Owner 深圳市宏士通科技有限公司