Preparation process of PVC (Polyvinyl chloride) decorative film

A preparation process and decorative film technology, applied in the field of PVC film preparation technology, can solve the problems of easy migration, unstable performance, human health and ecological environment hazards, etc., and achieve the effects of not easy migration and excellent mechanical properties.

Active Publication Date: 2018-04-06
广东全丰新材料科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The migration of plasticizer will reduce the physical properties of the product, make the product hard and brittle, and obviously damage the surface properties of the product, seriously affecting the performance and service life of the product
On the other hand, when the plasticizer in PVC products migrates outward,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] A PVC decorative film, the preparation process is as follows:

[0039] (1) Mixing: Weigh and mix each raw material according to parts by weight, then mix and stir evenly. The ratio of each raw material is as follows:

[0040] 100 parts of PVC resin (polymerization degree is 1400), 20 parts of polyurethane elastomer, 60 parts of triethyl citrate, stabilizer (mixture of barium zinc liquid stabilizer and organotin liquid stabilizer, the mass ratio is 1:2) 3 2 parts, 2 parts of pigment, 20 parts of rutile titanium dioxide (particle size 0.3 microns), 2 parts of light calcium carbonate, 10 parts of dicumyl peroxide;

[0041] Wherein, the preparation method of the polyurethane elastomer is as follows: 100 parts by mass of polyester polyol (number average molecular weight 2000), 40 parts by mass of MDI, 6 parts by mass of ethylene glycol, 4 parts by mass of methacrylamide, hydroxy acetoacetate Put 6 parts by mass of ethyl ester in a mixer at 100°C and stir...

Example Embodiment

[0048] Example 2

[0049] A PVC decorative film, the preparation process is as follows:

[0050] (1) Mixing: Weigh and mix each raw material according to parts by weight, then mix and stir evenly. The ratio of each raw material is as follows:

[0051]100 parts of PVC resin (polymerization degree: 1700), 30 parts of polyurethane elastomer, 50 parts of triethyl citrate, stabilizer (mixture of barium zinc liquid stabilizer and organotin liquid stabilizer, the mass ratio is 1:2) 3 2 parts, 2 parts of pigment, 20 parts of rutile titanium dioxide (particle size 0.3 micron), 2 parts of light calcium carbonate, 8 parts of dicumyl peroxide;

[0052] Wherein, the preparation method of the polyurethane elastomer is as follows: 100 parts by mass of polyester polyol (number average molecular weight 2000), 40 parts by mass of MDI, 6 parts by mass of ethylene glycol, 4 parts by mass of methacrylamide, hydroxy acetoacetate Put 6 parts by mass of ethyl ester in a mixer at 100°C and stir for ...

Example Embodiment

[0059] Example 3

[0060] A PVC decorative film, the preparation process is as follows:

[0061] (1) Mixing: Weigh and mix each raw material according to parts by weight, then mix and stir evenly. The ratio of each raw material is as follows:

[0062] 100 parts of PVC resin (polymerization degree: 1600), 30 parts of polyurethane elastomer, 60 parts of triethyl citrate, stabilizer (mixture of barium zinc liquid stabilizer and organotin liquid stabilizer, the mass ratio is 1:2) 3 2 parts, 2 parts of pigment, 20 parts of rutile titanium dioxide (particle size 0.3 microns), 2 parts of light calcium carbonate, 10 parts of dicumyl peroxide;

[0063] Wherein, the preparation method of the polyurethane elastomer is as follows: 100 parts by mass of polyester polyol (number average molecular weight 3000), 30 parts by mass of MDI, 6 parts by mass of ethylene glycol, 4 parts by mass of methacrylamide, hydroxy acetoacetate Put 6 parts by mass of ethyl ester in a mixer at 100°C and stir f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation process of a PVC (Polyvinyl chloride) decorative film. The preparation process comprises the following steps: mixing PVC resin, a polyurethane elastomer, a plasticizer, a stabilizer, pigments, titanium dioxide, light calcium carbonate and dicumyl peroxide, and performing internal mixing, open milling, extrusion filtering, four-roll calendaring, pulling, embossing, cooling, trimming and coiling, thereby obtaining the decorative film. The decorative film has an excellent formaldehyde absorption effect, and the plasticizer is less in migration and stable inperformance.

Description

technical field [0001] The invention relates to the field of PVC, in particular to a preparation process of a decorative PVC film. Background technique [0002] With the gradual improvement of people's living standards and the rise of the real estate industry, surface decoration materials have entered a period of rapid development. Among them, film materials such as PVC film, PET film and composite film have simple production processes, various surface decoration patterns and effects, and use methods. Simple and cost-effective, it occupies a dominant position in the new surface decoration material market. PVC film has good wear resistance, good corrosion resistance, high quality and low price, and is developing rapidly. It is widely used in indoor and furniture decoration, decoration industry, aircraft interior membrane, cabin membrane and other fields. It can make the surface of the decorated object obtain higher hardness, prevent the surface from being artificially scratc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L75/06C08K13/02C08K5/11C08K3/22C08K3/26C08K5/14C08J5/18B29D7/01
CPCB29D7/01C08J5/18C08J2327/06C08J2475/06C08K5/11C08K5/14C08K13/02C08K2003/2241C08K2003/265
Inventor 童慧
Owner 广东全丰新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products