ECO (Epichlorohydrin) ion-conducting type spongy charging roller and preparation method thereof

An ion-conducting and conductive sponge technology, which is applied to equipment, corona discharge devices, and electrical recording technology applying charge patterns, etc., can solve the problems of short service life, poor conductivity, mechanical properties and durability problems such as poor performance, long service life, improved electrical conductivity, and good wear resistance

Inactive Publication Date: 2018-04-17
DONGGUAN WALTON RUBBER & PLASTIC NEW MATERIAL CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing charging rollers have poor conductivity, poor mechanical properties and durability, and short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ECO (Epichlorohydrin) ion-conducting type spongy charging roller and preparation method thereof
  • ECO (Epichlorohydrin) ion-conducting type spongy charging roller and preparation method thereof
  • ECO (Epichlorohydrin) ion-conducting type spongy charging roller and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An ECO ion-conductive sponge charging roller, comprising a roller shaft, a foamed conductive sponge layer sleeved outside the roller shaft, and an ECO ion-conductive rubber layer sleeved outside the foamed conductive sponge layer; the foamed conductive sponge The layer is made of the following raw materials in parts by weight:

[0044]

[0045] The ECO ion conductive rubber layer is made of the following raw materials in parts by weight:

[0046]

[0047] The ion-conducting agent is ammonium sulfate, ammonium nitrate or ammonium iodide.

[0048] The blowing agent is a mixture composed of 4,4-oxobisbenzenesulfonyl hydrazide, azodicarbonamide and diisopropyl azodicarboxylate in a weight ratio of 2:1.5:1.

[0049] The accelerator is a mixture of zinc dibutyldithiocarbamate and 2-mercaptobenzothiazole in a weight ratio of 2:1; the active agent is made of zinc oxide, zinc stearate and polyethylene glycol A mixture of diols in a weight ratio of 1.5:0.8:1.

[0050]The...

Embodiment 2

[0059] The difference between this embodiment and the above-mentioned embodiment 1 is that the foamed conductive sponge layer is made of the following raw materials in parts by weight:

[0060]

[0061]

[0062] The ECO ion conductive rubber layer is made of the following raw materials in parts by weight:

[0063]

[0064] The ionic conductive agent is LiBF 4 、LiPF 6 or LiAsF 6 .

[0065] The foaming agent is a mixture composed of 4,4-oxobisbenzenesulfonyl hydrazide, azodicarbonamide and diisopropyl azodicarboxylate in a weight ratio of 2.5:1.8:1.

[0066] The accelerator is a mixture of zinc dibutyldithiocarbamate and 2-mercaptobenzothiazole in a weight ratio of 2.5:1; the active agent is made of zinc oxide, zinc stearate and polyethylene A mixture of diols in a weight ratio of 1.8:0.9:1.

[0067] The bridging agent is a vinyl chloride-vinyl acetate-butyl acrylate terpolymer with a vinyl chloride unit content of 45%, a vinyl acetate unit content of 27.5%, and a ...

Embodiment 3

[0070] The difference between this embodiment and the above-mentioned embodiment 1 is that the foamed conductive sponge layer is made of the following raw materials in parts by weight:

[0071]

[0072] The ECO ion conductive rubber layer is made of the following raw materials in parts by weight:

[0073]

[0074] The ion-conducting agent is LiSbF 6 or LiCF 3 SO 3 .

[0075] The foaming agent is a mixture composed of 4,4-oxobisbenzenesulfonyl hydrazide, azodicarbonamide and diisopropyl azodicarboxylate in a weight ratio of 3:2:1.

[0076] The accelerator is a mixture of zinc dibutyldithiocarbamate and 2-mercaptobenzothiazole in a weight ratio of 3:1; the active agent is made of zinc oxide, zinc stearate and polyethylene A mixture of diols in a weight ratio of 2:1:1.

[0077] The bridging agent is a vinyl chloride-vinyl acetate-butyl acrylate terpolymer with a vinyl chloride unit content of 50%, a vinyl acetate unit content of 25%, and a butyl acrylate unit content o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
electrical resistanceaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of charging rollers and particularly relates to an ECO (Epichlorohydrin) ion-conducting type spongy charging roller and a preparation method thereof. The ECO ion-conducting type spongy charging roller comprises a roller shaft, a foaming-conducting sponge layer sheathed at the outer side of the roller shaft and an ECO ion-conducting rubber layer sheathedat the outer side of the foaming-conducting sponge layer, wherein the foaming-conducting sponge layer is prepared from the following raw materials in parts by weight: 40-60 parts of ethylene-propylene-diene monomer rubber, 20-40 parts of superconducting carbon black, 0.5-1.5 parts of ion conducting agent, 3-7 parts of foaming agent, 4-7 parts of accelerator, 2-6 parts of active agent, 1-2 parts of bridging agent and 2-4 parts of processing aid. The ECO ion-conducting type spongy charging roller is good in conductivity, mechanical property and durability and long in service life.

Description

technical field [0001] The invention relates to the technical field of charging rollers, in particular to an ECO ion-conductive sponge charging roller and a preparation method thereof. Background technique [0002] The charging roller used on the printing equipment is responsible for contacting and rotating the photosensitive drum, so that the photosensitive drum is evenly charged, and the electrostatic latent image after exposure is generated. The existing charging roller has poor conductivity, poor mechanical properties and durability, and short service life. Contents of the invention [0003] In order to overcome the shortcomings and deficiencies in the prior art, the object of the present invention is to provide an ECO ion-conductive sponge charging roller, which has good electrical conductivity, good mechanical properties, good durability and long service life. [0004] Another object of the present invention is to provide a preparation method of an ECO ion-conductiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L71/03C08L71/02C08L27/06C08L23/30C08K13/02C08K3/04C08K5/47C08K5/39C08K3/22C08K5/098C08K5/20C08K5/103C08J9/10G03G15/02
CPCC08J9/0023C08J9/0033C08J9/0061C08J9/0066C08J9/0095C08J9/102C08J9/103C08J9/105C08J2203/04C08J2323/16C08J2427/06C08J2471/02C08K2201/001C08L71/03C08L2203/20C08L2205/02C08L2205/035G03G15/0233C08L71/02C08L27/06C08L23/30C08K13/02C08K3/22C08K5/098C08K5/39C08K5/47
Inventor 黄本林李志刚罗兴亮杨树娟
Owner DONGGUAN WALTON RUBBER & PLASTIC NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap