Magnetic motor slot wedge and preparation method thereof

A motor slot wedge and magnetic technology, applied in the field of motors, can solve the problems of lack of mechanical strength, inability to meet long-term use, low permeability, etc., and achieve the effects of improving efficiency and service life, reducing temperature rise and noise, and high permeability

Inactive Publication Date: 2018-07-27
安徽省旌德县江南机电配件有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The magnetic slot wedges in the prior art have low magnetic permeability, and do

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1:

[0022] A magnetic motor slot wedge, the raw material of which is composed of unsaturated polyester resin, internal mold release agent, tert-butyl peroxide, dibenzoyl peroxide, reduced iron powder, alkali-free glass fiber, curing agent, accelerator , Multi-element iron-nickel alloy powder, iron-cobalt alloy powder, and iron-silicon alloy powder composition;

[0023] In terms of weight percentage, the above components are: 16% unsaturated polyester resin, 0.2% internal release agent, 0.9% tert-butyl peroxide, 0.3% dibenzoyl peroxide, 43% reduced iron powder , Alkali-free glass fiber 23%, diaminodiphenylmethane curing agent 1.2%, 2-methylimidazole accelerator 0.3%, iron-cobalt alloy powder 1.5%, iron-silicon alloy powder 3%, the balance is multi-element iron-nickel alloy powder ;

[0024] In terms of mass percentage content, in the multi-element iron-nickel alloy powder, the nickel content is 30%, the molybdenum content is 7%, the manganese content is 3%, the coppe...

Example Embodiment

[0030] Example 2:

[0031] A magnetic motor slot wedge, the raw material of which is composed of unsaturated polyester resin, internal mold release agent, tert-butyl peroxide, dibenzoyl peroxide, reduced iron powder, alkali-free glass fiber, curing agent, accelerator , Multi-element iron-nickel alloy powder, iron-cobalt alloy powder, and iron-silicon alloy powder composition;

[0032] In terms of weight percentage, the above components are: unsaturated polyester resin 20%, internal release agent 0.6%, tert-butyl peroxybenzoate 0.9%, dibenzoyl peroxide 0.6%, reduced iron powder 35% , Alkali-free glass fiber 17%, diaminodiphenylmethane curing agent 1.8%, 2-methylimidazole accelerator 0.1%, iron-cobalt alloy powder 3.5%, iron-silicon alloy powder 5%, the balance is multi-element iron-nickel alloy powder ;

[0033] In terms of mass percentage content, in the multi-element iron-nickel alloy powder, the nickel content is 40%, the molybdenum content is 0.2%, the manganese content is 10%, ...

Example Embodiment

[0039] Example 3:

[0040] A magnetic motor slot wedge, the raw material of which is composed of unsaturated polyester resin, internal mold release agent, tert-butyl peroxide, dibenzoyl peroxide, reduced iron powder, alkali-free glass fiber, curing agent, accelerator , Multi-element iron-nickel alloy powder, iron-cobalt alloy powder, and iron-silicon alloy powder composition;

[0041] In terms of weight percentages, the above components are: unsaturated polyester resin 17%, internal release agent 0.3%, t-butyl peroxide 0.8%, dibenzoyl peroxide 0.5%, reduced iron powder 37% , Alkali-free glass fiber 18%, diaminodiphenylmethane curing agent 1.3%, 2-methylimidazole accelerator 0.1%, iron-cobalt alloy powder 2%, iron-silicon alloy powder 3.5%, the balance is multi-element iron-nickel alloy powder ;

[0042] In terms of mass percentage content, in the multi-element iron-nickel alloy powder, the nickel content is 70%, the molybdenum content is 1%, the manganese content is 4%, the copper ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of motor, and in particular, relates to a magnetic motor slot wedge and a preparation method thereof. The invention provides the magnetic motor slot wedgecomprising the raw materials by the weight percentage: 16%-20% of unsaturated polyester resin, 0.2%-0.6% of an internal demoulding agent, 0.5%-0.9% of tert-butyl peroxybenzoate, 0.3%-0.6% of dibenzoylperoxide, 35%-43% of a reduced iron powder, 17%-23% of alkali-free glass fibers, 1.5%-3.5% of an iron-cobalt alloy powder, 3%-5% of an iron-silicon alloy powder and the like. The invention also provides the preparation method of the magnetic motor slot wedge. The prepared magnetic motor slot wedge has the characteristics of high magnetic conductivity, high splitting strength and high bending strength, can make the temperature rise and the noise reduce in operation of an electric generator, improves the efficiency and service life of a motor, and reduces the maintenance cost.

Description

technical field [0001] The invention relates to the technical field of motors, in particular to a magnetic motor slot wedge and a preparation method thereof. Background technique [0002] Due to the insulation and manufacturing process requirements of large and medium-sized AC high-voltage motors, the stator winding adopts formed coils, and the iron core of the stator is made into open slots. The opening of the slot will cause the change of cogging reluctance to be intensified, and the air gap magnetic density distribution will be uneven, which will increase the harmonic wave of the air gap magnetic conduction tooth, which will cause the increase of the motor excitation current, the increase of the rotor surface loss and the pulse vibration loss, resulting in The temperature rise of the motor increases and the efficiency decreases. The above-mentioned problems cannot be solved by adopting common slot wedges in large and medium-sized AC high-voltage motors. Magnetic slot we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/06C08K13/04C08K7/14C08K3/08C08K3/02C08K5/14
CPCC08K13/04C08K3/02C08K3/08C08K5/14C08K7/14C08K2003/023C08K2003/0843C08K2003/0856C08K2003/0862C08K2201/01C08L67/06
Inventor 侯观林丁玉青
Owner 安徽省旌德县江南机电配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap