Environmental-protection heatproof flame-retardation silicone rubber and preparation method thereof

A silicone rubber, environmentally friendly technology, applied in the field of flame retardant, can solve the problem of easy combustion of silicone rubber, achieve high heat resistance, stable performance, and improve the effect of heat resistance and flame retardancy

Inactive Publication Date: 2018-08-24
天长市荣盛有机硅科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the technical problems existing in the background technology, the present invention proposes an environmentally friendly heat-resistant and flame-retardant silicone rubber, which solves the problem that silicone rubber is easy to burn, improves the safety performance of silicone rubber, and has a simple preparation process and easy operation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An environmentally friendly heat-resistant and flame-retardant silicone rubber, the raw materials of which include by weight: 80 parts of methyl vinyl silicone rubber, 20 parts of carbon black, 10 parts of cerium carboxyethylphenyl hypophosphite, 1 part of melamine cyanurate, 0.5 parts of zinc borate, 1 part of silane coupling agent, 8 parts of zinc stearate, 5 parts of paraffin oil, 2 parts of sulfur powder, 2 parts of accelerator M, 2 parts of anti-aging agent BLE.

Embodiment 2

[0017] A kind of environment-friendly heat-resistant flame-retardant silicone rubber, its raw material comprises by weight: 120 parts of methyl vinyl silicone rubber, 30 parts of carbon black, 20 parts of carboxyethylphenyl lanthanum hypophosphite, 4 parts of melamine cyanurate, 2 parts of zinc borate, 3 parts of silane coupling agent, 12 parts of zinc stearate, 8 parts of paraffin oil, 3.5 parts of sulfur powder, 6 parts of accelerator DM, 4 parts of anti-aging agent RD.

Embodiment 3

[0019] A kind of environment-friendly heat-resistant flame-retardant silicone rubber, its raw material comprises by weight: 100 parts of methyl vinyl silicone rubber, 25 parts of carbon black, 14 parts of praseodymium carboxyethylphenyl hypophosphite, 2 parts of melamine cyanurate, 1 part of zinc borate, 2 parts of silane coupling agent, 10 parts of zinc stearate, 6.5 parts of paraffin oil, 3 parts of sulfur powder, 4 parts of accelerator TMTD, 3 parts of anti-aging agent 2246.

[0020] The preparation method of the above-mentioned environment-friendly heat-resistant and flame-retardant silicone rubber comprises the following steps: mixing methyl vinyl silicone rubber, carbon black, carboxyethylphenyl praseodymium phosphite, melamine cyanurate, zinc borate, silane coupling agent, Add paraffin oil and anti-aging agent 2246 into a mixer at 60°C and knead for 9 minutes, then add zinc stearate, sulfur powder and accelerator TMTD and knead for 9 minutes to prepare a masterbatch; put...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmental-protection heatproof flame-retardation silicone rubber. The heatproof flame-retardation silicone rubber comprises the following components: methyl vinyl silicone rubber, carbon black, carboxyethyl phenyl hypophosphorous acid metal salt, melamine cyanurate, zinc borate, a silane coupling agent, zinc stearate, a plasticizer, sulfur powder, a promoter, and anantioxidant. The invention also provides a preparation method of the environmental-protection heatproof flame-retardation silicone rubber. The method comprises the following steps: adding methyl vinylsilicone rubber, carbon black, carboxyethyl phenyl hypophosphorous acid metal salt, melamine cyanurate, zinc borate, the silane coupling agent, the plasticizer, and the antioxidant in a mixing machine and uniformly mixing the raw materials, adding zinc stearate, sulphur and the promoter and uniformly mixing the materials to prepare a mother material, and adding the mother material in a vulcanizerfor sulfuration to prepare the environmental-protection heatproof flame-retardation silicone rubber. The silicon material of the heatproof flame-retardation silicone rubber has the advantages of highoxygen index, no halogen, safety, environmental protection, and wide application prospect.

Description

technical field [0001] The invention relates to the technical field of flame retardancy, in particular to an environmentally friendly heat-resistant flame-retardant silicone rubber and a preparation method thereof. Background technique [0002] Silicone rubber refers to the rubber whose main chain is composed of silicon and oxygen atoms alternately, and there are usually two organic groups attached to the silicon atoms. Ordinary silicone rubber is mainly composed of silicone chains containing methyl groups and a small amount of vinyl groups. The introduction of phenyl groups can improve the high and low temperature resistance of silicone rubber, and the introduction of trifluoropropyl and cyano groups can improve the resistance of silicone rubber. Heat and oil resistance. Silicone rubber has good gas permeability, physiological inertia and other characteristics, and has a wide range of applications. [0003] In recent years, the flame retardant modification of silicone rub...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L91/06C08K13/02C08K3/04C08K5/5313C08K5/3492C08K3/38C08K5/098C08K3/06
CPCC08K2003/387C08L83/04C08L2201/02C08L2201/08C08L91/06C08K13/02C08K3/04C08K5/5313C08K5/34928C08K3/38C08K5/098C08K3/06
Inventor 张新华李保生
Owner 天长市荣盛有机硅科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap