A kind of preparation method of vanadium-doped strontium titanate nanometer photocatalytic material

A catalytic material, strontium titanate technology, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problem of large microstructure adjustability of materials , to achieve the effects of low preparation cost, low reaction temperature and strong visible light response ability

Active Publication Date: 2021-04-16
WUHAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composition elements of perovskite are diverse, but the basic structure is similar. Past research on perovskite has provided the basis for the study of its physical properties and solid-state chemical properties, and provided guidance for the application of perovskite; the good crystal form of perovskite has It is beneficial to the characterization of the bulk phase structure, and it is also beneficial to infer its surface properties from the bulk phase structure, because the catalytic reaction mostly occurs on the surface of the catalyst, so mastering the surface properties of the catalyst is very critical for analyzing the reaction mechanism; in addition, because the elements that make up the perovskite itself and The diversity of doping elements, the valence state, stoichiometric ratio and defect density of different perovskite elements also have many differences, and the microstructure of the material is highly adjustable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of vanadium-doped strontium titanate nanometer photocatalytic material
  • A kind of preparation method of vanadium-doped strontium titanate nanometer photocatalytic material
  • A kind of preparation method of vanadium-doped strontium titanate nanometer photocatalytic material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Weigh 2.11g (0.01mol) Sr(NO 3 ) 2 Dissolve in 20ml deionized water, stir until completely dissolved;

[0035] 2. Add 2.8ml (C) dropwise to the solution obtained in a. 3 h 7 O) 4 Ti (ρ=0.9600g / mL), stirring while adding, to obtain a white suspension system as dispersed as possible;

[0036]3. Immediately add 0.8g NaOH to the mixed system obtained in b, and set the volume to 40ml (the concentration of NaOH is 0.5mol / L);

[0037] 4. Use an ultrasonic disperser to fully dissolve the Chinese medicine c, transfer it to a 50ml hydrothermal reaction kettle, and keep it warm at 200°C for 24 hours;

[0038] 5. The obtained SrTiO 3 A small amount of SrCO was washed away with 1% dilute nitric acid solution 3 , and then washed with deionized water, dried at 80°C for later use, and the obtained white solid powder is undoped pure phase strontium titanate.

Embodiment 2

[0040] 1. Weigh 2.11g (0.01mol) Sr(NO 3 ) 2 Dissolve in 20ml deionized water, stir until completely dissolved;

[0041] 2. Add 2.8ml (C) dropwise to the solution obtained in a. 3 h 7 O) 4 Ti (ρ=0.9600g / mL), stirring while adding, to obtain a white suspension system as dispersed as possible;

[0042] 3. Put 0.0045g of V 2 o 5 Add the mixed system obtained in b, while fully stirring, then add 0.8g NaOH, and set the volume to 40ml (the concentration of NaOH is 0.5mol / L);

[0043] 4. Use an ultrasonic disperser to fully dissolve the Chinese medicine c, transfer it to a 50ml hydrothermal reaction kettle, and keep it warm at 200°C for 24 hours;

[0044] 5. The obtained SrTiO 3 A small amount of SrCO was washed away with 1% dilute nitric acid solution 3 , and then washed with deionized water, dried at 80° C. for later use, and the obtained yellow solid powder is vanadium-doped strontium titanate with a doping amount of 0.5 mol%.

Embodiment 3

[0046] 1. Weigh 2.11g (0.01mol) Sr(NO 3 ) 2 Dissolve in 20ml deionized water, stir until completely dissolved;

[0047] 2. Add 2.8ml (C) dropwise to the solution obtained in a. 3 h 7 O) 4 Ti (ρ=0.9600g / mL), stirring while adding, to obtain a white suspension system as dispersed as possible;

[0048] 3. Add 0.0091g ​​of V 2 o 5 Add the mixed system obtained in b, while fully stirring, then add 0.8g NaOH, and set the volume to 40ml (the concentration of NaOH is 0.5mol / L);

[0049] 4. Use an ultrasonic disperser to fully dissolve the Chinese medicine c, transfer it to a 50ml hydrothermal reaction kettle, and keep it warm at 200°C for 24 hours;

[0050] 5. The obtained SrTiO 3 A small amount of SrCO was washed away with 1% dilute nitric acid solution 3 , and then washed with deionized water, dried at 80° C. for later use, and the obtained yellow solid powder is vanadium-doped strontium titanate with a doping amount of 1.0 mol%.

[0051] Do a series of tests for embodimen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing vanadium-doped strontium titanate nanometer photocatalytic material. Mix the vanadium sources required for doping, and then react for several hours under high temperature conditions, and finally grow into vanadium-doped strontium titanate. The method has the characteristics of few types of raw materials, simple operation method, simple process, low cost, and environmental protection. The prepared vanadium-doped strontium titanate photocatalytic material is useful for studying its photoresponsive photocatalytic mechanism and for other perovskite photocatalytic materials. The preparation is of great significance.

Description

technical field [0001] The invention belongs to the technical field of preparation of photocatalytic nanometer materials and treatment of environmental pollutants, and in particular relates to a preparation method and application of metal vanadium ion-doped strontium titanate. Background technique [0002] In 1972, Japanese scientists Fujishima and Honda used TiO 2 Experiments with electrodes for photocatalytic water splitting opened the door to research on semiconducting oxides as photocatalysts. Following TiO 2 Later, it was found that with d 0 The electronic configuration of titanate, niobate, tantalate and in the p region has d 10 Electron-configured photocatalysts have certain advantages in visible light response. Among them, titanates with perovskite structure, as a kind of semiconductor oxide photofunctional materials, have become one of the focuses in the field of photocatalysis in the past ten years. [0003] Perovskite has attracted attention in the field of ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/22B01J35/02
CPCB01J23/22B01J35/004B01J35/023
Inventor 曾玉彬王传义邓翠萍赵杰
Owner WUHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com