Thermoplastic elastomer particle for dish washing machine and preparation method
A thermoplastic elasticity, dishwasher technology, applied in the field of dishwasher sealing materials and preparation, can solve the problems of poor compensation of EPDM rubber materials, unstable vulcanization and foaming processes, and easy bulging of sealing strips. Good mechanical properties, improved anti-oxidative degradation performance, good sealing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0020] Using the above-mentioned preparation method of thermoplastic elastomer pellets for dishwashers, the specific steps are:
[0021] Step 1: Weighing: Accurately weigh each component according to the number of parts in claim 1;
[0022] Step 2: Uniform mixing: Put the hydrogenated styrene-butadiene block copolymer and extender oil accurately weighed according to claim 1 into the high-speed mixer, and set the speed of the high-speed mixer to 500 -800r / min, the mixing time is 10min. After the mixing is completed, add polypropylene, ethylene-vinyl acetate copolymer, fillers, pigments, and anti-corrosion materials that are accurately weighed according to the range of parts in claim 1 Oxygen, lubricant and anti-fungal agent. At this time, the speed of the high-speed mixer is set to 1000~1500r / min, the mixing time is 5min, and the material is mixed evenly;
[0023] Step 3: Granulation: Put the uniformly mixed materials in step 2 into the twin-screw granulator for melt-shearing extrusi...
Example Embodiment
[0025] Example one:
[0026] The thermoplastic elastomer pellets used for dishwashers in the present invention are weighed (weight) as follows:
[0027] (Table 1:)
[0028] Hydrogenated styrene-butadiene block copolymer
[0029] Put the hydrogenated styrene-butadiene block copolymer and filler oil accurately weighed in accordance with (Table 1:) into the high-speed mixer. The speed of the high-speed mixer is set to 500-800r / min, and the mixing time is 10min. Add polypropylene, ethylene-vinyl acetate copolymer, fillers, pigments, antioxidants, lubricants and antifungal agents that have been accurately weighed in accordance with (Table 1:) to the materials after this mixing is completed. The rotating speed of the mixer is set to 1000~1500r / min, the mixing time is 5min, and the material is obtained by uniform mixing;
[0030] Put the uniformly mixed materials into the twin-screw granulator for melt-shearing extrusion granulation. The parameters of the twin-screw granulator are set to...
Example Embodiment
[0032] Embodiment two:
[0033] (Table 2:)
[0034] Hydrogenated styrene-butadiene block copolymer
[0035] Put the hydrogenated styrene-butadiene block copolymer and extender oil accurately weighed according to (Table 2:) into the high-speed mixer. The speed of the high-speed mixer is set to 500-800r / min, and the mixing time is 10min. Add polypropylene, ethylene-vinyl acetate copolymer, fillers, pigments, antioxidants, lubricants and anti-fungal agents that have been accurately weighed in accordance with (Table 2:) to the materials after this mixing is completed. The rotating speed of the mixer is set to 1000~1500r / min, the mixing time is 5min, and the material is obtained by uniform mixing;
[0036] Put the uniformly mixed materials into the twin-screw granulator for melt-shearing extrusion granulation. The parameters of the twin-screw granulator are set to a temperature of 170°C in the first zone, 170°C in the second zone, and a temperature in the third zone 180℃, the tempera...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction