Waterproof and heat insulation coating and preparation method thereof

A technology for thermal insulation coatings and raw materials, applied in the direction of starch coatings, polyester coatings, coatings, etc., can solve the problems of low adhesion and poor thermal insulation performance of coatings, and achieve enhanced adhesion performance, low surface energy, and excellent hydrophobic properties and the effect of self-cleaning performance

Inactive Publication Date: 2018-12-28
合肥久新不锈钢厨具有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the insulation performance of the coating prepared by this invention is poor, and the bonding force between building materials is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof and heat insulation coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment relates to a waterproof and thermal insulation coating, which includes the following raw materials in parts by weight: 45 parts of starch-modified acrylic emulsion, 12 parts of modified magnesium stearate powder, 4 parts of polyester fiber, 5 parts of aluminum silicate fiber cotton, 10 parts of thickening agent, 6 parts of sodium dodecylbenzene sulfate, 3 parts of sodium rosinate, 4 parts of polyoxypropylene polyoxyethylene copolymer, 8 parts of silicone defoamer, and 10 parts of silane coupling agent.

[0028] Wherein, the preparation method of the starch-modified acrylic acid emulsion is: adding starch and acrylic acid emulsion into a closed reaction vessel at a mass ratio of 1:2, heating at 60°C, and then adding 3-aminopropyltrimethoxy The mixture of silane, stannous octoate and triethylamine was stirred at a speed of 100r / min for 2 hours, cooled naturally to 30°C, and then pentaerythritol was slowly added dropwise at a rate of 1 drop / min, and 20 Minu...

Embodiment 2

[0038]This embodiment relates to a waterproof and thermal insulation coating, which includes the following raw materials in parts by weight: 55 parts of starch-modified acrylic emulsion, 16 parts of modified magnesium stearate powder, 8 parts of polyester fiber, 8 parts of aluminum silicate fiber cotton, 16 parts of thickening agent, 12 parts of sodium dodecylbenzene sulfate, 7 parts of sodium rosinate, 8 parts of polyoxypropylene polyoxyethylene copolymer, 12 parts of silicone defoamer, and 16 parts of silane coupling agent.

[0039] Wherein, the preparation method of the starch-modified acrylic acid emulsion is: adding starch and acrylic acid emulsion into a closed reaction vessel at a mass ratio of 1:2, heating at 80°C, and then adding 3-aminopropyltrimethoxy The mixture of silane, stannous octoate and triethylamine was stirred at a speed of 140r / min for 4 hours, cooled naturally to 38°C, and then pentaerythritol was slowly added dropwise at a rate of 1 drop / min, and 20 Min...

Embodiment 3

[0049] This embodiment relates to a waterproof and thermal insulation coating, which includes the following raw materials in parts by weight: 47 parts of starch-modified acrylic emulsion, 13 parts of modified magnesium stearate powder, 5 parts of polyester fiber, 6 parts of aluminum silicate fiber cotton, 12 parts of thickener, 8 parts of sodium dodecylbenzene sulfate, 4 parts of sodium rosinate, 5 parts of polyoxypropylene polyoxyethylene copolymer, 9 parts of silicone defoamer, 12 parts of silane coupling agent.

[0050] Wherein, the preparation method of the starch-modified acrylic acid emulsion is: adding starch and acrylic acid emulsion into a closed reaction vessel at a mass ratio of 1:2, heating at 60°C, and then adding 3-aminopropyltrimethoxy The mixture of silane, stannous octoate and triethylamine was stirred at a speed of 100r / min for 2 hours, cooled naturally to 30°C, and then pentaerythritol was slowly added dropwise at a rate of 1 drop / min, and 20 Minutes, then s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof and heat insulation coating and a preparation method thereof, and relates to the technical field of coatings. The coating comprises raw materials in parts by weight as follows: 45-55 parts of starch modified acrylic emulsion, 12-16 parts of modified magnesium stearate powder, 4-8 parts of polyester fiber, 5-8 parts of aluminium silicate cellucotton, 10-16 partsof a thickener, 6-12 parts of sodium dodecyl benzene sulfate, 3-7 parts of sodium abietate, 4-8 parts of a polyoxyethylene-polyoxypropylene copolymer, 8-12 parts of a silicone defoamer and 10-16 parts of a silane coupling agent. The preparation method of the coating comprises the step of mixing and stirring the materials. The coating has quite excellent waterproof and heat insulation properties and has high adhesion to building materials.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a waterproof and thermal insulation coating and a preparation method thereof. Background technique [0002] At present, coatings are generally applied on building materials to avoid oxidation of materials and improve the aesthetics of materials. In the prior art, most coatings are generally poor in waterproof performance and thermal insulation performance, and their adhesion is average. After being washed away by rain, sunlight, etc. over time, the paint is easy to fall off, resulting in unsightly buildings, and cannot protect building materials, resulting in shortened service life. [0003] The Chinese invention patent application with the publication number CN102719155A discloses a polymer waterproof coating and a preparation method thereof, which is made of powder and liquid in a weight ratio of 1-5:1; the powder is prepared in parts by weight The number includes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D103/02C09D167/00C09D7/61C09D7/63C09D7/65C09D7/44
CPCC08L2205/035C08L2205/16C09D7/44C09D7/61C09D7/63C09D7/65C09D7/70C09D133/00C08L3/02C08L67/00C08L71/02C08L93/04C08L5/00C08L33/26C08L5/12C08K13/06C08K9/04C08K5/098C08K7/10C08K5/41
Inventor 辛松
Owner 合肥久新不锈钢厨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com