Acrylic resin coating material, preparation and application in aluminum profile

A technology of acrylic resin and methacrylic acid, applied in the direction of coating, etc., can solve the problems of environmental protection, etc., and achieve the effects of fast drying speed, excellent film-forming performance, excellent wear resistance and water resistance

Inactive Publication Date: 2019-02-19
CHANGSHA XIAORU INFORMATION TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a kind of acrylic resin coating and its preparation and application in alu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic resin coating material, preparation and application in aluminum profile
  • Acrylic resin coating material, preparation and application in aluminum profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method for acrylic resin paint, comprising the steps of:

[0030] (1) Butyl methacrylate, isooctyl acrylate, glycidyl methacrylate, methacrylic acid and dicyclohexylmethane-4,4'-diisocyanate, vinyltriethoxysilane, 3-amino Mix propyltrimethoxysilane evenly, then drop it into deionized water at a constant speed, control the dropping time for 30 minutes, stir, ultrasonically oscillate, add the initiator, heat to 70°C under nitrogen atmosphere, keep it warm for 1 hour, and continue heating to 80°C, keep warm for 2 hours, and cool to room temperature to obtain a modified acrylic emulsion, which is set aside;

[0031] (2) Put the diphenyl ether formaldehyde resin and sucrose polyester into the reaction kettle, add deionized water and sodium dodecylbenzenesulfonate, heat to 85°C, stir and emulsify for 1 hour to obtain modified diphenyl ether Formaldehyde resin, spare;

[0032] (3) Deionized water, modified acrylic emulsion, modified diphenyl ether formaldehyde ...

Embodiment 2

[0043] A preparation method for acrylic resin paint, comprising the steps of:

[0044](1) Butyl methacrylate, isooctyl acrylate, glycidyl methacrylate, methacrylic acid and dicyclohexylmethane-4,4'-diisocyanate, vinyltriethoxysilane, 3-amino Propyltrimethoxysilane is mixed evenly, then dropped into deionized water at a constant speed, the dropping time is controlled at 50 minutes, stirred, ultrasonically oscillated, and the initiator is added, heated to 75°C under a nitrogen atmosphere, kept for 2 hours, and continued to heat to 85°C, keep warm for 3 hours, and cool to room temperature to obtain a modified acrylic emulsion, which is set aside;

[0045] (2) Put the diphenyl ether formaldehyde resin and sucrose polyester into the reaction kettle together, add deionized water and sodium dodecylbenzenesulfonate, heat to 95°C, stir and emulsify for 2 hours to obtain modified diphenyl ether Formaldehyde resin, spare;

[0046] (3) Deionized water, modified acrylic emulsion, modifie...

Embodiment 3

[0057] A preparation method for acrylic resin paint, comprising the steps of:

[0058] (1) Butyl methacrylate, isooctyl acrylate, glycidyl methacrylate, methacrylic acid and dicyclohexylmethane-4,4'-diisocyanate, vinyltriethoxysilane, 3-amino Mix propyltrimethoxysilane evenly, then drop it into deionized water at a constant speed, control the dropping time for 30 minutes, stir, ultrasonically oscillate, add the initiator, heat to 75°C under nitrogen atmosphere, keep it warm for 1 hour, and continue heating to 85°C, heat preservation for 2 hours, and cool to room temperature to obtain a modified acrylic emulsion, which is set aside;

[0059] (2) Put the diphenyl ether formaldehyde resin and sucrose polyester into the reaction kettle, add deionized water and sodium dodecylbenzenesulfonate, heat to 95°C, stir and emulsify for 1 hour to obtain modified diphenyl ether Formaldehyde resin, spare;

[0060] (3) Deionized water, modified acrylic emulsion, modified diphenyl ether forma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an acrylic resin coating material, preparation and an application in an aluminum profile. The modified acrylic emulsion is taken as a main raw material, modified diphenyl etherformaldehyde resin and the like are supplemented to prepare the acrylic resin coating material, the volatile organic compound (VOC) content is low, the environmental protection standard is met, the film forming performance on the surface of the aluminum profile is excellent, the abrasion resistance and the water resistance are excellent, and the drying speed is fast.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an acrylic resin coating and its preparation and application in aluminum profiles. Background technique [0002] Traditional aluminum profile surface treatment methods are generally divided into anodizing, electrophoretic coating, fluorocarbon spraying and powder coating. A large amount of water is required in the process of anodizing and electrophoretic coating, and at the same time, a large amount of wastewater will be generated after treatment, which is difficult to treat and causes great pollution to the environment. Anodizing and electrocoating are also very power-hungry during the process. The cost of fluorocarbon spraying is high, the control is difficult, and the coating is very prone to orange peel. It is difficult to ensure the thickness of the coating by powder coating, and it is easy to fade. [0003] With the implementation of the new environmental protection law...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/10C09D161/00C09D7/61
CPCC08K2003/2241C08K2201/011C09D133/10C09D7/61C08L61/00C08K3/36C08K3/22
Inventor 不公告发明人
Owner CHANGSHA XIAORU INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap