A kind of graphene/aluminum composite conductive material and preparation method thereof

A technology of aluminum composite materials and conductive materials, applied in the direction of graphene, cable/conductor manufacturing, metal/alloy conductors, etc., can solve problems such as difficulty in uniform dispersion, easy agglomeration, and density difference, so as to avoid agglomeration and enhance mechanical properties and conductivity, to ensure the effect of uniform distribution

Active Publication Date: 2021-01-12
苏州碳素集电新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The huge difference in density makes it difficult to mix conventional powders uniformly;
[0010] (2) The C-C bond in conventionally prepared graphene is a strong hydrophobic structure, so it is very easy to agglomerate and it is difficult to disperse evenly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene/aluminum composite conductive material and preparation method thereof
  • A kind of graphene/aluminum composite conductive material and preparation method thereof
  • A kind of graphene/aluminum composite conductive material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]The invention provides a method for preparing a graphene / aluminum composite conductive material, which can solve the technical problem of uniform dispersion of graphene in the composite material, thereby achieving optimal mechanical properties and electrical conductivity.

[0040]The preparation method of graphene / aluminum composite conductive material includes the following steps:

[0041](1) Preparation of porous graphene on organic substrates

[0042]Expose one surface of an organic polymer film polyimide with a thickness of 150um to laser radiation, the laser is selected as CO with a wavelength of 10.6μm2Infrared laser, laser power is 5W, pulse frequency is 20kHz, laser scanning speed is 800mm / s. The surface of the polyimide film is carbonized to form porous graphene, that is, porous graphene on an organic substrate is obtained, and the pore structure is asfigure 2 As shown, the thickness of porous graphene is 100 microns, such asimage 3 As shown, the Raman spectrum of porous graph...

Embodiment 2

[0049]The preparation method of the graphene / aluminum composite conductor material in this embodiment is the same as that in Embodiment 1, the laser power used is 4W, and the other conditions are the same as in Embodiment 1. The tensile strength of the prepared composite material is 293Mpa, and the electrical conductivity is 60% IACS.

Embodiment 3

[0051]The preparation method of the graphene / aluminum composite conductor material in this example is the same as that in Example 1, the aluminum powder particle size used is an average of 10 μm, and the other conditions are the same as in Example 1. The tensile strength of the prepared composite material is 315Mpa, and the conductivity is 68% IACS.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a graphene / aluminum composite conductive material and a preparation method thereof. The preparation method comprises the following steps: firstly, exposing an organic polymer film to laser irradiation to prepare porous graphene; adsorbing and permeating aluminum powder particles into a porous network of graphene, and carrying out high-temperature sintering treatment to obtain a graphene / aluminum composite material precursor; and finally, sequentially treating the precursor through a pressure infiltration process, a hot extrusion process and a hot annealing process to obtain the graphene / aluminum composite conductive material. In the preparation method, the graphene in the graphene / aluminum composite conductive material is formed by directly carbonizing the organic polymer under the laser irradiation, and the part, not affected by the laser, of the organic polymer film serves as a substrate to support the graphene, so that the agglomeration of the graphene is effectively avoided, and the uniform distribution of the graphene in the composite material is achieved. Compared with pure aluminum without graphene, the electrical conductivity and mechanical propertyof the graphene / aluminum composite material are both improved.

Description

Technical field[0001]The invention relates to the field of graphene-based composite materials, in particular to a graphene / aluminum composite conductive material and a preparation method thereof.Background technique[0002]Graphene is a two-dimensional material with a single layer of carbon atoms forming a honeycomb structure. The carbon atoms form bonds through sp hybridization. Each carbon atom forms a σ bond with three adjacent carbon atoms, and the remaining p orbitals alternately form a conjugated π bond. Thanks to this special two-dimensional structural feature, graphene has excellent properties in terms of electricity, mechanics, and heat:[0003](1) Electricity: Graphene has a large π bond that allows π electrons to move freely. This gives graphene excellent conductivity, and its electron mobility can reach 15000cm2 / (V·S), approximately 140 times the electron mobility in silicon, is the material with the best conductivity at room temperature.[0004](2) In terms of mechanics, grap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B13/00H01B1/02H01B1/04C01B32/184
CPCC01B32/184H01B1/02H01B1/04H01B13/00H01B13/0026
Inventor 鞠宝钢陈杰李年
Owner 苏州碳素集电新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap