Preparation method of modified hydroxyethyl cellulose cation slow-cracking asphalt emulsifier

A technology of hydroxyethyl cellulose and asphalt emulsifier, used in building components, building insulation materials, construction and other directions, can solve the problems of increased wastewater treatment cost, poor water solubility, unfavorable promotion, etc., and achieves excellent surface activity and mild reaction conditions. , the effect of low price

Active Publication Date: 2019-05-10
HEBEI UNIV OF TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned small molecule emulsifiers have a generally high critical micelle concentration at normal temperature; and chitosan-based emulsifiers need to consume a large amount of acid in the production proces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Preparation of emulsifier

[0031] Dissolve 27.69g (0.13mol) of dodecyldimethyl tertiary amine in 20ml of absolute ethanol, raise the temperature to 60°C, and slowly add 15.64g (0.17mol) of epichlorohydrin (60-70 minutes), React at 60°C for 6h, after cooling to room temperature, distill at 45°C for 60 minutes with a rotary evaporator to remove solvent and unreacted raw materials; vacuum dry at 45°C to obtain a long-chain quaternary ammonium salt intermediate.

[0032] Disperse 7.4g (0.01mol) of hydroxyethyl cellulose in 25ml of isopropanol, add 20ml of NaOH solution (concentration: 12wt%), swell at room temperature for 13h, then raise the temperature to 45°C, add 12.22g (0.04mol) of the above Chain quaternary ammonium salt intermediate, react at 45°C for 5h, cool to room temperature, centrifuge, wash; dry at 80°C to obtain modified hydroxyethyl cellulose cationic slow-cracking asphalt emulsifier.

[0033] The critical micelle concentration (CMC) of the above-mentioned ...

Embodiment 2

[0038] Preparation of emulsifier

[0039]Dissolve 31.33g (0.13mol) of tetradecyldimethyl tertiary amine in 20ml of anhydrous methanol, raise the temperature to 65°C, and slowly add 16.65g (0.18mol) of epichlorohydrin (60-70 minutes), React at 65°C for 6h, cool to room temperature, and distill at 50°C for 70 minutes with a rotary evaporator to remove solvent and unreacted raw materials; vacuum dry at 45°C to obtain a long-chain quaternary ammonium salt intermediate. Disperse 7.4g (0.01mol) of hydroxyethyl cellulose in 25ml of isopropanol, add 20ml of NaOH solution (concentration: 14wt%), swell at room temperature for 14h, then raise the temperature to 50°C, add 13.34g (0.04mol) of the above Chain quaternary ammonium salt intermediate, react at 50°C for 5h, cool to room temperature, centrifuge, wash; dry at 80°C to obtain modified hydroxyethyl cellulose cationic slow-cracking asphalt emulsifier.

[0040] The critical micelle concentration (CMC) of the above-mentioned modified h...

Embodiment 3

[0044] Preparation of emulsifier

[0045] Dissolve 34.97g (0.13mol) of hexadecyldimethyl tertiary amine in 20ml of isopropanol, raise the temperature to 65°C, and slowly add 16.65g (0.18mol) of epichlorohydrin (60-70 minutes), React at 65°C for 6h, after cooling to room temperature, use a rotary evaporator to distill at 40°C for 70 minutes to remove solvent and unreacted raw materials; vacuum dry at 45°C to obtain a long-chain quaternary ammonium salt intermediate. Disperse 7.4g (0.01mol) of hydroxyethyl cellulose in 25ml of isopropanol, add 20ml of NaOH solution (concentration: 15wt%), swell at room temperature for 16h, then raise the temperature to 50°C, add 14.46g (0.04mol) of the above Chain quaternary ammonium salt intermediate, react at 50°C for 5h, cool to room temperature, centrifuge, wash; dry at 80°C to obtain modified hydroxyethyl cellulose cationic slow-cracking asphalt emulsifier.

[0046] The critical micelle concentration (CMC) of the above-mentioned modified h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Critical micelle concentrationaaaaaaaaaa
Critical micelle concentrationaaaaaaaaaa
Critical micelle concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a modified hydroxyethyl cellulose cation slow-cracking asphalt emulsifier. The method comprises the following steps: adding hydroxyethyl celluloses intoisopropanol for dispersion, adding a NaOH solution, then swelling for 12-16 h at normal temperature, heating to the temperature of 40-50 DEG C, adding a long-chain quaternary ammonium salt intermediate, reacting for 4-6 h at the temperature of 40-50 DEG C, cooling to the room temperature, centrifuging and washing; and drying at the temperature of 80 DEG C to obtain the modified hydroxyethyl cellulose cation slow-cracking asphalt emulsifier. The raw materials of the emulsifier prepared by the invention are environmentally friendly, the price is low, a preparation process is simple, the production cost is low, and the emulsification performance is high.

Description

technical field [0001] The invention relates to a preparation method of a modified hydroxyethyl cellulose cationic asphalt emulsifier, belonging to the technical field of fine chemicals. Background technique [0002] With the construction of the modern urban comprehensive transportation system and the improvement of the road network structure, the regular maintenance and repair of the road surface is becoming more and more important. Emulsified asphalt has become an important material in road repair and maintenance technology due to its unique room temperature construction, energy saving, low VOC, environmental protection and many other advantages. Among them, cationic asphalt emulsion is widely used because of its own characteristics, when it contacts with stone, its adhesion is stronger and it is not easy to fall off. Slurry seal is an effective means of highway maintenance, but the asphalt emulsion and stones need to be stirred before construction, which requires the asp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08B11/145C08J3/03C08L95/00
Inventor 王月欣侯闰翰张倩张子旭王晓曦高孟瑶
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap