BOPET anti-UV master batch material and preparation process thereof

A master batch and mixer technology, applied in the field of polymer materials, can solve the problem of low service life of BOPET film, and achieve the effects of being suitable for promotion, simple preparation process and uniform color and luster.

Inactive Publication Date: 2019-06-07
SHENZHEN JINZHICHENG PLASTIC TECH CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a BOPET anti-UV masterbatch material and its preparation process, which ha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A BOPET anti-UV masterbatch material, comprising the following ingredients: 5 parts of light stabilizer, 3 parts of antioxidant, 3 parts of insect repellent, 5 parts of coloring agent, 5 parts of compatibilizer, 3 parts of nucleating agent, 5 parts of dispersed lubricant, 10 parts of filler and 20 parts of carrier resin, wherein the light stabilizer is a mixture of light shielding agent, ultraviolet absorber and quencher, wherein the light shielding agent is carbon black, and the ultraviolet absorber is o-hydroxyl A mixture of benzophenone, benzotriazole and salicylate, the quencher is a divalent organonickel chelate, the antioxidant is butylhydroxyanisole, the insect repellent is deltamethrin, and the coloring agent It is one of titanium dioxide, zinc powder, cadmium red, ferric oxide, chrome yellow, zinc yellow and Hansa yellow, the compatibilizer is oxazoline, the nucleating agent is rosin nucleating agent, and the dispersing lubricant is three A mixture of ethylhexy...

Embodiment 2

[0034] A BOPET anti-UV masterbatch material, comprising the following ingredients: 6 parts of light stabilizer, 4 parts of antioxidant, 4 parts of insect repellent, 6 parts of colorant, 6 parts of compatibilizer, 4 parts of nucleating agent, 6 parts of dispersed lubricant, 11 parts of filler and 25 parts of carrier resin, wherein the light stabilizer is a mixture of light shielding agent, ultraviolet absorber and quencher, wherein the light shielding agent is carbon black, and the ultraviolet absorber is o-hydroxyl A mixture of benzophenone, benzotriazole and salicylate, the quencher is a divalent organonickel chelate, the antioxidant is butylhydroxyanisole, the insect repellent is deltamethrin, and the coloring agent It is one of titanium dioxide, zinc powder, cadmium red, ferric oxide, chrome yellow, zinc yellow and Hansa yellow, the compatibilizer is oxazoline, the nucleating agent is rosin nucleating agent, and the dispersing lubricant is three A mixture of ethylhexyl phos...

Embodiment 3

[0043]A BOPET anti-UV masterbatch material, comprising the following ingredients: 7 parts of light stabilizer, 5 parts of antioxidant, 5 parts of insect repellent, 7 parts of colorant, 7 parts of compatibilizer, 5 parts of nucleating agent, 7 parts of dispersed lubricant, 13 parts of filler and 30 parts of carrier resin, wherein the light stabilizer is a mixture of light shielding agent, ultraviolet absorber and quencher, wherein the light shielding agent is carbon black, and the ultraviolet absorber is o-hydroxyl A mixture of benzophenone, benzotriazole and salicylate, the quencher is a divalent organonickel chelate, the antioxidant is butylhydroxyanisole, the insect repellent is deltamethrin, and the coloring agent It is one of titanium dioxide, zinc powder, cadmium red, ferric oxide, chrome yellow, zinc yellow and Hansa yellow, the compatibilizer is oxazoline, the nucleating agent is rosin nucleating agent, and the dispersing lubricant is three A mixture of ethylhexyl phosp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a BOPET anti-UV master batch material and a preparation process thereof, and relates to the technical field of high polymer materials. The light-cured insect-resistant plasticcomprises the following components in parts by weight: 5-7 parts of a light stabilizer, 3-5 parts of an antioxidant, 3-5 parts of an insect-resistant agent, 5-7 parts of a coloring agent, 5-7 parts ofa compatilizer, 3-5 parts of a nucleating agent, 5-7 parts of a dispersion lubricant, 10-13 parts of a filling agent and 20-30 parts of carrier resin. The light stabilizer is a mixture of a light shielding agent, an ultraviolet light absorber and a quenching agent, wherein the light shielding agent is carbon black, the ultraviolet light absorber is a mixture of o-hydroxydiphenyl ketone, benzotriazole and salicylate, and the quenching agent is a divalent organic nickel chelate. The light stabilizer is a mixture of a light shielding agent, an ultraviolet light absorber and a quenching agent, the light shielding agent is carbon black, the ultraviolet light absorber is a mixture of o-hydroxybenzophenone, benzotriazole and salicylate, and the quenching agent is a divalent organic nickel chelate. The BOPET master batch is uniform in color and luster and can delay aging caused by solar radiation under direct sunlight radiation.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a BOPET anti-UV masterbatch material and a preparation process thereof. Background technique [0002] BOPET film is a biaxially oriented polyester film. BOPET film has the characteristics of high strength, good rigidity, transparency, and high gloss; it is odorless, tasteless, colorless, non-toxic, and outstanding toughness; its tensile strength is 3 times that of PC film and nylon film, and its impact strength is BOPP 3-5 times that of the film, with excellent wear resistance, folding resistance, pinhole resistance and tear resistance, etc.; heat shrinkage is extremely small, at 120 ° C, only shrinks 1.25% after 15 minutes; has Good antistatic properties. The full name of masterbatch is plastic masterbatch, alias masterbatch is a kind of plastic processing aid developed in the 1980s. It is composed of excessive chemical additives, carrier resin and dispersant. Maste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08L93/04C08K13/02C08K5/07C08K3/04C08K5/3475C08K3/26C08K5/353C08K5/41C08K3/22C08K3/08C08K5/315C08J3/22
Inventor 程志成
Owner SHENZHEN JINZHICHENG PLASTIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap