A preparation method of nano-modified film material for improving polymer insulation surface resistance

A nano-modification, membrane material technology, applied in the coating and other directions, can solve the problems of unstable treatment effect, limited duration of fluorination effect, poor controllability, etc., to achieve excellent adhesion, reduced viscosity, controllable high sex effect

Active Publication Date: 2020-05-22
XI AN JIAOTONG UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, by opening the chemical bonds on the surface of the material by plasma to graft fluorine, the controllability is poor, the treatment effect is unstable, and the duration of the fluorination effect is limited. There are still key technical problems that need to be broken through.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of nano-modified film material for improving polymer insulation surface resistance
  • A preparation method of nano-modified film material for improving polymer insulation surface resistance
  • A preparation method of nano-modified film material for improving polymer insulation surface resistance

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] see figure 1 , a preparation method of nano-modified film materials for improving polymer insulation surface resistance, firstly through silane coupling, silane-modified perfluoropolyether and KH570 (γ -(methacryloyloxy)propyltrimethoxysilane) grafted onto the surface of the nanoparticle material to prepare a modified nanopowder; then add the modified nanopowder to the photocurable resin according to a certain proportion, After ultrasonic treatment, stirring and solution dispersion, etc., it is evenly coated on the surface of the insulating material by spraying or roller coating, and finally, the rapid curing of the resin is completed by irradiation with an LED ultraviolet light source with a wavelength of 365nm or 405nm; the specific steps are as follows:

[0040] S1. Through silane coupling, graft photocurable KH570 and silane-modified perfluoropolyether onto the surface of nanoparticles such as alumina, silica or zinc oxide, and achieve double Coupling to obtain mod...

Embodiment 1

[0061] Preparation of modified nanoparticles:

[0062] (1) Prepare the solution

[0063] To treat 100g of nano-alumina, first add KH570 with a concentration of 2wt%, then add modified perfluoropolyether with a concentration of 2wt%, and finally add it to 100ml of 95% ethanol to prepare a mixed solution;

[0064] (2) Adjust the pH of the solution

[0065] According to the pH value of the solution corresponding to each group of tests, use glacial acetic acid and 25% ammonia water to adjust the pH of the solution to 5;

[0066] (3) Coupling

[0067] Put the prepared solution into a round bottom flask, heat it to the corresponding temperature of the test plan by using a water bath, add 100g of nano-alumina, and react for 1h under the dispersion mode of magnetic stirring (100r / min). Condensation reflux;

[0068] (4) cleaning

[0069] Wash the nanoparticles multiple times with a suction filter to remove residues that have not undergone a coupling reaction with the surface of th...

Embodiment 2

[0078] Preparation of modified nanoparticles:

[0079] (1) Prepare the solution:

[0080] To treat 100g of nano-alumina, first add KH570 with a concentration of 3wt%, then add modified perfluoropolyether with a concentration of 3wt%, and finally add it to 100ml of 95% ethanol to prepare a mixed solution;

[0081] (2) Adjust the pH of the solution

[0082] According to the pH value of the solution corresponding to each group of tests, use glacial acetic acid and 25% ammonia water to adjust the pH of the solution to 5;

[0083] (3) Coupling

[0084] Put the prepared solution into the round bottom flask, heat it to the corresponding temperature of the test plan by using a water bath, add 100g of nano-alumina, and react for 1.2h under the dispersion mode of magnetic stirring (120r / min). carry out condensation reflux;

[0085] (4) cleaning

[0086] Wash the nanoparticles multiple times with a suction filter to remove residues that have not undergone a coupling reaction with th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a nano-modified film material capable of improving surface electrical resistance of a polymer insulating material. Silane modified perfluoropolyether and KH570 are grafted to the surface of a nanoparticle material by ultrasonic, suction filtration and drying steps in a silane coupling mode, and modified nano powder is prepared; the modified nano powder is added to light-cured resin, the resin is uniformly applied to the surface of an insulating material after being subjected to ultrasonic, stirring and solution dispersion treatment, the resin israpidly cured by ultraviolet source irradiation, and the nano-modified film material is obtained. Through combination with the advantages of photocuring, rapid coating of the surface of the insulatingmaterial is realized, the demand of improving the electrical resistance is met, and the problems of low timeliness and high cost of a traditional fluorination method are solved while the treatment speed is increased; the photocuring technology has huge potential in the aspect of fluorination modification of the surface of the insulating material, and the surface electrical resistance of the insulating material is expected to be improved stably.

Description

technical field [0001] The invention belongs to the technical field of material modification, and in particular relates to a method for preparing a nano-particle nano-modified film material for improving the electric resistance along the surface of polymer insulation. Background technique [0002] For a long time, the overall insulation performance of power equipment and pulse power equipment has been restricted by the dielectric strength along the surface of solid insulation. As an important factor, the surface state of the material has a great impact on the surface flashover characteristics of the material. At present, there are several types of surface treatment technologies at home and abroad to improve the electrical resistance along the surface of insulating materials, such as surface grinding, surface coating treatment, ion implantation, hydrofluoric acid treatment and electron irradiation treatment. These methods can improve the surface resistance of insulating mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D7/62
Inventor 张冠军王超李文栋李晓冉江智慧
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com