A chitosan hybrid bismuth oxybromide micro-nano multi-level material and its preparation and application

A technology of bismuth oxybromide and chitosan, which is applied in the field of composite materials and photocatalysis, can solve the problems of less active sites, cumbersome operation, and small absorption range, and achieve the effect of broadening absorption, good application prospects, and high photocatalytic activity

Active Publication Date: 2021-12-17
NORTHWEST NORMAL UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most bismuth oxybromide photocatalysts have disadvantages such as fewer active sites, and some bismuth oxybromide catalytic materials with higher activity have problems such as cumbersome operation and high prices of solvents and auxiliary materials.
Therefore, it is an inevitable trend in the development of bismuth oxybromide photocatalytic materials to develop a simple, cheap, and environmentally friendly method to prepare and solve the problems of small light absorption range in the visible light region and low catalyst specific surface area and few active sites.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A chitosan hybrid bismuth oxybromide micro-nano multi-level material and its preparation and application
  • A chitosan hybrid bismuth oxybromide micro-nano multi-level material and its preparation and application
  • A chitosan hybrid bismuth oxybromide micro-nano multi-level material and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Take 1.0 g of chitosan with a molecular weight of 15 kDa, add it to 20 mL of nitric acid solution (2 mol / L), stir to make it completely dispersed, and obtain a chitosan dispersion;

[0028] (2) Take 5.0 g of bismuth nitrate, add it into 30 mL of nitric acid solution (2 mol / L), stir to dissolve it completely, and obtain bismuth nitrate solution;

[0029] (3) Take 2.0 g of cetyl ammonium bromide, dissolve it in 10 mL of water, stir it to dissolve completely, and obtain bromide salt solution;

[0030] (4) Under magnetic stirring, slowly add the chitosan dispersion into the bismuth nitrate solution, and magnetically stir for 20 minutes to ensure that the reaction system is evenly dispersed; Slowly add to the reaction system, and stir for 40 minutes to react; then, move the reaction system into a PPL-lined stainless steel reactor, and conduct a hydrothermal reaction at 200°C for 9 hours. 8 h, the chitosan hybrid bismuth oxybromide micro-nano multi-layer material was obt...

Embodiment 2

[0032] (1) Take 1.5 g of chitosan with a molecular weight of 20 kDa, add it to 30 mL of acetic acid solution (10 wt%), stir to make it completely dispersed, and obtain a chitosan dispersion;

[0033] (2) Take 3.0 g of bismuth nitrate, add it to 30 mL of glacial acetic acid solution (10 wt%), stir to dissolve it completely, and obtain a bismuth nitrate solution;

[0034] (3) Dissolve 1.5 g of potassium bromide in 10 mL of water, stir to dissolve completely, and obtain potassium bromide solution;

[0035](4) Under magnetic stirring, slowly add the chitosan dispersion into the bismuth nitrate solution, and magnetically stir for 20 minutes to ensure that the reaction system is evenly dispersed; then slowly add the potassium bromide solution into the reaction system within 5 minutes under stirring and stirred for 40 min; then, the reaction system was transferred into a PPL-lined stainless steel reactor, and hydrothermally reacted at 120 °C for 15 h. The obtained product was separat...

Embodiment 3

[0037] (1) Take 0.5 g of chitosan with a molecular weight of 5 kDa, add it to 15 mL of nitric acid solution (4 mol / L), stir to make it completely dispersed, and obtain a chitosan dispersion;

[0038] (2) Take 2.5 g of bismuth bromide, add 25 mL of acetic acid solution (10 wt%), stir to dissolve completely, and obtain bismuth nitrate solution;

[0039] (3) Take 1.0 g of hexadecyl ammonium bromide, dissolve it in 10 mL of aqueous solution, stir to dissolve it completely, and obtain potassium bromide solution;

[0040] (4) Under magnetic stirring, slowly add the chitosan dispersion into the bismuth nitrate solution, and magnetically stir for 30 minutes to ensure that the reaction system is evenly dispersed; then slowly add the potassium bromide solution into the reaction system within 15 minutes under stirring and stirred for 40 min; then, the reaction system was transferred into a PPL-lined stainless steel reactor, and hydrothermally reacted at 220 °C for 12 h. The obtained prod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
decolorization rateaaaaaaaaaa
decolorization rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a chitosan hybrid bismuth oxybromide micro-nano multi-level material. The chitosan dispersion is slowly added to a bismuth salt solution, and magnetically stirred to make it uniformly dispersed; Slowly add bromine salt solution to the solution, stir and disperse evenly, then move the reaction system into a reaction kettle, conduct a hydrothermal reaction at 120-300°C for 6-20 h, separate the product by suction filtration, wash with distilled water, and dry in vacuum to obtain chitosan complex Bismuth oxybromide micro-nano multi-level material. In the present invention, chitosan is used as a template-directing agent and a structure-inducing agent, and bismuth salt and bromide salt are combined to form bismuth oxybromide through polymer hydrothermal assistance, and the photocatalysis of bismuth oxybromide is promoted through the induction of amino groups in chitosan molecular chain segments The material has highly exposed crystal faces and abundant oxygen vacancies, which broadens the absorption of the catalyst in the visible light region, making the chitosan hybrid bismuth oxybromide micro-nano multi-level photocatalytic material have high photocatalytic properties under simulated sunlight irradiation. photocatalytic activity.

Description

technical field [0001] The invention relates to a preparation method of a chitosan hybrid bismuth oxybromide micro-nano multi-level material, which is mainly used as a photocatalyst for the degradation treatment of organic pollutants, and belongs to the technical field of composite materials and the technical field of photocatalysis. Background technique [0002] Water resources are an indispensable natural resource in human production and life. However, with the frequent industrial activities of human beings, the phenomenon of water pollution has become more and more serious, and it has gradually become the main environmental problem that countries need to solve. For example: a variety of organic dyes in textile wastewater are not only carcinogens, but also inhibit the transmission of sunlight in water bodies and affect the photosynthesis of water body organisms. In order to solve the above problems, scientists have developed many water treatment methods such as adsorption...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/26B01J27/06B01J35/10C02F1/30C02F101/38
CPCB01J35/004B01J31/26B01J27/06B01J35/1004C02F1/30C02F2305/10C02F2101/308C02F2101/38
Inventor 王荣民张展程何玉凤王雪雪温明山
Owner NORTHWEST NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap