Preparation method of hydrogel composite biological patch for repairing abdominal-wall defects

A biological patch and hydrogel technology, applied in the field of biomedical tissue engineering, can solve difficult vascularization and oxygen, nutrient exchange and metabolite discharge, difficult growth of host cells and new tissues, and difficult cells with poor mechanical properties To achieve the effect of helping the growth of cells and tissues, promoting the regeneration and vascularization of abdominal wall tissue, and controlling the mechanical strength and degradation speed

Active Publication Date: 2019-07-23
SHANGHAI UNIV
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the following problems still exist: 1. When a single decellularized tissue is used for abdominal wall repair, its mechanical properties are poor and it is difficult to support the growth of cells and tissues; 2. After the decellularized tissue is implanted in the body, its degradation rate is too fast, and the new tissue does not Reconstruction is complete, resulti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of hydrogel composite biological patch for repairing abdominal-wall defects
  • Preparation method of hydrogel composite biological patch for repairing abdominal-wall defects
  • Preparation method of hydrogel composite biological patch for repairing abdominal-wall defects

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0022] see Figure 1 to Figure 3 , the preparation method of the hydrogel composite biological patch for repairing abdominal wall defects, the specific preparation steps are as follows:

[0023] a. Design of the mold structure: the mold consists of two parts: the mold base and the jacket. There are evenly distributed vertical cylinders on the base. The distance between adjacent cylinders is 500-800 microns, and the diameter of the cylinders is 500±5 microns. The shape of the mold is and size can be designed according to demand;

[0024] b. Preparation of pouring solution: Weigh a set amount of gelatin in a beaker, add deionized water, stir and dissolve in water at 60 degrees Celsius, and make a gelatin solution with a concentration of 15±1%; then weigh the biological crosslinking agent microorganism The mass ratio of transglutaminase to gelatin is 1:10±0.1; wait for the temperature of the gelatin solution to drop to room temperature, add the cross-linking agent and stir rapi...

Embodiment example 2

[0027] In this example, refer to figure 1 , figure 2 , image 3 , the preparation method of the hydrogel composite biological patch for repairing abdominal wall defects, using porcine dermis decellularized matrix powder and gelatin, through the method of mold casting and enzymatic cross-linking to prepare a hydrogel containing pre-vascularized channels Glue composite biological patch scaffold, the specific preparation steps are as follows:

[0028]a. Preparation of pouring solution: place the beaker on the electronic scale, first adjust to zero and then weigh the set amount of gelatin in the beaker, then add deionized water to the beaker to make the gelatin concentration 15%, and then put Its beaker is placed in the water bath of 60 ℃ and fully stirred, and its gelatin is all dissolved; Then take the biological cross-linking agent microbial transglutaminase of the gelatin of setting amount again, the weight ratio of its amount and gelatin is 1: 10. Put the gelatin solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of biomedicine tissue engineering, and discloses a preparation method of a hydrogel composite biological patch for repairing abdominal-wall defects. According to the preparation method, powder of pig derma after extracellular matrix removal and gelatin are used as biomaterials, mold casting and an enzyme promoting cross-linking shaping technology are used, and the composite hydrogel biological patch is prepared. According to the preparation technology disclosed by the invention, biomaterials of the powder of the pig derma after extracellular matrixremoval and the gelatin are mixed to prepare the patch, so that the hydrogel patch shows excellent biocompatibility, the biological mechanics characteristics of the hydrogel patch are strengthened, and the defects of conventional patches prepared from homogenous materials are solved. Besides, the preparation process is simple, and desired materials are easy to obtain. The composite biological patch bracket prepared by the preparation method contains a pre-vascularization passage, exchange of oxygen and nutrient substances and discharge of metabolic waste are facilitated, and vascularization speed of tissue is accelerated; and in addition, a perforated passage structure contributes to growth in of cells and tissue in the bracket, the reconstruction of abdominal wall tissue can be accelerated, breaking through technical bottlenecks existing in the biological patches is facilitated, and the treatment effects of repairing the abdominal-wall defects can be effectively improved.

Description

technical field [0001] The invention relates to the technical field of biomedical tissue engineering, in particular to a method for preparing a hydrogel composite biological patch for repairing abdominal wall defects. Background technique [0002] In today's clinical surgery, abdominal wall defect is a common disease. Abdominal wall hernia, severe war trauma on the abdominal wall, accidents, enlarged resection of abdominal wall tumors, etc. can all cause the formation of abdominal wall defects. The traditional surgical treatment is mainly to forcibly suture the muscles or ligaments around the abdominal wall defect. After the operation, the patient suffers from obvious pain, long recovery time and high recurrence rate. The emergence of artificial mesh has made a breakthrough in the treatment of abdominal wall. The abdominal wall defect is sutured through the intra-abdominal mesh implantation to reduce the tension of the abdominal wall and speed up the wound repair of the pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L27/36A61L27/44A61L27/52A61L27/58
CPCA61L27/362A61L27/44A61L27/52A61L27/58A61L2430/00C08L89/00
Inventor 胡庆夕刘随红张海光唐海沪陈箫
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap