Special halogen-free flame-retardant synergistic masterbatch for modification of polycarbonate resin and preparation method of halogen-free flame-retardant synergistic masterbatch

A polycarbonate resin and functional masterbatch technology, which is applied in the field of plastic modification processing, can solve the problems of flame retardant performance and physical and mechanical decline, poor high temperature thermal stability, and large loss of flame retardant performance, so as to prevent the internal and Oxygen contact, increase thermal decomposition temperature, good heat protection effect

Active Publication Date: 2019-12-20
江苏万纳普新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the invention is to: 3 –Potassium aluminum benzenesulfonylbenzenesulfonate has application defects such as poor high temperature thermal stability, weak interface adhesion, large loss of flame retardancy, low fluidity, and poor dispersion in the application process of halogen-free flame-retardant polycarbonate resin modification , and its thermal degradation due to powder friction in the process of twin-screw direct blending and extrusion, resulting in flame retardant performance and physical and mechanical decline, the present invention proposes a wall with flame retardant synergy and dense material Material pair 3 – Potassium aluminum benzenesulfonylbenzenesulfonate is coated with multiple composites, and then it is mixed with the corresponding flame retardant synergist and auxiliary agent at low temperature to prepare a halogen-free flame retardant for the modification of polycarbonate resin. Fuel efficiency functional masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special halogen-free flame-retardant synergistic masterbatch for modification of polycarbonate resin and preparation method of halogen-free flame-retardant synergistic masterbatch

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A special halogen-free flame retardant synergistic functional masterbatch for polycarbonate resin modification, the quality ratio of raw materials is as follows:

[0032] Multiple compound coating 3 – Potassium aluminum benzenesulfonylbenzenesulfonate

15.0 kg MBS 75.0 kg Polyphenylmethylsiloxane 5.0 kg RDP 3.0kg Styrene-acrylonitrile copolymer coated PTFE 2.5 kg Pentaerythritol Stearate 500.0 g

[0033] The multiple composite coatings used in the above-mentioned polycarbonate resin modification special halogen-free flame retardant synergistic functional masterbatch 3 -The preparation method of potassium aluminum benzenesulfonylbenzenesulfonate is as follows:

[0034] Add 230 L absolute ethanol, 120 kg 3 – Potassium aluminum benzenesulfonylbenzenesulfonate, 7 kg aluminum sol, 1 kg zinc oxide sol, stir evenly and add to 40°C, then add ammonia water with a mass percentage of 10.0 wt.% dropwise at an even speed, and adju...

Embodiment 2

[0037] A special halogen-free flame retardant synergistic functional masterbatch for polycarbonate resin modification, the quality ratio of raw materials is as follows:

[0038] Multiple compound coating 3 – Potassium aluminum benzenesulfonylbenzenesulfonate

10.0 kg MBS 80.0 kg Polyphenylmethylsiloxane 5.0 kg TPP 2.7kg Styrene-acrylonitrile copolymer coated PTFE 2.0 kg Ethylene bis stearamide 300.0 g

[0039] The preparation method of the multi-composite coating potassium aluminum 3-benzenesulfonylbenzenesulfonate used in the above-mentioned polycarbonate resin modified special halogen-free flame retardant synergistic functional masterbatch is as follows:

[0040] Add 230L absolute ethanol, 120kg 3 – Potassium aluminum benzenesulfonylbenzenesulfonate, 8 kg aluminum sol, 1.5 kg zinc oxide sol, stir evenly and add to 35°C, then add ammonia water with a mass percentage of 11.5 wt.% dropwise at an even speed, and adjust the pH ...

Embodiment 3

[0043] A special halogen-free flame retardant synergistic functional masterbatch for polycarbonate resin modification, the quality ratio of raw materials is as follows:

[0044] Multiple compound coating 3 – Potassium aluminum benzenesulfonylbenzenesulfonate

12.0kg MBS 78.0 kg Polyphenylmethylsiloxane 4.5 kg BDP 2.0 kg Styrene-acrylonitrile copolymer coated PTFE 3.0kg OP wax 500.0 g

[0045] The multiple composite coatings used in the above-mentioned polycarbonate resin modification special halogen-free flame retardant synergistic functional masterbatch 3 -The preparation method of potassium aluminum benzenesulfonylbenzenesulfonate is as follows:

[0046] Add 230 L absolute ethanol, 120 kg 3 – Potassium aluminum benzenesulfonylbenzenesulfonate, 7.5 kg aluminum sol, 2 kg zinc oxide sol, stir evenly and add to 37°C, then add ammonia water with a mass percentage of 12.5 wt.% dropwise at an even speed, and adjust the pH of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of modification and processing of plastics, in particular to special halogen-free flame-retardant synergistic masterbatch for modification of polycarbonateresin and a preparation method of the halogen-free flame-retardant synergistic masterbatch. Multiple-compounded coated potassium aluminum 3-benzenesulfonylbenzenesulfonate is adopted as an inorganicflame retardant, and the halogen-free flame-retardant synergistic masterbatch comprises the compositions: in percent by mass, 10.0-15.0% of multiple-compounded coated potassium aluminum 3-benzenesulfonylbenzenesulfonate, 75.0-80.0% of methyl methacrylate-butadiene-styrene terpolymer (MBS), 3.0-5.0% of polyphenylmethylsiloxane, 2.0-3.0% of organic phosphate, 2.0-3.0% of styrene-acrylonitrile copolymer-coated polytetrafluoroethylene and 0.3-0.5% of a lubricant. When the prepared functional masterbatch is compared with traditional flame-retardant functional masterbatch, the heat resistance and thermal stability of potassium aluminum 3-benzenesulfonylbenzenesulfonate are improved significantly, benzenesulfonic acid functional groups for development of flame retardancy of potassium aluminum 3-benzenesulfonylbenzenesulfonate is protected effectively, and potassium aluminum 3-benzenesulfonylbenzenesulfonate is adaptive to a high processing temperature of polycarbonate resin, so that the flameretardant effect of potassium aluminum 3-benzenesulfonylbenzenesulfonate on the polycarbonate resin is improved more effectively.

Description

technical field [0001] The invention relates to the technical field of plastic modification processing, in particular to a special halogen-free flame retardant synergistic functional masterbatch for polycarbonate resin modification and a preparation method thereof. Background technique [0002] As an important engineering plastic, polycarbonate is widely used in industrial and consumer electronics, automobile and rail vehicle interior decoration and other fields. However, applications in these fields often require polycarbonate parts and components to have high flame retardancy to make them fire safe. The flame retardant modification of polycarbonate can be realized by adding a flame retardant and melt blending through a twin-screw extruder. Flame retardants can prevent plastics from being ignited and inhibit flame propagation, which can effectively improve the combustion resistance of plastics. According to the classification of flame retardant elements, flame retardants ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L83/04C08L51/04C08L27/18C08L25/12C08K13/06C08K9/10C08K5/103C08K5/42C08K5/523C08J3/22
CPCC08J3/226C08J2369/00C08J2483/04C08J2451/04C08J2427/18C08J2425/12C08K13/06C08K9/10C08K5/103C08K5/42C08K5/523
Inventor 李翰卿汪晓东
Owner 江苏万纳普新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products