Gradient-temperature-sensitive strong-bonding hot melt adhesive and preparation method thereof
A temperature-sensitive, hot-melt adhesive technology, applied in the direction of surface pretreatment bonding methods, adhesives, adhesive types, etc., can solve problems such as poor toughness and cohesion, and low bonding strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] A gradient temperature-sensitive type strong bonding hot-melt adhesive, its formulation composition (parts by weight) is: adhesion promoter (20 parts), polycaprolactone (50 parts), KH560 (2 parts), KH792 (2 parts) parts), absolute ethanol (18 parts).
[0029] The polycaprolactone average molecular weight is 660g / mol
[0030] The preparation of described a kind of gradient temperature-sensitive strong bonding hot-melt adhesive comprises the following steps:
[0031] Step A: the synthesis of adhesion promoter, raw material components and content (weight) are as follows: main monomer: methyl methacrylate (30 parts), methyl acrylate (20 parts), butyl methacrylate (30 parts) parts) and butyl acrylate (15 parts);
[0032] Functional monomer: acrylic acid (5 parts);
[0033] Solvent: the ratio of toluene solution is 30%;
[0034] The synthesis method is a solvent-based polymerization method. The raw material and toluene are added into the reactor at a ratio of 1:0.7. After...
Embodiment 2
[0047] A gradient temperature-sensitive strong-adhesive hot-melt adhesive, the formula composition (parts by weight) is: adhesion promoter (25 parts), polycaprolactone (60 parts), KH560 (3 parts), KH792 (3 parts) parts), absolute ethanol (22 parts).
[0048] The polycaprolactone average molecular weight is 720g / mol
[0049] The preparation of described a kind of gradient temperature-sensitive strong bonding hot-melt adhesive comprises the following steps:
[0050] Step A: the synthesis of adhesion promoter, raw material components and content (weight) are as follows: main monomer: methyl methacrylate (30 parts), methyl acrylate (20 parts), butyl methacrylate (30 parts) parts) and butyl acrylate (15 parts);
[0051] Functional monomer: acrylic acid (6.5 parts);
[0052] Solvent: the ratio of toluene solution is 30%;
[0053] The synthesis method is a solvent-based polymerization method. The raw materials and toluene are added into the reactor at a ratio of 1:0.8. After the ...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com