Preparation method of anti-powder-falling silicon dioxide aerogel

A silica and aerogel technology, applied in chemical instruments and methods, inorganic chemistry, silicon compounds, etc., can solve the problems of reduced heat insulation performance, high labor costs, inconvenient storage, transportation, construction and installation, etc., to prevent The effect of falling powder

Active Publication Date: 2020-03-24
GONG YI VAN-RES INNOVATION COMPOSITE MATERIAL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the usual anti-powder solution is to use glass fiber cloth, aluminum foil cloth, etc. to stick on the surface of airgel fiber mat. This method has high labor costs and is not conducive to large-scale production. Moreover, the flexibility of the material after the front and back sides are pasted is not good. Good curling, bending, storage, transportation, construction and installation are not convenient enough
The coating preparation technology on the surface of airgel felt is one of the methods developed recently to avoid powder shedding. Usually, solvent-based coatings are applied on the surface of airgel to prevent slag, and solvent-based coatings will bring environmental pollution. In addition, the solvent will penetrate into the interior of the airgel, destroying the pore structure and reducing its thermal insulation performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of preparation method of anti-powder falling silica airgel, the steps are as follows:

[0020] (1) Mix ethyl orthosilicate, absolute ethanol and water evenly, then add 2 mol / L NH 4 Stir F solution and 0.2moL / L ammonia water evenly, leave standstill, obtain wet gel;

[0021] (2) Mix hydroxy silicone oil and tetraethyl orthosilicate evenly to form a silicone mixture;

[0022] (3) Immerse the wet gel in the silicone mixture, then add 0.2 mol / L ammonia water, react at 60 °C for 24 hours, and dry it to obtain the powder-repelling silica airgel;

[0023] Wherein, in step (1), in terms of molar ratio, ethyl orthosilicate: absolute ethanol: water=1:12:4; NH 4 The amount of F solution added is guaranteed in molar ratio, NH 4 F: tetraethyl orthosilicate=0.008:1; 3 : ethyl orthosilicate = 0.01: 1; in step (2) and step (3), in molar ratio, hydroxyl silicone oil: ethyl orthosilicate = 6: 1, NH 3 : hydroxy silicone oil = 0.04: 1, and the molar weight of hydroxy silicone o...

Embodiment 2

[0025] A kind of preparation method of anti-powder falling silica airgel, the steps are as follows:

[0026] (1) Take methyl orthosilicate, absolute ethanol and water and mix evenly, then add 2 mol / L NH 4 Stir F solution and 0.2moL / L ammonia water evenly, leave standstill, obtain wet gel;

[0027] (2) Mix hydroxy silicone oil and methyl orthosilicate evenly to form a silicone mixture;

[0028] (3) Immerse the wet gel in the organosilicon mixture, then add 0.1 mol / L sodium hydroxide solution, react at 50 ℃ for 18 hours, and dry it to obtain the powder-resistant silicon dioxide gas condensation glue;

[0029] Wherein, in step (1), in terms of molar ratio, methyl orthosilicate: absolute ethanol: water = 1:9:3; NH 4 The amount of F solution added is guaranteed in molar ratio, NH 4 F: Methyl orthosilicate = 0.01:1; 3 : methyl orthosilicate = 0.015: 1; in step (2) and step (3), in terms of molar ratio, hydroxyl silicone oil: orthosilicate = 4: 1, sodium hydroxide: hydroxyl sili...

Embodiment 3

[0031] A kind of preparation method of anti-powder falling silica airgel, the steps are as follows:

[0032] (1) Mix methyltrimethoxysilane, absolute ethanol and water evenly, then add 2 mol / L NH 4 Stir F solution and 0.2 mol / L ammonia water evenly, and let it stand to obtain a wet gel;

[0033] (2) Mix hydroxy silicone oil and butyl orthosilicate evenly to form a silicone mixture;

[0034] (3) Immerse the wet gel in the silicone mixture, then add 0.3 mol / L ammonium fluoride solution, react at 30 °C for 12 hours, and dry it to obtain the powder-resistant silicon dioxide gas condensation glue;

[0035] Wherein, in step (1), in terms of molar ratio, methyltrimethoxysilane: absolute ethanol: water = 1: 11: 2; NH 4 The amount of F solution added is guaranteed in molar ratio, NH 4 F: Methyltrimethoxysilane=0.004:1; 3 : methyltrimethoxysilane=0.005:1; step (2) and step (3), in terms of molar ratio, hydroxyl silicone oil:orthobutyl silicate=8:1, ammonium fluoride:hydroxyl silico...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of aerogel preparation, and discloses a preparation method of anti-powder-falling silicon dioxide aerogel. The preparation method comprises the following steps: uniformly mixing a silicon source, ethanol and water, sequentially adding an NH4F solution and ammonia water, uniformly stirring, and standing to obtain wet gel; uniformly mixing hydroxyl silicone oil and orthosilicate to form an organic silicon mixed solution; dipping the wet gel into the organic silicon mixed solution, then adding a basic catalyst, carrying out static reaction for 8-24 hours at the temperature of 30-60 DEG C, and carrying out drying treatment, so as to obtain the anti-powder-falling silicon dioxide aerogel. By dipping the wet gel in the micromolecular organic silicon mixed solution, and carrying out bonding reaction on small molecular organic silicon and hydroxyl in a wet gel skeleton under alkaline catalysis, the wet gel skeleton coated with the small molecular organic silicon is formed to fix a silicon dioxide aerogel network framework, so that silicon dioxide aerogel particles are fixed microcosmically due to the bonding effect of the aerogel and the small molecular organic silicon after drying is finished, and the powder falling condition can be prevented.

Description

technical field [0001] The invention belongs to the technical field of airgel preparation, and in particular relates to a preparation method of powder-falling-proof silica airgel. Background technique [0002] At present, the development of new energy, the improvement of the utilization rate of existing energy and the conservation of energy have attracted great attention from all countries. my country is an energy-poor country, therefore, rational use of energy and energy conservation are of great significance to the sustainable development of our society. Adopting new technologies and processes to develop environmentally friendly heat insulation materials is one of the most effective and economical measures to save energy. [0003] SiO 2 As an emerging super heat insulation material, airgel has an extremely low thermal conductivity, which is far lower than the thermal conductivity of 0.25W / m K of static air at room temperature, and has an incomparable heat insulation effe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/158
CPCC01B33/1585
Inventor 姚栋嘉牛利伟李静张继承刘喜宗张东生董会娜何凤霞
Owner GONG YI VAN-RES INNOVATION COMPOSITE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products