A kind of 100% recyclable polyethylene composite film and its preparation method and application

A polyethylene and composite film technology, applied in the field of polyethylene materials, can solve the problems of poor temperature resistance, difficulty in meeting process requirements, and inability to meet the temperature resistance requirements of zipper bags and nozzle bags, so as to achieve difficult delamination and excellent Composite fastness, excellent hot tack and heat seal strength effects

Active Publication Date: 2021-10-15
江门市华龙膜材股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For ordinary PE film or ordinary composite PE film (such as PE / PE), due to the poor temperature resistance of ordinary PE film, the film is soft and easy to stretch, it is difficult to meet the process requirements of high-speed printing, lamination, bag making and automatic filling , and cannot meet the temperature resistance requirements of zipper bags and nozzle bags

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 100% recyclable polyethylene composite film and its preparation method and application
  • A kind of 100% recyclable polyethylene composite film and its preparation method and application
  • A kind of 100% recyclable polyethylene composite film and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] The present invention also provides a preparation method of the 100% recyclable polyethylene composite film described in the above technical solution, when the adhesive layer is a low-density polyethylene film, the method comprises the following steps:

[0056] After melting and plasticizing the raw materials of the outer layer of the printing layer, the middle layer of the printing layer and the inner layer of the printing layer, the three-layer blown film co-extrusion process is used to co-extrude the blown film to obtain the primary printing layer;

[0057] The primary printing layer is sequentially subjected to longitudinal uniaxial stretching, annealing and corona treatment to obtain a composite printing layer;

[0058] Melting and plasticizing the raw materials of the outer layer of the heat-sealing layer, the middle layer of the heat-sealing layer and the inner layer of the heat-sealing layer, and then co-extruding the blown film using a three-layer blown film co-...

Embodiment 1

[0088] In the 100% recyclable polyethylene composite film prepared in this example, the adhesive layer is a solvent-free glue layer, the thickness is negligible, the thickness of the printing layer is 20 μm, and the heat-sealing layer is 20 μm;

[0089] In the printing layer, the mass ratio of the outer layer of the printing layer, the middle layer of the printing layer and the inner layer of the printing layer is 3:4:3; in terms of mass percentage, the outer layer of the printing layer includes 45% of metallocene medium density polyethylene 3505MC and 55% of High-density polyethylene HTA108; in terms of mass percentage, the middle layer of the printing layer includes 25% of bimodal medium-density polyethylene FB1350 and 75% of metallocene low-density polyethylene 6056ML; in terms of mass percentage, the inner layer of the printing layer includes 35% of Metallocene medium density polyethylene 4002ML and 65% high density polyethylene 5960G;

[0090] In the heat-sealing layer, t...

Embodiment 2

[0102] In the 100% recyclable polyethylene composite film prepared in this example, the adhesive layer is a solvent-free glue layer, the thickness is negligible, the thickness of the printing layer is 30 μm, and the heat-sealing layer is 20 μm;

[0103] In the printing layer, the mass ratio of the outer layer of the printing layer, the middle layer of the printing layer and the inner layer of the printing layer is 1:2:1; in terms of mass percentage, the outer layer of the printing layer includes 45% of metallocene medium density polyethylene 3505MC and 55% of High-density polyethylene HTA108; in terms of mass percentage, the middle layer of the printing layer includes 25% of bimodal medium-density polyethylene FB1350 and 75% of metallocene low-density polyethylene 6056ML; in terms of mass percentage, the inner layer of the printing layer includes 35% of Metallocene medium density polyethylene 4002ML and 65% high density polyethylene 5960G;

[0104] In the heat-sealing layer, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polyethylene materials, and in particular relates to a 100% recyclable polyethylene composite film and its preparation method and application. The 100% recyclable polyethylene composite film provided by the present invention comprises a sequentially bonded composite printing layer, an adhesive layer and a composite heat-sealing layer; The direction to the composite heat-sealing layer is from outside to inside, and the composite printing layer includes the outer layer of the printing layer, the middle layer of the printing layer and the inner layer of the printing layer in sequence; the adhesive layer is low-density polyethylene film or solvent-free glue layer; the composite heat-sealing layer is a multi-layer co-extruded polyethylene heat-sealing film, and the composite heat-sealing layer includes an outer layer of a heat-sealing layer, a middle layer of a heat-sealing layer and an inner layer of a heat-sealing layer in sequence. Experimental results show that the 100% recyclable polyethylene composite film provided by the invention can be 100% recyclable, and has the characteristics of thin thickness, low density, puncture resistance and low sealing temperature.

Description

technical field [0001] The invention belongs to the technical field of polyethylene materials, and in particular relates to a 100% recyclable polyethylene composite film and its preparation method and application. Background technique [0002] In food, lotion, cosmetics and other industries, compared with waste paper and waste metal, waste plastics are relatively complicated to recycle due to their complex composition and different forms, especially food packaging for printing, fragrance preservation, pressure resistance, and anti-break Bags, moisture-proof, improved shelf life and other requirements, the structure of each bag is 2 to 4 layers of materials with different components, such as PET / PE, BOPP / PE, PET / VMPET / PE, NY / PE, PET / AL / NY / PE, after use, it cannot be stripped, recycled or reused at all, and can only be incinerated or landfilled, causing great pollution to the environment. [0003] At present, biaxially stretched BOPE composite PE can be recycled after use, b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/06B32B27/32B32B7/02B32B7/12B32B33/00B65D65/40B29D7/01
CPCB29D7/01B32B7/02B32B7/12B32B27/08B32B27/32B32B33/00B32B2307/306B32B2307/54B32B2307/558B32B2307/7265B65D65/40Y02W30/80
Inventor 文斌森魏洪媚
Owner 江门市华龙膜材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com