Castor oil-based water-based light-cured nonionic emulsion, and preparation method and application thereof

A castor oil-based, non-ionic technology, applied in the field of castor oil-based water-based light-curable non-ionic emulsion and its preparation, can solve the problem of less flexible chain segments, achieve high reproducibility, excellent mechanics and water resistance, and reduce petrochemical resources The effect of pressure

Active Publication Date: 2020-12-08
DONGGUAN CTL NEW MATERIAL TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Third, the patent uses a hyperbranched resin prepared from dimethylol propionic acid, which has a branched molecular structure and fewer flexible segments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Castor oil-based water-based light-cured nonionic emulsion, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Add metered castor oil and ricinoleic acid (the molar ratio of castor oil to ricinoleic acid is 1:9) and N, N'-diisopropylcarbodiimide (amount of 1% of the molar amount of ricinoleic acid), stir and heat up to 120°C for 3 hours of vacuum dehydration reaction, then cool down to 65°C and add a certain amount of acetone (the amount is 10 times the total mass of castor oil and ricinoleic acid) to dissolve , then put it at 5°C and add a certain amount of cyclohexane (the amount is 15 times the total mass of castor oil and ricinoleic acid) to make the product crystallize and precipitate out, and dry it in vacuum to obtain pure castor oil-based star-shaped prepolymer thing;

[0022] (2) Mix isophorone diisocyanate (3 times the molar amount of castor oil) and dibutyltin dilaurate (0.1% by weight of pure castor oil-based star prepolymer) in a constant temperature water bath at 15°C Drop the mixture into the pure castor oil-based star-shaped prepolymer prepared in step (1), ...

Embodiment 2

[0026] (1) Add metered castor oil and ricinoleic acid (the molar ratio of castor oil to ricinoleic acid is 1:12) and dicyclohexylcarbodiimide (the molar amount of ricinoleic acid is 3%), stir and heat up to 150°C for 2 hours of vacuum dehydration reaction, then cool down to 75°C and add a certain amount of cyclohexanone (the amount is 15 times the total mass of castor oil and ricinoleic acid) to dissolve, and then dissolve it Place at 15°C and add a certain amount of octane (the amount is 10 times the total mass of castor oil and ricinoleic acid) to precipitate the product crystallization, and dry it in vacuum to obtain pure castor oil-based star prepolymer;

[0027] (2) Drop a mixture of toluene diisocyanate (3.1 times the molar amount of castor oil) and dibutyltin dilaurate (0.15% of the weight of pure castor oil-based star prepolymer) in a constant temperature water bath at 25°C Put it into the pure castor oil-based star-shaped prepolymer prepared in step (1), pay attention...

Embodiment 3

[0031] (1) Add metered castor oil and ricinoleic acid (the molar ratio of castor oil to ricinoleic acid is 1: 15) and 1-(3-dimethylaminopropyl)-3-ethyl Carbodiimide hydrochloride (the dosage is 2% of the molar amount of ricinoleic acid), stir and heat up to 130°C for 2.5 hours of vacuum dehydration reaction, then cool down to 68°C and add a certain amount of methyl ethyl ketone (the amount is castor oil and 12 times the total mass of castor oil and ricinoleic acid) to dissolve, then put it at 10°C and add a certain amount of n-hexane (the amount is 13 times the total mass of castor oil and ricinoleic acid) to precipitate the product crystallization, and vacuum dry Promptly obtain pure castor oil-based star prepolymer;

[0032] (2) Mix p-phenylene diisocyanate (3.2 times the molar amount of castor oil) and dibutyltin dilaurate (0.12% by weight of pure castor oil-based star prepolymer) in a constant temperature water bath at 20°C Drop into the pure castor oil-based star-shaped ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of water-based UV curing materials, and particularly relates to a preparation method of a castor oil-based water-based light-cured nonionic emulsion. The preparationmethod comprises the following steps: (1) reacting castor oil, ricinoleic acid and an esterification catalyst, dissolving, and adding a precipitating agent to precipitate the product; (2) mixing diisocyanate and dibutyltin dilaurate, slowly adding the mixture into the product obtained in the previous step, and reacting to obtain an intermediate; (3) dissolving the intermediate in a solvent, and then adding polyethylene glycol acrylate to react with a polymerization inhibitor to obtain a star castor oil-based water-based UV-cured prepolymer; and (4) mixing the star castor oil-based water-basedUV-cured prepolymer, a vegetable oil-based reactive nonionic surfactant, a free radical photoinitiator and a cationic photoinitiator, adding water, and uniformly dispersing to obtain the castor oil-based water-based light-cured nonionic emulsion. The star castor oil-based water-based UV cured prepolymer prepared by the method disclosed by the invention has high crosslinking density, so that a coating film prepared from the prepolymer has excellent mechanical properties, water resistance and the like, and can be used as a film-forming base material in the fields of environment-friendly coatings, printing ink and adhesives.

Description

technical field [0001] The invention belongs to the field of water-based UV curing materials, and in particular relates to a castor oil-based water-based light-curable nonionic emulsion and a preparation method and application thereof. Background technique [0002] The consumption of fossil resources and environmental pollution not only affect the ecological environment, but also hinder the development of organic polymer chemical industry based on fossil raw materials. Biomass resources are currently the only resources that can be used sustainably. A large number of natural products can be extracted from agricultural and forestry resources, many of which contain active reactive groups such as double bonds or hydroxyl groups. It is easy to build a UV curing system, thereby converting agricultural and forestry natural resources into UV curing raw materials, which greatly expands the raw materials of UV curing materials. source. Castor oil is an important biomass resource, its...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/03C08G18/75C08G18/76C08G18/64C08G18/10C08G18/67C09D175/14C09J175/14C09D11/00C08L75/14
CPCC08J3/03C08G18/755C08G18/64C08G18/10C08G18/6795C08G18/7614C08G18/7671C08G18/758C09D175/14C09J175/14C09D11/00C08J2375/14
Inventor 袁腾尹鉴卢开平卢杰宏赵文爱杨卓鸿
Owner DONGGUAN CTL NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap