Preparation method of hierarchical porous iron-titanium dioxide/ZSM-5 molecular sieve
A ZSM-5, titanium dioxide technology, applied in the direction of titanium dioxide, catalyst activation/preparation, titanium oxide/hydroxide, etc., can solve the problem of limited regeneration adsorption capacity, insufficient to meet green, environmental protection, high efficiency, secondary pollution and other problems, Achieve the effects of green materials, high synthesis efficiency and mild conditions
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0058] The preparation method of a kind of hierarchical porous iron-titanium dioxide / ZSM-5 molecular sieve of the present invention is specifically implemented according to the following steps:
[0059] Step 1, preparation of clear and transparent TiO 2 Gel, specifically: at 20°C, add 1.0g of ethyl titanate to 50ml of absolute ethanol, stir vigorously at a speed of 30rad / min for 30min to make it evenly mixed, and then add dropwise to it with a mass concentration of 15% boric acid solution and 15ml deionized water, then continue to stir vigorously for 3h, and stand at 20°C for 4h to obtain TiO 2 gel;
[0060] Step 2, fully contacting attapulgite with nitric acid and sodium hydroxide solution respectively, uniformly dispersed, and grinding to obtain amorphous silicon source powder; specifically:
[0061] Step 2.1, mix 1g of powdered natural attapulgite and 8ml of sodium hydroxide solution with a mass fraction of 10% evenly, mix and stir at 95°C for 2.5h, centrifuge after full ...
Embodiment 2
[0078] The preparation method of a kind of hierarchical porous iron-titanium dioxide / ZSM-5 molecular sieve of the present invention is specifically implemented according to the following steps:
[0079] Step 1, preparation of clear and transparent TiO 2 Gel, specifically: at 15°C, add 3.0g of ethyl titanate to 100ml of absolute ethanol, use a 500ml three-neck flask to dissolve and stir, the stirring speed is 18rad / min, and the stirring time is 25min; use a burette to mix Add a boric acid solution with a concentration of 3.5% to the solution at a rate of 0.1d / s, add 20ml of deionized water, continue to react for 4h at a speed of 10rad / min, and then stand in an environment of 25°C for 3h to obtain TiO 2 gel system;
[0080] Step 2, fully contacting attapulgite with nitric acid and sodium hydroxide solution respectively, uniformly dispersed, and grinding to obtain amorphous silicon source powder; specifically:
[0081] Step 2.1, mix 2g of powdered natural attapulgite and 20ml o...
Embodiment 3
[0094] The preparation method of a kind of hierarchical porous iron-titanium dioxide / ZSM-5 molecular sieve of the present invention is specifically implemented according to the following steps:
[0095] Step 1, preparation of clear and transparent TiO 2 Gel, specifically: add 1.8g of ethyl titanate to 50ml of absolute ethanol at 40°C, use a 500ml three-neck flask to dissolve and stir, the stirring speed is 20rad / min, and the stirring time is 20min; 5% boric acid solution was added at a rate of 0.5d / s, and 20ml of deionized water was added, and the reaction was continued for 3h at a speed of 18rad / min, and then stood at 25°C for 4h to obtain TiO 2 gel system;
[0096] Step 2, fully contacting attapulgite with nitric acid and sodium hydroxide solution respectively, uniformly dispersed, and grinding to obtain amorphous silicon source powder; specifically:
[0097] Step 2.1, mix 5g of powdery natural attapulgite and 100ml of sodium hydroxide solution with a mass concentration of...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com