Graphitized carbon loaded nano zero-valent iron material and preparation method and application thereof

A nano-zero-valent iron and graphitized carbon technology, applied in chemical instruments and methods, chemical/physical processes, oxidized water/sewage treatment, etc. Deal with the problems that need to be further improved to achieve the effect of increasing stability and reusability, increasing stability and durability, and easy adsorption

Active Publication Date: 2021-04-06
CHINESE RES ACAD OF ENVIRONMENTAL SCI
View PDF18 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the operation process and synthesis conditions of the fine preparation method are complicated, which is not conducive to the large-scale industrial production of materials.
[0004] Chinese patent application CN 106044921 A provides a method for preparing carbon sphere-supported nano-zero-valent iron composite materials, which includes (1) preparing carbon spheres containing hydrophilic functional groups (-OH, -COOH) by hydrothermal method; (2) Chelate iron ions and functional groups by soaking; (3) Finally, drop potassium borohydride or sodium borohydride solution into

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphitized carbon loaded nano zero-valent iron material and preparation method and application thereof
  • Graphitized carbon loaded nano zero-valent iron material and preparation method and application thereof
  • Graphitized carbon loaded nano zero-valent iron material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A preparation method of graphitized carbon-supported nanometer zero-valent iron material, comprising the following steps:

[0046] (1) Ferrous acetate and 2-aminoterephthalic acid are placed in a ball mill reactor with a mass ratio of 3:1;

[0047] (2) Add a zirconia grinding medium with a diameter of 5 mm to the ball mill reactor, adjust the rotating speed of the ball mill to 300 rpm, add 1 mL / g of ethylene glycol solution and grind for 5 hours to obtain a polymer material;

[0048] (3) Put the polymer material in a tube furnace and heat it up to 800°C at a heating rate of 10°C / min under a nitrogen atmosphere; pyrolyze for 3 hours and cool to obtain graphitized carbon-loaded nano-zero-valent iron material .

Embodiment 2

[0050] A preparation method of graphitized carbon-supported nanometer zero-valent iron material, comprising the following steps:

[0051] (1) Ferric sulfate and 2-aminoterephthalic acid are placed in a ball mill reactor at a mass ratio of 2:1;

[0052] (2) Add an alumina grinding medium with a diameter of 5 mm to the ball mill reactor, adjust the rotating speed of the ball mill to 350 rpm, add 1 mL / g of dimethylformamide solution and grind for 4 hours to obtain a polymer material;

[0053] (3) Put the polymer material in a tube furnace and heat it to 900°C at a heating rate of 10°C / min in an argon atmosphere; pyrolyze it for 3 hours and cool it down to obtain graphitized carbon-supported nano-zero-valent iron Material.

Embodiment 3

[0055] A preparation method of graphitized carbon-supported nanometer zero-valent iron material, comprising the following steps:

[0056] (1) ferric chloride and 2-aminoterephthalic acid are placed in a ball mill reactor with a mass ratio of 4:1;

[0057] (2) add the agate ball grinding medium of diameter 10mm in the ball mill reactor, adjust the rotating speed of ball mill to be 290rpm, add the ethylene glycol solution of 1mL / g and grind for 5 hours to obtain polymer material;

[0058] (3) Put the polymer material in a tube furnace and heat it to 750°C at a heating rate of 5°C / min under a nitrogen atmosphere; pyrolyze for 3 hours and cool to obtain graphitized carbon-loaded nano-zero-valent iron material .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of preparation of nano zero-valent iron carbon materials, and particularly relates to a graphitized carbon loaded nano zero-valent iron material and a preparation method and application thereof. The preparation method of the graphitized carbon loaded nano zero-valent iron material comprises the following steps: (1) putting ferric salt and 2-aminoterephthalic acid into a reaction kettle of a ball mill; (2) adding a grinding medium into a reaction kettle of a ball mill, and grinding to obtain a ball-milled material; and (3) pyrolyzing the ball-milled material, and cooling to obtain the graphitized carbon loaded nano zero-valent iron material. The prepared graphitized carbon loaded nano zero-valent iron material has higher and more durable catalytic degradation efficiency, and can better remove pollutants in an environmental water sample, especially organic dye pollutants.

Description

technical field [0001] The invention belongs to the field of preparation of nanometer zero-valent iron-carbon materials, and in particular relates to a graphitized carbon-supported nanometer zero-valent iron material and its preparation method and application. Background technique [0002] Advanced Oxidation Processes (AOPs) is a method for treating toxic organic pollutants by generating hydroxyl radicals (OH·) with strong oxidizing properties. Among them, the Fenton method is an important part of the advanced oxidation technology. Compared with the traditional physical and biological treatment methods, the Fenton method using active free radicals as the oxidant has a fast reaction speed and high salinity, so it is widely used in sewage treatment. Iron exists widely in nature, and the use of iron-based materials in the removal of organic matter by the Fenton method has attracted extensive attention. Fenton's reagent consists of ferrous ions (Fe 2+ ) and hydrogen peroxide (...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/24C02F1/72C02F101/30
CPCB01J27/24C02F1/725C02F2101/30C02F2101/308
Inventor 赵晓丽吕宏洲吴丰昌蔡亚岐
Owner CHINESE RES ACAD OF ENVIRONMENTAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap