High-performance modified PP sheet and processing technology thereof

A high-performance, modified technology, applied in other household appliances, applications, household appliances, etc., can solve the problems of easy deformation and normal use of PP panels, insufficient load-bearing capacity, etc., and achieves not easy to delaminate and fracture, fast forming, and high connection strength. Effect

Inactive Publication Date: 2021-04-06
太仓市兴羿防腐塑料制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Purpose of the invention: In order to overcome the above deficiencies, the purpose of the present invention is to provide a high-performance modified PP board, which solves the problem of insufficient load-bearing capacity of the PP board in the prior art, and the problem that the PP board is easily deformed during use and affects normal use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance modified PP sheet and processing technology thereof
  • High-performance modified PP sheet and processing technology thereof
  • High-performance modified PP sheet and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0061] Such as Figure 1-3 The high-performance modified PP sheet shown includes carbon fiber reinforced epoxy resin composite material upper skin 1, carbon fiber reinforced epoxy resin composite material lower skin 2, PP honeycomb board 3, a set of epoxy resin foam 4, a Set of epoxy resin foam reinforced bracket 5, upper epoxy resin film 6 and lower epoxy resin film 7, the carbon fiber reinforced epoxy resin composite material upper skin 1 and carbon fiber reinforced epoxy resin composite material lower skin 2 The cross-sectional area of ​​the carbon fiber reinforced epoxy resin composite material is the same, and the upper skin 1 of the carbon fiber reinforced epoxy resin composite material and the lower skin 2 of the carbon fiber reinforced epoxy resin composite material are set oppositely. Between the skin 1 and the lower skin 2 of the carbon fiber reinforced epoxy resin composite material, the set of epoxy resin foam 4 and the set of epoxy resin foam reinforcing brackets ...

Embodiment 2

[0065] Based on the structure of the first embodiment, the epoxy resin foam 4 includes a foaming epoxy resin and a curing agent, and the foaming epoxy resin includes an epoxy resin, a chemical foaming agent and a nano toughening agent.

[0066] Wherein, the epoxy resin includes E-51 bisphenol A type epoxy resin, nano calcium carbonate, 4,4,-diaminodiphenylmethane, 2-phenylimidazole and acetone, and the E-51 bisphenol Type A epoxy resin, nano-calcium carbonate, 4,4,-diaminodiphenylmethane, 2-phenylimidazole and acetone are calculated in parts by weight:

[0067] E-51 bisphenol A type epoxy resin 110-120 parts

[0068] Nano calcium carbonate 6-8 parts

[0069] 4,4,- 60-68 parts of diaminodiphenylmethane

[0070] 2-phenylimidazole 0.6-0.9 parts

[0071] Acetone 40-50 parts.

[0072] In addition, the chemical blowing agent includes sodium dodecylbenzenesulfonate, benzenesulfonyl hydrazide, talcum powder, azodicarbonamide, trifluoropropylene, rosin resin, sodium bicarbonate, de...

Embodiment 3

[0103] The epoxy resin foam 4 includes foaming epoxy resin and curing agent, and the foaming epoxy resin includes epoxy resin, chemical foaming agent and nano toughening agent.

[0104] Wherein, the epoxy resin includes E-51 bisphenol A type epoxy resin, nano calcium carbonate, 4,4,-diaminodiphenylmethane, 2-phenylimidazole and acetone, and the E-51 bisphenol Type A epoxy resin, nano-calcium carbonate, 4,4,-diaminodiphenylmethane, 2-phenylimidazole and acetone are calculated in parts by weight:

[0105] E-51 bisphenol A type epoxy resin 110 parts

[0106] Nano calcium carbonate 6 parts

[0107] 4,4,- 60 parts of diaminodiphenylmethane

[0108] 0.6 parts of 2-phenylimidazole

[0109] Acetone 40 parts.

[0110] In addition, the chemical blowing agent includes sodium dodecylbenzenesulfonate, benzenesulfonyl hydrazide, talcum powder, azodicarbonamide, trifluoropropylene, rosin resin, sodium bicarbonate, deodorant, clay powder, Calcium carbonate, sodium dodecylsulfonate and wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance modified PP sheet and a processing technology, and belongs to the technical field of processing and application of novel high polymer materials. The PP sheet comprises carbon fiber reinforced epoxy resin composite material upper skin, carbon fiber reinforced epoxy resin composite material lower skin, a PP honeycomb sheet, a group of epoxy resin foam, a group of epoxy resin foam reinforced brackets, upper epoxy resin adhesive film and lower epoxy resin adhesive film. Each epoxy resin foam reinforced bracket comprises a first reinforcing rod, a second reinforcing rod, a third reinforcing rod, a fourth reinforcing rod, a middle supporting rod and an outer wall. According to the high-performance modified PP sheet, each arranged epoxy resin foam reinforced bracket is formed by folding one steel wire, the outer wall and the reinforcing rods inside are connected end to end one by one, it can be guaranteed that the connecting strength at each folding position is high, and when an enclosure is in use and stressed with force, the high-performance modified PP sheet is not prone to being broken. The processing technology is simple, forming is rapid to carry out, the production efficiency is improved, the production cost is reduced, and therefore the requirement for industrial application in the industrial field is met.

Description

technical field [0001] The invention belongs to the technical field of novel processing and application of polymer materials, and in particular relates to a high-performance modified PP plate. The invention also relates to a processing technology of high-performance modified PP board. Background technique [0002] PP hollow sheet (polypropylene hollow sheet) is made of polypropylene raw material blended with polyethylene raw material and extruded through a hollow sheet production line. It is widely used in construction industry, advertising industry, agriculture, interior decoration, breeding industry, packaging and transportation industry, etc. field. [0003] When used in the packaging and transportation industry, the traditional PP hollow boards are generally connected with vertical corrugated ribs between the double-layer PP boards. The overall strength of this structure is small, and its force can only be in the vertical direction. During packaging and transportation,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C44/12B29C69/00C08J9/10C08J9/08C08J9/06C08L63/02C08K13/02C08K3/26C08K5/18C08K5/3445B29L7/00
CPCB29C44/12B29C69/00B29L2007/002C08J9/0028C08J9/0071C08J9/06C08J9/08C08J9/103C08J9/105C08J2203/02C08J2203/04C08J2363/02C08K5/18C08K5/3445C08K13/02C08K2003/265C08K2201/011
Inventor 王志红
Owner 太仓市兴羿防腐塑料制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com