White copper-based antibacterial master batch for fibers, and preparation method thereof
An antibacterial masterbatch, white technology, applied in the chemical characteristics of fibers, rayon manufacturing, textiles and papermaking, etc., can solve the problems of different copper valence states and existing states, narrowing of fiber application range, and large color differences, etc., to achieve repeatable High performance, widen the dyeing range, and excellent washing resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0048] Example 1
[0049]A fiber-based antibacterial parental particles, 0.4% nano-copper nickel alloy antibacterial agent, 99% PP, 0.2% low molecular wax, 0.2% oleic acid and 0.2% antioxidant 1010. Among them, the average particle diameter of the nano-copper nickel alloy antibacterial agent is 200 nm, and the dispersion treatment of oleic acid is coated.
[0050] The method of preparation of the antibacterial patent includes the steps of:
[0051] (1) Workage: Grinding the PP to the grinding machine into a PP powder;
[0052] (2) Weighing: Non-copper nickel alloy antibacterial agent, PP powder, low molecular wax, oleic acid, antioxidant 1010;
[0053] (3) Mix: 0.4% nano-copper nickel alloy antibacterial agent, 99% PP powder, 0.2% low molecular wax, 0.2% oleic acid and 0.2% antioxidant 1010 to high and low speed Mixed, wherein the low speed mixed rotation speed is 700 rpm, the mixing time is 2 minutes, the high speed mixed rotation speed is 1400 rpm, and the mixing time is 30 seco...
Example Embodiment
[0056] Example 2
[0057] A fiber-based antibacterial parental particles, a 1% nanopronron nickel alloy antibacterial agent, 98.1% PA6, 0.3% silane coupling agent KH560, 0.3% fatty acid and 0.3% antioxidant 1098 Wherein, the nanopronron nickel alloy antibacterial agent has an average particle diameter of 300 nm, and the dispersion treatment of fatty acid coated. The extrusion temperature is 250 ° C, and the other is the same as the preparation conditions and preparation methods of Example 1.
Example Embodiment
[0058] Example 3
[0059] A white copper-based antibacterial parental particles, 3% nano-zinc copper nickel alloy antibacterial agent, 95.5% PA66, 0.5% phthalate coupling agent, 0.5% ascorbic acid and 0.5% antioxidant 168 Composition, where the nanoplanm copper nickel alloy antibacterial agent has an average particle diameter of 600 nm, and the dispersion of ascorbic acid is coated. The extrusion temperature is 275 ° C, and the other is the same as the preparation conditions and preparation methods of Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap